US4963603A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Composite fiberboard and process of manufacture
Assignee: AWI Licensing LLC
•
Filing: 1989-11-15
•
Granted: 1990-10-16
•
Expires: 2009-11-15
Abstract
Abstract A novel composite board of mineral wool, perlite, and cellulosic newsprint fibers for use primarily as a ceiling tile is disclosed. The board displays virtually no sag (less than 200 mils) when exposed to high temperature and high humidity while displaying quite acceptable strength. The board, or product without mineral wool or perlite, is manufactured by selective deposition of a latex composition on the cellulosic newsprint fibers.
Inventors
- 👤 John Felegi, Jr.
- 👤 Kenneth P. Kehrer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 23:57
CPC Classifications
C; C04; C04B; C04B26/00; C04B26/02; C04B26/04; D; D21; D21H; D21H13/00; D21H13/36; D21H13/38; D21H13/40; D21H19/00; D21H19/36; D21H19/44; D21H19/56; D21H19/58; D21H23/00; D21H23/76; D21H23/765
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
158 words
A composite board which comprises up to 87% by weight mineral wool, 5-65% by weight perlite, up to 25% by weight clay, 4-35% by weight cellulosic newsprint composed primarily of cellulosic fibers, and 2-15% by weight of a thermoplastic polymeric binder having a glass transition temperature of from 80° C. to 115° C., the ratio of said binder to said cellulosic newsprint being no greater than about 1.25 when said cellulosic newsprint content is less than 6% by weight and said ratio being no greater than 0.7 when said cellulosic newsprint content is at Ieast 6% by weight, wherein the cellulose fibers in said board are substantially completely coated with said thermoplastic binder, said board displaying a sag of less than 200 mils when a 0.6 inch thick sample, 9 inches wide and 24 inches long is supported at both ends and exposed to a temperature of 85° F. and a relative humidity of 95% for 24 hours.
Claim 2
Dependent Claim
158 words
A composite board which comprises up to 87% by weight mineral wool, 5-65% by weight perlite, up to 25% by weight clay, 4-35% by weight cellulosic newsprint composed primarily of cellulosic fibers, and 2-15% by weight of a thermoplastic polymeric binder having a glass transition temperature of from 80° C. to 115° C., the ratio of said binder to said cellulosic newsprint being no greater than about 1.25 when said cellulosic newsprint content is less than 6% by weight and said ratio being no greater than 0.7 when said cellulosic newsprint content is at Ieast 6% by weight, wherein the cellulose fibers in said board are substantially completely coated with said thermoplastic binder, said board displaying a sag of less than 200 mils when a 0.6 inch thick sample, 9 inches wide and 24 inches long is supported at both ends and exposed to a temperature of 85° F. and a relative humidity of 95% for 24 hours.
Claim 3
Dependent Claim
158 words
A composite board which comprises up to 75% by weight mineral wool, 5-65% by weight perlite, up to 25% by weight clay, 4-35% by weight cellulosic newsprint composed primarily of cellulosic fibers, and 4-15% by weight of a thermoplastic polymeric binder having a glass transition temperature of from 80° C. to 115° C., the ratio of said binder to said cellulosic newsprint being no greater than about 1 when said cellulosic newsprint content is less than 6% by weight and said ratio being no greater than 0.4 when said cellulosic newsprint content is at least 6% by weight, wherein the cellulose fibers in said board are substantially completely coated with said thermoplastic binder, said board displaying a sag of less than 200 mils when a 0.6 inch thick sample, 9 inches wide and 24 inches long is supported at both ends and exposed to a temperature of 85° F. and a relative humidity of 95% for 24 hours.
Claim 4
Dependent Claim
158 words
A composite board which comprises up to 75% by weight mineral wool, 5-65% by weight perlite, up to 25% by weight clay, 4-35% by weight cellulosic newsprint composed primarily of cellulosic fibers, and 4-15% by weight of a thermoplastic polymeric binder having a glass transition temperature of from 80° C. to 115° C., the ratio of said binder to said cellulosic newsprint being no greater than about 1 when said cellulosic newsprint content is less than 6% by weight and said ratio being no greater than 0.4 when said cellulosic newsprint content is at least 6% by weight, wherein the cellulose fibers in said board are substantially completely coated with said thermoplastic binder, said board displaying a sag of less than 200 mils when a 0.6 inch thick sample, 9 inches wide and 24 inches long is supported at both ends and exposed to a temperature of 85° F. and a relative humidity of 95% for 24 hours.
