Method of forming oxide superconducting layers by solid state diffusion
Assignee: US Philips Corp
•
Filing: 1990-02-06
•
Granted: 1991-01-29
•
Expires: 2010-02-06
Abstract
Abstract A superconductive thin layer of an oxidic material is manufactured by contacting at least two starting substtances with each other, after which diffusion and a chemical reaction in the solid state occur by means of increasing the temperature, while forming the superconductive thin layer.
Inventors
- 👤 Jan W. Severin
- 👤 Gijsbertus de With
- 👤 Dagobert M. de Leeuw
- 👤 Cornelis A. H. A. Mutsaers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:49
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0296; H10N60/0576; Y; Y10; Y10S; Y10S505/00; Y10S505/725; Y10S505/73
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
102 words
A method of manufacturing a thin layer of an oxide superconductive material on a non-superconductive oxide base, said method comprising mechanically contacting two starting non-superconductive substances, which react together to form a superconductive oxide material, said starting substances being provided as a thin layer of an oxide non-superconductive substance on an oxide non-superconductive substance base and heating in an oxidizing atmosphere, said starting substances while in mechanical contact with each other thereby causing diffusion in a solid state reaction to take place between said starting substances and causing said superconductive thin layer of an oxide material to form on said non-superconductive base.
Claim 2
Independent Claim
102 words
A method of manufacturing a thin layer of an oxide superconductive material on a non-superconductive oxide base, said method comprising mechanically contacting two starting non-superconductive substances, which react together to form a superconductive oxide material, said starting substances being provided as a thin layer of an oxide non-superconductive substance on an oxide non-superconductive substance base and heating in an oxidizing atmosphere, said starting substances while in mechanical contact with each other thereby causing diffusion in a solid state reaction to take place between said starting substances and causing said superconductive thin layer of an oxide material to form on said non-superconductive base.
Claim 3
Dependent Claim
44 words
A method as claimed in claim 1, characterized in that one of the starting substances forms a substrate on which the other starting substance(s) is (are) provided in the form of a thin layer, after which the step for increasing the temperature takes place.
Claim 4
Dependent Claim
42 words
A method as claimed in claim 1, characterized in that the starting substances are provided on an inert substrate in the form of two thin layers one on top of the other, after which the step for increasing the temperature takes place.
Claim 5
Dependent Claim
43 words
A method as claimed in claim 2 of manufacturing a superconductive thin layer of YBa 2 Cu 3 O 7- δ, in which a substrate of Y 2 Cu 2 O 5 is used having thereon a thin layer of BaCuO 2 .
Claim 6
Dependent Claim
42 words
A method as claimed in claim 2 of manufacturing a superconductive thin layer of YBa 2 Cu 3 O 7- δ in which a substrate of CuO is used having thereon a thin layer of Y 2 Ba 4 O 7 .
Claim 7
Dependent Claim
59 words
A method as claimed in claim 2 of manufacturing a superconductive thin layer of YBa 2 Cu 3 O 7 --Z, wherein Z is about 0.1 to 0.5 in which a substrate of Y 2 BaCuO 5 is used having thereon a thin layer of a mixture of 40 mol % CuO and 60 mol % BaCuO 2 .
Claim 8
Dependent Claim
54 words
A method as claimed in claim 3 of manufacturing a superconductive thin layer of La x Me 2-x CuO 4 in which Me is chosen from Ca, Sr and Ba, wherein x is between 1 and 2 and wherein the starting substances are thin layers of La 2 CuO 4 and LaMeCuO 4 .
References Cited (Backward Citations)
US3397084A
Cited
US4367102A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-01-28 | 1994-07-30 | 1995-01-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-01-28 | 1998-07-30 | 1999-01-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-01-28 | 2002-07-30 | 2003-01-29 | $7700.00 | Window Closed / Lapsed |