Method of electroless depositing of gold onto superconducting particles
Assignee: Northrop Grumman Corp
•
Filing: 1989-02-21
•
Granted: 1990-11-20
•
Expires: 2009-02-21
Abstract
Abstract A method of electroless deposition of gold from a solution onto ceramic oxide superconducting particles is characterized by the steps: (1) adding gold chloride to organic solvent-optional reducing agent for the gold chloride to provide a gold solution, (2) mixing the ceramic oxide superconducting particles with the gold solution, to provide a suspension, (3) optionally adding reducing agent for the gold chloride, (4) stirring and heating the suspension to deposit a layer of gold metal on the particles, and (5) separating the particles.
Inventors
- 👤 Robert G. Charles
- 👤 Graham A. Whitlow
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:06
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; C; C23; C23C; C23C18/00; C23C18/16; C23C18/31; C23C18/42; C23C18/44; Y; Y10; Y10S; Y10S505/00; Y10S505/725; Y10S505/739; Y10S505/775; Y10S505/785
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
183 words
A method of electroless deposition of gold from a solution onto ceramic oxide particles, comprising alkaline earth metal-copper oxide, comprising the steps: (1) adding gold chloride to at least one organic compound that is effective to act as solvent and optional reducing agent for the gold chloride, in a nonaqueous liquid environment non-reactive to subsequently added ceramic oxide particles, to provide a gold solution, (2) mixing ceramic oxide particles comprising alkaline earth metal-copper oxide having superconducting properties with the gold solution, to provide a suspension of the ceramic oxide particles in the gold solution, (3) optionally adding an organic compound that is effective to act as a reducing agent for gold chloride, (4) heating the suspension so that a layer of gold metal, from approximately 2 Angstroms to 1,000 Angstroms thick, deposits on the ceramic oxide particles, (5) separating the gold coated ceramic oxide particles, and (6) removing organic constituents from the gold coated ceramic oxide particles; where, if the organic compound added in step (1) does not act as a reducing agent, an organic compound reducing agent is added in step (3).
Claim 2
Independent Claim
183 words
A method of electroless deposition of gold from a solution onto ceramic oxide particles, comprising alkaline earth metal-copper oxide, comprising the steps: (1) adding gold chloride to at least one organic compound that is effective to act as solvent and optional reducing agent for the gold chloride, in a nonaqueous liquid environment non-reactive to subsequently added ceramic oxide particles, to provide a gold solution, (2) mixing ceramic oxide particles comprising alkaline earth metal-copper oxide having superconducting properties with the gold solution, to provide a suspension of the ceramic oxide particles in the gold solution, (3) optionally adding an organic compound that is effective to act as a reducing agent for gold chloride, (4) heating the suspension so that a layer of gold metal, from approximately 2 Angstroms to 1,000 Angstroms thick, deposits on the ceramic oxide particles, (5) separating the gold coated ceramic oxide particles, and (6) removing organic constituents from the gold coated ceramic oxide particles; where, if the organic compound added in step (1) does not act as a reducing agent, an organic compound reducing agent is added in step (3).
Claim 3
Dependent Claim
11 words
The method of claim 1 where the gold chloride is anhydrous.
Claim 4
Dependent Claim
37 words
The method of claim 1 where the alkaline earth metal-copper oxide is selected from the group consisting of yttrium-alkaline earth metal-copper oxide; rare earth metal-alkaline earth metal-copper oxide; bismuth-alkaline earth metal-copper oxide; and thallium-alkaline earth metal-copper oxide.
Claim 5
Dependent Claim
19 words
The method of claim 1 where the alkaline earth metal-copper oxide is YBa 2 Cu 3 O 7-x .
Claim 6
Dependent Claim
83 words
The method of claim 1 where the organic compound that is effective to act as solvent and optional reducing agent used in step (1) is selected from the group consisting of amino substituted benzene, halogen substituted benzene, hydrocarbon substituted benzene having a total of up to 12 carbon atoms as additions to the benzene ring, mono-hydroxyl substituted benzene, nitro substituted benzene, aliphatic alcohols having up to 8 carbon atoms, organic ethers containing up to a total of 12 carbon atoms; and mixtures thereof.
