US4965096A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for preparing improved lithium-silicate glare-reducing coating for a cathode-ray tube
Assignee: RCA Licensing Corp
•
Filing: 1988-08-25
•
Granted: 1990-10-23
•
Expires: 2008-08-25
Abstract
Abstract An antistatic, glare-reducing coating, as for the surface of the viewing surface of a CRT is prepared by (a) warming a glass support surface above room temperature, (b) coating a surface of the warm support with an aqueous solution containing a lithium-stabilized silica sol and an inorganic metallic compound, and drying the deposited coating, (c) heating the glass support surface and the coating to a temperature of about 65° C. for about 30 seconds, and (d) washing and then drying the coating.
Inventors
- 👤 Samuel B. Deal
- 👤 Donald W. Bartch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 08:05
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/25; H; H01; H01J; H01J29/00; H01J29/02; H01J29/10; H01J29/18; H01J29/24; H01J29/86; H01J29/89; H01J29/896; H01J9/00; H01J9/20; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/23; C03C2218/00; C03C2218/10; C03C2218/11; C03C2218/113
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
93 words
A method for preparing an optical viewing screen having a glare-reducing viewing surface comprising (a) warming a glass support to a temperature of about 50° C., (b) coating a surface of said warm support with an aqueous solution containing lithium-stabilized silica sol, and drying the deposited coating, (c) exposing said surface of said support and said deposited coating to a heat source for about 30 seconds to raise said surface and said deposited coating to a temperature of about 65° C., (d) washing said dry coating with water, and (e) drying said coating.
Claim 2
Independent Claim
93 words
A method for preparing an optical viewing screen having a glare-reducing viewing surface comprising (a) warming a glass support to a temperature of about 50° C., (b) coating a surface of said warm support with an aqueous solution containing lithium-stabilized silica sol, and drying the deposited coating, (c) exposing said surface of said support and said deposited coating to a heat source for about 30 seconds to raise said surface and said deposited coating to a temperature of about 65° C., (d) washing said dry coating with water, and (e) drying said coating.
Claim 3
Independent Claim
135 words
A method for preparing an optical viewing screen having an antistatic, glare-reducing viewing surface for a cathode-ray tube comprising (a) warming a glass faceplate to a temperature of about 50° C., (b) coating an exterior surface of said warm faceplate with an aqueous solution containing lithium-stabilized silica sol and an inorganic metallic compound selected from the group consisting of palladium sulfate, tin sulfate, tin chloride and gold chloride present in a concentration within the range of 0.005 to 0.02 weight percent for imparting antistatic characteristics to said coating, and drying the deposited coating, (c) reheating the exterior surface of said faceplate and said deposited coating to a temperature of about 65° C. for 30 seconds without substantially heating the body of said faceplate, (d) washing said dry coating with water, and (e) drying said coating.
Claim 4
Independent Claim
135 words
A method for preparing an optical viewing screen having an antistatic, glare-reducing viewing surface for a cathode-ray tube comprising (a) warming a glass faceplate to a temperature of about 50° C., (b) coating an exterior surface of said warm faceplate with an aqueous solution containing lithium-stabilized silica sol and an inorganic metallic compound selected from the group consisting of palladium sulfate, tin sulfate, tin chloride and gold chloride present in a concentration within the range of 0.005 to 0.02 weight percent for imparting antistatic characteristics to said coating, and drying the deposited coating, (c) reheating the exterior surface of said faceplate and said deposited coating to a temperature of about 65° C. for 30 seconds without substantially heating the body of said faceplate, (d) washing said dry coating with water, and (e) drying said coating.
Claim 5
Dependent Claim
23 words
The method defined in claim 1 wherein, at step (a), said glass support is heated to temperatures of about 48° to 50° C.
Claim 6
Dependent Claim
23 words
The method defined in claim 2 wherein, at step (a), said glass faceplate is heated to temperatures of about 48° to 50° C.
Claim 7
Independent Claim
118 words
A method for preparing an optical viewing screen having an antistatic, glare-reducing viewing surface for a cathode-ray tube comprising (a) warming a glass faceplate of said tube to about 48° to 50° C., (b) coating an exterior surface of said warm faceplate with an aqueous solution containing lithium-stabilized silica sol and a palladium compound in a concentration within the range of 0.005 to 0.02 weight percent for imparting an antistatic characteristic to said coating, and drying the deposited coating, (c) reheating the exterior surface of said faceplate for about 30 seconds to a temperature of about 65° C. without substantially heating the body of the faceplate, (d) washing said dry coating with water, and (e) drying said coating.
Claim 8
Independent Claim
118 words
A method for preparing an optical viewing screen having an antistatic, glare-reducing viewing surface for a cathode-ray tube comprising (a) warming a glass faceplate of said tube to about 48° to 50° C., (b) coating an exterior surface of said warm faceplate with an aqueous solution containing lithium-stabilized silica sol and a palladium compound in a concentration within the range of 0.005 to 0.02 weight percent for imparting an antistatic characteristic to said coating, and drying the deposited coating, (c) reheating the exterior surface of said faceplate for about 30 seconds to a temperature of about 65° C. without substantially heating the body of the faceplate, (d) washing said dry coating with water, and (e) drying said coating.
References Cited (Backward Citations)
US3114668A
Cited
US3635751A
Cited
US3898509A
Cited
US3689312A
Cited
US3940511A
Cited
JPS5113487A
Cited
US4563612A
Cited
US4560581A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-22 | 1994-04-23 | 1994-10-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-22 | 1998-04-23 | 1998-10-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-22 | 2002-04-23 | 2002-10-23 | $7700.00 | Window Closed / Lapsed |