Claim 5
Dependent Claim
128 words
A composite board which comprises about 20-50% by weight mineral wool, about 20-50% by weight perlite, up to 25% by weight clay, 10-30% by weight cellulosic newsprint composed primarily of cellulosic fibers, and 4-15% by weight of a thermoplastic polymeric binder having a glass transition temperature of from 80° C. to 115° C., the ratio of said binder to said cellulosic newsprint being no greater than about 0.7, wherein the cellulosic fibers in said board are substantially completely coated with said thermoplastic binder, said board displaying a sag of less than 200 mils when a 0.6 inch thick sample, 9 inches wide and 24 inches long is supported at both ends and exposed to a temperature of 85° F. and a relative humidity of 95% for 24 hours.
Claim 6
Dependent Claim
128 words
A composite board which comprises about 20-50% by weight mineral wool, about 20-50% by weight perlite, up to 25% by weight clay, 10-30% by weight cellulosic newsprint composed primarily of cellulosic fibers, and 4-15% by weight of a thermoplastic polymeric binder having a glass transition temperature of from 80° C. to 115° C., the ratio of said binder to said cellulosic newsprint being no greater than about 0.7, wherein the cellulosic fibers in said board are substantially completely coated with said thermoplastic binder, said board displaying a sag of less than 200 mils when a 0.6 inch thick sample, 9 inches wide and 24 inches long is supported at both ends and exposed to a temperature of 85° F. and a relative humidity of 95% for 24 hours.
Claim 7
Dependent Claim
146 words
A composite board which comprises about 20-50% by weight mineral wool, about 20-50% by weight perlite, up to 25% by weight clay. 10-30% by weight cellulosic newsprint composed primarily of cellulosic fibers, and 4-15% by weight of a thermoplastic polymeric binder having a glass transition temperature of from 80° C. to 115° C., the ratio of said binder to said cellulosic newsprint being no greater than about 0.7, wherein the cellulosic fibers in said board are substantially completely coated with said thermoplastic binder, said board displaying a sag of less than 200 mils when a 0.6 inch thick sample, 9 inches wide and 24 inches long is supported at both ends and exposed to a temperature of 85° F. and a relative humidity of 95% for 24 hours, and a modulus of rupture, as measured by the procedure in ASTM D-1087, of greater than 150 psi.
Claim 8
Dependent Claim
146 words
A composite board which comprises about 20-50% by weight mineral wool, about 20-50% by weight perlite, up to 25% by weight clay. 10-30% by weight cellulosic newsprint composed primarily of cellulosic fibers, and 4-15% by weight of a thermoplastic polymeric binder having a glass transition temperature of from 80° C. to 115° C., the ratio of said binder to said cellulosic newsprint being no greater than about 0.7, wherein the cellulosic fibers in said board are substantially completely coated with said thermoplastic binder, said board displaying a sag of less than 200 mils when a 0.6 inch thick sample, 9 inches wide and 24 inches long is supported at both ends and exposed to a temperature of 85° F. and a relative humidity of 95% for 24 hours, and a modulus of rupture, as measured by the procedure in ASTM D-1087, of greater than 150 psi.
Claim 9
Dependent Claim
31 words
A composite board as in claim 4 comprising 20-40% mineral wool, 20-35% perlite, 10-30% cellulosic newsprint and 6-10% latex having a glass transition temperature of from 80° C. to 115° C.
Claim 10
Dependent Claim
31 words
A composite board as in claim 4 comprising 20-40% mineral wool, 20-35% perlite, 10-30% cellulosic newsprint and 6-10% latex having a glass transition temperature of from 100° C. to 115° C.
Claim 11
Dependent Claim
35 words
A composite board as in claim 4 comprising about 20-50% mineral wool, about 20.50% perlite, about 13-23% cellulosic newsprint, and about 4-0.6% latex having a glass transition temperature of from 100° C. to 115° C.
Claim 12
Dependent Claim
46 words
A composite board as in claim 4 comprising about 35% mineral wool, about 30% perlite, about 25% cellulosic newsprint, about 8.5-10% latex having a glass transition temperature of 100° C. and where the ratio of said latex to said cellulosic newsprint is no greater than 0.4.