Claim 7
Dependent Claim
45 words
The method of claim 1 where the organic compound that is effective to act as a reducing agent for gold chloride which may be added in optional step (3) is selected from the group consisting of poly-hydroxyl substituted benzene, naphthohydroquinone, ascorbic acid, and mixtures thereof.
Claim 8
Dependent Claim
15 words
The method of claim 1 where the ceramic particles have diameters up to 10,000 Angstroms.
Claim 9
Dependent Claim
33 words
The method of claim 1 where the ceramic particles have diameters up to 1,000 Angstroms and the layer of gold metal deposited in step (4) is from 2 Angstroms to 100 Angstroms thick.
Claim 10
Dependent Claim
30 words
The method of claim 1 where organic compound is added in step (3) and the suspension is stirred and heated from approximately 30° C. to 100° C. in step (4).
Claim 11
Dependent Claim
22 words
The method of claim 1 where organic compound is added in step (3) and the suspension is heated prior to step (3).
Claim 12
Dependent Claim
21 words
The method of claim 1 where as a last step, the gold coated ceramic oxide particles are pressed into a structure.
Claim 13
Dependent Claim
27 words
The method of claim 5 where the ceramic oxide particles are suspended in the organic compound used in step (1) prior to mixing with the gold solution.
Claim 14
Independent Claim
142 words
A method of electroless deposition of gold from a solution onto ceramic oxide particles, comprising alkaline earth metal-copper oxides, comprising the steps: (1) adding gold chloride to at least one organic compound selected from the group consisting of nitrobenzene, methyl alcohol, ethyl alcohol, diethylether, and mixtures thereof, to provide a gold solution, (2) mixing ceramic oxide particles comprising alkaline earth metal-copper oxide having superconducting properties with the gold solution, to provide a suspension of the ceramic oxide particles in the gold solution, (3) mixing a reducing agent selected from the group consisting of hydroquinone, ascorbic acid, and mixtures thereof with the suspension of step (2) and stirring and heating the suspension admixture so that a layer of gold metal, from approximately 2 Angstroms to 1,000 Angstroms thick, deposits on the ceramic oxide particles, and (4) separating the gold coated ceramic oxide particles.
Claim 15
Independent Claim
142 words
A method of electroless deposition of gold from a solution onto ceramic oxide particles, comprising alkaline earth metal-copper oxides, comprising the steps: (1) adding gold chloride to at least one organic compound selected from the group consisting of nitrobenzene, methyl alcohol, ethyl alcohol, diethylether, and mixtures thereof, to provide a gold solution, (2) mixing ceramic oxide particles comprising alkaline earth metal-copper oxide having superconducting properties with the gold solution, to provide a suspension of the ceramic oxide particles in the gold solution, (3) mixing a reducing agent selected from the group consisting of hydroquinone, ascorbic acid, and mixtures thereof with the suspension of step (2) and stirring and heating the suspension admixture so that a layer of gold metal, from approximately 2 Angstroms to 1,000 Angstroms thick, deposits on the ceramic oxide particles, and (4) separating the gold coated ceramic oxide particles.
Claim 16
Dependent Claim
37 words
The method of claim 13 where the alkaline earth metal-copper oxide is selected from the group consisting of yttrium-alkaline earth metal-copper oxide; rare earth metal-alkaline earth metal-copper oxide; bismuth-alkaline earth metal-copper oxide; and thallium-alkaline earth metal-copper oxide.
References Cited (Backward Citations)
US2865376A
Cited
US3300328A
Cited
US3589916A
Cited
US4009297A
Cited
US4005229A
Cited
US4374876A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-11-19 | 1994-05-21 | 1994-11-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-11-19 | 1998-05-21 | 1998-11-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-11-19 | 2002-05-21 | 2002-11-20 | $7700.00 | Window Closed / Lapsed |