Method of fabricating thin layers from high-temperature oxide superconductors
Assignee: Forschungszentrum Jülich
•
Filing: 1989-02-13
•
Granted: 1990-10-23
•
Expires: 2009-02-13
Abstract
Abstract A method and apparatus for producing thin superconductor film of high temperature oxide type ceramic superconductors by cathodic sputtering and in which the highest possible oxygen partial pressure is utilized in the space between the cathode and the substrate. Ionizing radiation can be introduced into the space as well.
Inventors
- 👤 Ulrich Poppe
- 👤 Jurgen Schubert
- 👤 Wilhelm Evers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 10:43
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/08; C23C14/087; H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0296; H10N60/0408; Y; Y10; Y10S; Y10S505/00; Y10S505/725; Y10S505/73; Y10S505/731
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
118 words
A method of making a thin-layer superconductor body, comprising the steps of: (a) heating a substrate; (b) juxtaposing a cathodically poled target composed of a high-transition-temperature oxide with a critical temperature greater than 77 degrees K superconductor with said substrate; (c) providing an atmosphere ionized by glow discharge around said substrate and said target; (d) effecting cathodic atomization of said target and deposition of cathodically atomized material from said target onto the heated substrate in the presence of said atmosphere to form a thin-layer superconductor body on said substrate; and (e) maintaining a partial pressure of oxygen in said atmoshphere of at least 67 Pa and sustaining reactive cathodic deposition of said high-temperature oxide superconductor on said substrate.
Claim 2
Independent Claim
118 words
A method of making a thin-layer superconductor body, comprising the steps of: (a) heating a substrate; (b) juxtaposing a cathodically poled target composed of a high-transition-temperature oxide with a critical temperature greater than 77 degrees K superconductor with said substrate; (c) providing an atmosphere ionized by glow discharge around said substrate and said target; (d) effecting cathodic atomization of said target and deposition of cathodically atomized material from said target onto the heated substrate in the presence of said atmosphere to form a thin-layer superconductor body on said substrate; and (e) maintaining a partial pressure of oxygen in said atmoshphere of at least 67 Pa and sustaining reactive cathodic deposition of said high-temperature oxide superconductor on said substrate.
Claim 3
Dependent Claim
12 words
The method defined in claim 1 wherein said atmoshphere is pure oxygen.
Claim 4
Dependent Claim
36 words
The method defined in claim 1, further comprising the step of flushing said substrate with oxygen or ozone to increase the oyygen partial pressure at said substrate during the deposition of said material on said substrate.
Claim 5
Dependent Claim
68 words
The method defined in claim 1, further comprising the steps of supplying oxygen or ozone at said target and evacuating gas in the region of said substrate so as to generate a substantially laminar flow of the oxygen or ozone from said target to said substrate to increase the oxygen partial pessure and the deposition rate at said substrate during the deposition of said material on said substrate.
Claim 6
Dependent Claim
25 words
The method defined in claim 1, further comprising the step of introducing ionizing radiation into a gas space defined between said target and said substrate.
Claim 7
Dependent Claim
15 words
The method defined in claim 5 wherein microwave radiation is introduced into said gas spaced.
Claim 8
Dependent Claim
28 words
The method defined in claim 1, further comprising the step of exposing a surface of said substrate adapted to receive a deposit of said material with ultraviolet radiation.
Claim 9
Independent Claim
142 words
An apparatus for making a thin-layer superconductor body, comprising: a support for a substrate; means for heating said substrate; a cathodically poled target composed of a high-transition-temperature oxide superconductor with a critical temperature greater than 77 degrees K juxtaposed with said support and spaced therefrom so that a distance of 5 to 20 mm is maintained between said target and said substrate; means for providing an atmosphere ionized by glow discharge around said substrate and said target; means for effecting cathodic atomization of said target and depostion of cathodically atomized material from said target onto the heated substrate in the presence of said atmosphere to form a thin-layer superconductor body on said substrate; and means for maintaining a partial pressure of oxygen of at least 67 Pa in said atmosphere sustaining reactive cathodic deposition of said high-temperature oxide superconductor on said substrate.
Claim 10
Independent Claim
142 words
An apparatus for making a thin-layer superconductor body, comprising: a support for a substrate; means for heating said substrate; a cathodically poled target composed of a high-transition-temperature oxide superconductor with a critical temperature greater than 77 degrees K juxtaposed with said support and spaced therefrom so that a distance of 5 to 20 mm is maintained between said target and said substrate; means for providing an atmosphere ionized by glow discharge around said substrate and said target; means for effecting cathodic atomization of said target and depostion of cathodically atomized material from said target onto the heated substrate in the presence of said atmosphere to form a thin-layer superconductor body on said substrate; and means for maintaining a partial pressure of oxygen of at least 67 Pa in said atmosphere sustaining reactive cathodic deposition of said high-temperature oxide superconductor on said substrate.
Claim 11
Dependent Claim
25 words
The apparatus defined in claim 8, further comprising: a shield surrounding said cathodically poled target; and an insulator interposed between said shield and said target.
Claim 12
Dependent Claim
24 words
The apparatus defined in claim 9, further comprising means for introducing ionizing radiation into a gas space defined between said target and said substrate.
Claim 13
Dependent Claim
29 words
The apparatus defined in claim 10 wherein said means for introducing ionizing radiation into a gas space defined between said target and said substrate is a source of microwaves.
Claim 14
Dependent Claim
20 words
The apparatus defined in claim 9, further comprising means for irradiating a surface of said substrate with hard ultraviolet radiation.
Claim 15
Dependent Claim
19 words
The apparatus defined in claim 9, further comprising means for flushing a surface of said substrate with a gas.
Claim 16
Dependent Claim
20 words
The apparatus defined in claim 13, further comprising means for irradiating said surface of said substrate with hard ultraviolet radiation.
Claim 17
Dependent Claim
24 words
The apparatus defined in claim 14, further comprising means for introducing ionizing radiation into a gas space defined between said target and said substrate.
Claim 18
Dependent Claim
29 words
The apparatus defined in claim 15, wherein said means for introducing ionizing radiation into a gas space defined between said target and said substrate is a source of microwaves.
References Cited (Backward Citations)
US4842704A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-22 | 1994-04-23 | 1994-10-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-22 | 1998-04-23 | 1998-10-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-22 | 2002-04-23 | 2002-10-23 | $7700.00 | Window Closed / Lapsed |