Assignee: Denso Corp
•
Filing: 1989-06-09
•
Granted: 1990-11-13
•
Expires: 2009-06-09
Abstract
Abstract Aqueous titanium tetrachloride solution, i.e., one component (X) for forming multi-component ceramic compound, and a suitable amount of zirconium oxynitrate, i.e., another component (Y) are mixed. Hydroxide coprecipitate of Ti4+ and Zr4+ containing the components is formed from the mixture solution. The coprecipitate is cleaned, dried, then calcined, for example, at 1100 DEG C., thus producing powder containing 0.32-micron particles. This powder is mixed with TiO2 and PbO, in a suitable amount to be added to the other component (Y) of the multi-component ceramic compound. The resultant mixture is calcined, for example, at 740 DEG for 1 hour, into fine powder containing 0.32-micron particles. The calcined powder is then press-molded, for example, under the pressure of 1 ton/cm2, then calcined, for example, at 1220 DEG C. for 1 hour, thereby forming multi-component ceramics.
Inventors
- 👤 Shin-ichi Shirasaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 19:32
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/48; C04B35/49; C04B35/491; C04B35/493
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
210 words
A method of producing Pb(Zr 0 .5 Ti 0 .5)O 3 , comprising the steps of: (1) adding an aqueous solution containing a titanium component to a solution containing a zirconium component; wherein the zirconium component is added in an amount necessary for producing said Pb(Zr 0 .5 Ti 0 .5)O 3 and a first portion of the titanium component is added in an amount which is not sufficient for producing said Pb(Zr 0 .5 Ti 0 .5)O 3 ; (2) adding the solutions in step (1) to a coprecipitate forming solution to form a coprecipitate containing the zirconium and titanium components from the solutions; (3) calcining the coprecipitate at a temperature of 700° to 1300° C., to form a fine modified powder made of particles having a diameter of 0.01 to 1.0 micron; and (4) mixing the powder produced in step (3) with a second portion of a titanium component and powders of components of the Pb(Zr 0 .5 Ti 0 .5)O 3 composition other than Zr and Ti; calcining the mixture at a temperature of 500° to 1300° C., to produce a calcined powder of a multi-component ceramic composition, and (5) molding the calcined powder and sintering the molded mixture at a temperature of 700° to 2000° C.
Claim 2
Independent Claim
210 words
A method of producing Pb(Zr 0 .5 Ti 0 .5)O 3 , comprising the steps of: (1) adding an aqueous solution containing a titanium component to a solution containing a zirconium component; wherein the zirconium component is added in an amount necessary for producing said Pb(Zr 0 .5 Ti 0 .5)O 3 and a first portion of the titanium component is added in an amount which is not sufficient for producing said Pb(Zr 0 .5 Ti 0 .5)O 3 ; (2) adding the solutions in step (1) to a coprecipitate forming solution to form a coprecipitate containing the zirconium and titanium components from the solutions; (3) calcining the coprecipitate at a temperature of 700° to 1300° C., to form a fine modified powder made of particles having a diameter of 0.01 to 1.0 micron; and (4) mixing the powder produced in step (3) with a second portion of a titanium component and powders of components of the Pb(Zr 0 .5 Ti 0 .5)O 3 composition other than Zr and Ti; calcining the mixture at a temperature of 500° to 1300° C., to produce a calcined powder of a multi-component ceramic composition, and (5) molding the calcined powder and sintering the molded mixture at a temperature of 700° to 2000° C.
Claim 3
Dependent Claim
40 words
A method according to claim 1, wherein the zirconium component is an aqueous zirconium solution, the first portion of the titanium component is an aqueous titanium tetrachloride solution, and the second portion of the titanium component contains TiO 2 .
Claim 4
Dependent Claim
33 words
A method according to claim 2, wherein the aqueous zirconium solution is formed from a compound selected from the group consisting of zirconium oxychloride, zirconium oxynitrate, zirconium chloride, zirconium nitride or metallic zirconium.
Claim 5
Dependent Claim
13 words
A method according to claim 1, wherein said coprecipitate-forming solution is ammonia water.
Claim 6
Independent Claim
199 words
A method of producing Pb(Zr 0 .05 Ti 0 .5)O 3 , comprising the steps of: (1) adding an aqueous solution containing a titanium component to a solution containing a zirconium, thereby forming a sol containing the components titanium and zirconium from the solutions, wherein the zirconium component is added in an amount necessary for producing said Pb(Zr 0 .5 Ti 0 .5)O 3 , and a first portion of the titanium component, is added in an amount not sufficient for producing said Pb(Zr 0 .5 Ti 0 .5)O 3 ; (2) calcining the sol at a temperature of 700° to 1300° C., to form a fine modified powder made of particles having a diameter of 0.01 to 1.0 micron; (3) mixing the modified powder produced in step (2) with a powder of a second portion of a titanium component and powders of components of the Pb(Zr 0 .5 Ti 0 .5)O 3 composition, other than zirconium and titanium, calcining the mixture at a temperature of 500° to 1300° C., to produce a calcined powder of multi-component ceramic composition; and (4) molding the calcined powder of step (3) and sintering the at a temperature of 700° to 2000° C.
Claim 7
Independent Claim
199 words
A method of producing Pb(Zr 0 .05 Ti 0 .5)O 3 , comprising the steps of: (1) adding an aqueous solution containing a titanium component to a solution containing a zirconium, thereby forming a sol containing the components titanium and zirconium from the solutions, wherein the zirconium component is added in an amount necessary for producing said Pb(Zr 0 .5 Ti 0 .5)O 3 , and a first portion of the titanium component, is added in an amount not sufficient for producing said Pb(Zr 0 .5 Ti 0 .5)O 3 ; (2) calcining the sol at a temperature of 700° to 1300° C., to form a fine modified powder made of particles having a diameter of 0.01 to 1.0 micron; (3) mixing the modified powder produced in step (2) with a powder of a second portion of a titanium component and powders of components of the Pb(Zr 0 .5 Ti 0 .5)O 3 composition, other than zirconium and titanium, calcining the mixture at a temperature of 500° to 1300° C., to produce a calcined powder of multi-component ceramic composition; and (4) molding the calcined powder of step (3) and sintering the at a temperature of 700° to 2000° C.
References Cited (Backward Citations)
US3963630A
Cited
SU829603A1
Cited
JPS6051664A
Cited
US4587225A
Cited
US4643984A
Cited
US4696810A
Cited
JPS6153114A
Cited
US4812426A
Cited
JPS62191465A
Cited
JPH01111918A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-11-12 | 1994-05-14 | 1994-11-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-11-12 | 1998-05-14 | 1998-11-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-11-12 | 2002-05-14 | 2002-11-13 | $7700.00 | Window Closed / Lapsed |