US4981816A
Expired / Lapsed
US
⏱️ 0.0 years remaining
MO/TI Contact to silicon
Assignee: Intersil Corp
•
Filing: 1989-11-30
•
Granted: 1991-01-01
•
Expires: 2009-11-30
Abstract
Abstract A metal for fabricating contact structures through via openings in VLSI circuits employs a dual layer of refractory metal. A thin titanium layer is deposited, over which a molybdenum layer is formed. An annealing treatment further improves contact resistance characteristics. The method results in a contact structure which exhibits desirable properties of thermal compatibility, step coverage, contact resistance and improved processing characteristics.
Inventors
- 👤 Manjin J. Kim
- 👤 Dale M. Brown
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 11:32
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/047; H10D; H10D64/00; H10D64/01; H10D64/011; H10D64/0111; H10P; H10P50/00; H10P50/20; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10W20/033; H10W20/056; H10W20/40; H10W20/41; H10W20/44; H10W20/4403; H10W20/4437; H10W20/4441; Y; Y10; Y10S; Y10S148/00; Y10S148/02
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
168 words
A method for fabricating a contact structure through a via opening in insulative material disposed on a silicon substrate having an oxide layer thereon, said method comprising the steps of: disposing a thin layer consisting essentially of only titanium, and essentially devoid of tungsten, over the insulative material and in contact with the oxide layer exposed through the via opening; disposing a thick layer over the titanium layer, including that portion of the titanium layer in the via opening, the thick layer comprising material selected from the group consisting of tungsten, molybdenum and alloys thereof and selected to improve thermal stability of the contact structure; selectively removing the thick layer in accordance with a first specified pattern; selectively removing the titanium layer in accordance with a second specified pattern; and annealing the contact structure at a temperature between about 550° C., and about 560° C. to cause the titanium layer to dissolve the oxide layer and form a contact having a resistance below about 100 ohms·μm 2 .
Claim 2
Independent Claim
168 words
A method for fabricating a contact structure through a via opening in insulative material disposed on a silicon substrate having an oxide layer thereon, said method comprising the steps of: disposing a thin layer consisting essentially of only titanium, and essentially devoid of tungsten, over the insulative material and in contact with the oxide layer exposed through the via opening; disposing a thick layer over the titanium layer, including that portion of the titanium layer in the via opening, the thick layer comprising material selected from the group consisting of tungsten, molybdenum and alloys thereof and selected to improve thermal stability of the contact structure; selectively removing the thick layer in accordance with a first specified pattern; selectively removing the titanium layer in accordance with a second specified pattern; and annealing the contact structure at a temperature between about 550° C., and about 560° C. to cause the titanium layer to dissolve the oxide layer and form a contact having a resistance below about 100 ohms·μm 2 .
Claim 3
Dependent Claim
13 words
The method of claim 1 in which the titanium is deposited by sputtering.
Claim 4
Dependent Claim
20 words
The method of claim 1 in which the thick layer and the titanium layer are removed by reaction ion etching.
Claim 5
Dependent Claim
20 words
The method of claim 3 in which the thick layer is etched in an atmosphere of CCl 4 and oxygen.
Claim 6
Dependent Claim
20 words
The method of claim 3 in which the thick layer is etched in an atmosphere of SF 6 and chlorine.
Claim 7
Dependent Claim
27 words
The method of claim 3 in which the thick layer is etched in an atmosphere selected from the group consisting of SF 6 and CCl 4 .
Claim 8
Dependent Claim
24 words
The method of claim 3 in which the thick layer and the titanium layer are etched without breaking the vacuum of the etching system.
Claim 9
Dependent Claim
17 words
The method of claim 1 in which the annealing occurs at a temperature above about 400° C.
Claim 10
Dependent Claim
24 words
The method of claim 1 in which the annealing step occurs in an atmosphere selected from the group consisting of hydrogen and forming gas.
Claim 11
Dependent Claim
16 words
The method of claim 3 in which the thick layer and the titanium are wet etched.
Claim 12
Dependent Claim
32 words
The method of claim 1 wherein the thin titanium layer and the thick layer are both deposited by sputtering under vacuum conditions in a single pump-down and without breaking the vacuum conditions.
Claim 13
Dependent Claim
19 words
The method of claim 1 wherein the titanium layer is deposited to a thickness between 100 and 1,000 angstroms.
Claim 14
Dependent Claim
17 words
The method of claim 1 wherein the thick layer is no more than about 1,000 angstroms thick.
Claim 15
Dependent Claim
19 words
The method of claim 2 wherein the titanium layer is sputtered at a selected vacuum pressure and without heating.
Claim 16
Dependent Claim
32 words
The method of claim 7 wherein the thick layer is etched in an atmosphere of CCl 4 and oxygen and the titanium layer is etched in an atmosphere of CCl 4 .
References Cited (Backward Citations)
US3858304A
Cited
US4078963A
Cited
JPS5247384A
Cited
US4141022A
Cited
JPS5585042A
Cited
US4576678A
Cited
JPS56158423A
Cited
JPS587829A
Cited
US4390393A
Cited
US4473436A
Cited
US4478678A
Cited
US4595453A
Cited
US4640738A
Cited
JPS61214427A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-12-31 | 1994-07-02 | 1995-01-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-12-31 | 1998-07-02 | 1999-01-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-12-31 | 2002-07-02 | 2003-01-01 | $7700.00 | Window Closed / Lapsed |