Claim 13
Dependent Claim
118 words
In the process for making a product containing at least the components of 4-35% by weight cellulosic newsprint composed primarily of cellulose fibers, and 2-15% by weight of a thermoplastic polymeric binder wherein the components are mixed with water to form an aqueous slurry, and said slurry is flocculated While being fed to a mold and shaped, the shaped material drained of liquid and pressed into the shape and thickness of said product and then heated to solidify said product, the improvement wherein said polymeric binder is coated on the cellulose fibers of the newsprint substantially completely before the slurry is fed to the mold and the ratio of binder-to-cellulosic newsprint used is no greater than about 1.25.
Claim 14
Dependent Claim
118 words
In the process for making a product containing at least the components of 4-35% by weight cellulosic newsprint composed primarily of cellulose fibers, and 2-15% by weight of a thermoplastic polymeric binder wherein the components are mixed with water to form an aqueous slurry, and said slurry is flocculated While being fed to a mold and shaped, the shaped material drained of liquid and pressed into the shape and thickness of said product and then heated to solidify said product, the improvement wherein said polymeric binder is coated on the cellulose fibers of the newsprint substantially completely before the slurry is fed to the mold and the ratio of binder-to-cellulosic newsprint used is no greater than about 1.25.
Claim 15
Dependent Claim
121 words
In the process for making a composite board containing at least the components of mineral wool perlite. 10-30% by weight cellulosic newsprint composed primarily of cellulose fibers, and 4-15% by weight of a thermoplastic polymeric binder wherein the components are mixed with water to form an aqueous slurry, and said slurry is flocculated while being fed to a mold and shaped, the shaped material drained of liquid and pressed into the shape and thickness of said board and then heated to solidify said board, the improvement wherein said polymeric binder is coated on the cellulose fibers of the newsprint substantially completely before the slurry is fed to the mold and the ratio of binder-to-cellulosic newsprint used is no greater than 0.7.
Claim 16
Dependent Claim
121 words
In the process for making a composite board containing at least the components of mineral wool perlite. 10-30% by weight cellulosic newsprint composed primarily of cellulose fibers, and 4-15% by weight of a thermoplastic polymeric binder wherein the components are mixed with water to form an aqueous slurry, and said slurry is flocculated while being fed to a mold and shaped, the shaped material drained of liquid and pressed into the shape and thickness of said board and then heated to solidify said board, the improvement wherein said polymeric binder is coated on the cellulose fibers of the newsprint substantially completely before the slurry is fed to the mold and the ratio of binder-to-cellulosic newsprint used is no greater than 0.7.
Claim 17
Dependent Claim
27 words
A process as in claim 10 wherein said thermoplastic binder is an anionic latex dispersion in which the latex particle diameter is no greater than 0.12 micron.
Claim 18
Dependent Claim
30 words
A process as in claim 10 wherein said thermoplastic binder is an anionic latex dispersion and a coagulant is added to the mixture of components before said slurry is flocculated.
Claim 19
Dependent Claim
68 words
A process as in claim 12 wherein said mixture is formed in two steps, the first step in which only water, newsprint composed primarily of cellulose fibers, coagulant and a portion of the anionic latex dispersion are used to form the mixture and the second step in which the remaining components and the remainder of said latex dispersion and, optionally, additional coagulant are added to form the mixture.
Claim 20
Dependent Claim
105 words
In the process for making a product containing at least the components of 4-35% by weight cellulosic newsprint composed primarily of cellulose fibers, and 2-15% by weight of a thermoplastic polymeric binder wherein the components are mixed with water to form an aqueous slurry, and said slurry is flocculated while being fed to a mold and shaped, the shaped material drained of liquid and pressed into the shape and thickness of said product and then heated to solidify said product, the improvement wherein said polymeric binder is coated on the cellulose fibers of the newsprint substantially completely before the slurry is fed to the mold.
Claim 21
Dependent Claim
105 words
In the process for making a product containing at least the components of 4-35% by weight cellulosic newsprint composed primarily of cellulose fibers, and 2-15% by weight of a thermoplastic polymeric binder wherein the components are mixed with water to form an aqueous slurry, and said slurry is flocculated while being fed to a mold and shaped, the shaped material drained of liquid and pressed into the shape and thickness of said product and then heated to solidify said product, the improvement wherein said polymeric binder is coated on the cellulose fibers of the newsprint substantially completely before the slurry is fed to the mold.
References Cited (Backward Citations)
US4711685A
Cited
EP0266850A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-15 | 1994-04-16 | 1994-10-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-15 | 1998-04-16 | 1998-10-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-15 | 2002-04-16 | 2002-10-16 | $7700.00 | Window Closed / Lapsed |