Process for preparing hydroxyl polyester for use in a powder coating and a powder coating composition thereof
Assignee: KOREA CHEMICAL CO Inc
•
Filing: 1988-12-29
•
Granted: 1990-12-04
•
Expires: 2008-12-29
Abstract
Abstract A crystalline polyester resin derived from the reaction between a prepolymer and trimellitic anhydride in an amount of less than 10 wt % of the prepolymer where prepolymer as an intermediate product formed from the reaction between an alcohol mixture containing at least 40 mole % ethylene glycol and at least 30 mol % neopentyl glycol, and an acid mixture containing terephthalic acid or dimethyl terephthalate of at least 40 mole % and a linear dicarboxylic acid, or between an alcohol mixture containing 100 wt % terephthalic acid or dimethyl terephthalate. The crystalline polyester resin is very suitable for use in powder coating compositions and has a hyodroxyl number of 20 to 100, an average molecular weight of 1000 to 3500 and a melt viscosity at 160 DEG C. of 500 to 4000 cps as well as the characteristics of dense, regular, and repetitive structure.
Inventors
- 👤 Bong J. Kim
- 👤 Won S. Kim
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 20:17
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/78; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/42; C08G18/4205; C08G18/4208; C08G18/4211; C08G18/4219; C08G18/70; C08G18/72; C08G18/80; C08G18/8061; C08G18/807; C08G18/8074; C08G63/02; C08G63/12; C08G63/16; C08G63/20; C09; C09D; C09D167/00; C09D167/04; C09D175/00; C09D175/04; C09D175/06; C08G2150/00; C08G2150/20; C08G2250/00
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
66 words
A method of preparing a substantially linear crystalline polyester resin which comprises the following steps: (a) reacting an acid selected from the group consisting of terephthalic acid and dimethyl terephthalate with an alcohol mixture including ethylene glycol as a major component to form a prepolymer; and (b) reacting said prepolymer with trimellitic anhydride under a nitrogen gas atmosphere to form a substantially linear crystalline polyester resin.
Claim 2
Independent Claim
66 words
A method of preparing a substantially linear crystalline polyester resin which comprises the following steps: (a) reacting an acid selected from the group consisting of terephthalic acid and dimethyl terephthalate with an alcohol mixture including ethylene glycol as a major component to form a prepolymer; and (b) reacting said prepolymer with trimellitic anhydride under a nitrogen gas atmosphere to form a substantially linear crystalline polyester resin.
Claim 3
Dependent Claim
21 words
A method according to claim 1, wherein said acid further includes a linear dicarboxylic acid containing 4 to 12 carbon atoms.
Claim 4
Dependent Claim
51 words
The method of claim 2, wherein said acid includes one of said terephthalic acid or dimethyl terephthalate in an amount of at least 40 mole %, and said alcohol mixture includes ethylene glycol and neopentyl glycol in amounts of at least 40 mole % and at least 30 mole %, respectively.
Claim 5
Dependent Claim
26 words
The process of claim 1, wherein said alcohol mixture includes ethylene glycol, neopentyl glycol and any one of 1,4-butanediol, 1,6-hexanediol, 1,4-cyclohexane dimethanol, 1,5-pentanediol, and diethylene glycol.
Claim 6
Dependent Claim
23 words
The process of claim 1, wherein said trimellitic anhydride is present in an amount of less than 10 wt % of said prepolymer.
Claim 7
Dependent Claim
47 words
The process of claim 1, wherein antimony triacetate is used as a catalyst in amounts of 0.01 to 2 wt % of said total resin when said acid value of resin is as low as 5 during the second stage reaction of said trimellitic anhydride with prepolymer.
Claim 8
Dependent Claim
22 words
The process of claim 1, wherein said N 2 gas is added at a rate of from 2000 to 4000 cc/1 min.
Claim 9
Dependent Claim
38 words
The process of claim 1, wherein the final product has a melting viscosity of from 500 to 4,000 cps at 160° C., an average molecular weight of 1,000 to 3,500, and a hydroxyl number of 20 to 100.
Claim 10
Dependent Claim
29 words
A powder coating composition comprising: a blocked isocyanate, a flowing agent, a curing catalyst, a pigment, and a crystalline hydroxyl polyester produced according to the process of claim 1.
Claim 11
Dependent Claim
26 words
The process of claim 2, wherein said alcohol mixture includes ethylene glycol, neopentyl glycol and any one of 1,4-butanediol, 1,6-hexanediol, 1,4-cyclohexane dimethanol, 1,5-pentanediol, and diethylene glycol.
Claim 12
Dependent Claim
23 words
The process of claim 2, wherein said trimellitic anhydride is present in an amount of less than 10 wt % of said prepolymer.
Claim 13
Dependent Claim
47 words
The process of claim 2, wherein antimony triacetate is used as a catalyst in amounts of 0.01 to 2 wt % of said total resin when said acid value of resin is as low as 5 during the second stage reaction of said trimellitic anhydride with prepolymer.
Claim 14
Dependent Claim
22 words
The process of claim 2, wherein said N 2 gas is added at a rate of from 2000 to 4000 cc/1 min.
Claim 15
Dependent Claim
38 words
The process of claim 2, wherein the final product has a melting viscosity of from 500 to 4,000 cps at 160° C., an average molecular weight of 1,000 to 3,500, and a hydroxyl number of 20 to 100.
Claim 16
Dependent Claim
29 words
A powder coating composition comprising: a blocked isocyanate, a flowing agent, a curing catalyst, a pigment, and a crystalline hydroxyl polyester produced according to the process of claim 2.
References Cited (Backward Citations)
US4217440A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-12-03 | 1994-06-04 | 1994-12-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-12-03 | 1998-06-04 | 1998-12-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-12-03 | 2002-06-04 | 2002-12-04 | $7700.00 | Window Closed / Lapsed |