Gold diffusion method for semiconductor devices of high switching speed
Assignee: Sanken Electric Co Ltd
•
Filing: 1989-12-12
•
Granted: 1990-10-16
•
Expires: 2009-12-12
Abstract
Abstract Gold is diffused into a silicon substrate by first depositing an ultrathin layer of gold on one of the main faces of the substrate and then by heating the substrate to a temperature range of about 300°-850° C., instead of to about 1000° according to the prior art. Then, following the removal of the remaining gold layer from over the substrate, the latter is reheated to a higher temperature ranging from about 700° C. to about 1000° C. for activating the diffused gold. The gold diffusion at the reduced temperature serves to decrease the surface irregularities of the substrate as a result of gold-silicon alloy zones created at the interface between gold layer and silicon substrate during the thermal diffusion process.
Inventors
- 👤 Yutaka Yoshizawa
- 👤 Akira Uemura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 09:02
CPC Classifications
H; H10; H10P; H10P32/00; H10P32/10; H10P32/14; H10P32/18; H10P32/17; H10P32/171; H10P36/00; H10P95/00; H10P95/90; Y; Y10; Y10S; Y10S148/00; Y10S148/038; Y10S148/062; Y10S438/00; Y10S438/904
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
105 words
In the fabrication of a semiconductor device capable of high-speed switching operation, a method of gold diffusion which comprises: (a) providing a semiconductor substrate having a pair of opposite main faces; (b) forming a layer of gold on one of the main faces of the semiconductor substrate; (c) causing the diffusion of gold from the gold layer into the semiconductor substrate by heating the semiconductor substrate to a first predetermined temperature; (d) removing the remaining gold layer from the semiconductor substrate; and (e) activating the diffused gold by heating the semiconductor substrate to a second predetermined temperature that is higher than the first predetermined temperature.
Claim 2
Dependent Claim
105 words
In the fabrication of a semiconductor device capable of high-speed switching operation, a method of gold diffusion which comprises: (a) providing a semiconductor substrate having a pair of opposite main faces; (b) forming a layer of gold on one of the main faces of the semiconductor substrate; (c) causing the diffusion of gold from the gold layer into the semiconductor substrate by heating the semiconductor substrate to a first predetermined temperature; (d) removing the remaining gold layer from the semiconductor substrate; and (e) activating the diffused gold by heating the semiconductor substrate to a second predetermined temperature that is higher than the first predetermined temperature.
Claim 3
Dependent Claim
34 words
The gold diffusion method of claim 1 wherein the first predetermined temperature is in the range of about 300°-850° C., and wherein the second predetermined temperature is in the range of about 700°-1100° C.
Claim 4
Dependent Claim
23 words
The gold diffusion method of claim 2 wherein the second predetermined temperature is at least 50° C. higher than the first predetermined temperature.
Claim 5
Dependent Claim
16 words
The gold diffusion method of claim 1 wherein the gold layer is formed by vapor deposition.
Claim 6
Independent Claim
226 words
A method of fabricating a semiconductor device capable of high-speed switching operation, which method comprises: (a) providing a semiconductor substrate comprising a first region of a first conductivity type exposed at part of a first of a pair of opposite main faces of the substrate, and a second region of a second conductivity type, opposite to the first conductivity type, disposed contiguous to the first region and exposed at the first main face of the substrate so as to surround the first region, the first and second regions creating a pn-junction therebetween; (b) forming an insulating covering on the first main face of the semiconductor substrate, the insulating covering having an aperture exposing part of the first semiconductor region; (c) forming a layer of gold at least on that part of the first semiconductor region which is exposed through the aperture in the insulating covering; (d) causing the diffusion of gold from the gold layer into the semiconductor substrate by heating the semiconductor substrate, with the insulating covering formed thereon, to a first predetermined temperature; (e) removing the remaining gold layer from the exposed surface of the first semiconductor region; (f) activating the diffused gold by heating the semiconductor substrate to a second predetermined temperature that is higher than the first predetermined temperature; and (g) forming an electrode in electrical connection to the first semiconductor region.
Claim 7
Independent Claim
226 words
A method of fabricating a semiconductor device capable of high-speed switching operation, which method comprises: (a) providing a semiconductor substrate comprising a first region of a first conductivity type exposed at part of a first of a pair of opposite main faces of the substrate, and a second region of a second conductivity type, opposite to the first conductivity type, disposed contiguous to the first region and exposed at the first main face of the substrate so as to surround the first region, the first and second regions creating a pn-junction therebetween; (b) forming an insulating covering on the first main face of the semiconductor substrate, the insulating covering having an aperture exposing part of the first semiconductor region; (c) forming a layer of gold at least on that part of the first semiconductor region which is exposed through the aperture in the insulating covering; (d) causing the diffusion of gold from the gold layer into the semiconductor substrate by heating the semiconductor substrate, with the insulating covering formed thereon, to a first predetermined temperature; (e) removing the remaining gold layer from the exposed surface of the first semiconductor region; (f) activating the diffused gold by heating the semiconductor substrate to a second predetermined temperature that is higher than the first predetermined temperature; and (g) forming an electrode in electrical connection to the first semiconductor region.
Claim 8
Dependent Claim
22 words
The method of claim 5 wherein the insulating covering is a lamination of a silicon oxide layer and a silicon nitride layer.
Claim 9
Dependent Claim
30 words
The method of claim 5 wherein the gold layer is formed by vapor deposition on the exposed surface of the first semiconductor region as well as on the insulating covering.
Claim 10
Independent Claim
227 words
A method of fabricating a semiconductor device capable of high-speed switching operation, which method comprises: (a) providing a semiconductor substrate comprising a first region of a first conductivity type exposed at part a first of a pair of opposite main faces of the substrate, and a second region of a second conductivity type, opposite to the first conductivity type, disposed contiguous to the first region and exposed at the first main face of the substrate so as to surround the first region, the first and second regions creating a pn-junction therebetween, the semiconductor substrate having an insulating covering on the first main face of the semiconductor substrate, the insulating covering having an aperture exposing part of the first semiconductor region; (b) forming a layer of gold at least on that part of the first semiconductor region which is exposed through the aperture in the insulating covering; (c) causing the diffusion of gold from the gold layer into the semiconductor substrate by heating the semiconductor substrate, with the insulating covering formed thereon, to a first predetermined temperature; (d) removing the remaining gold layer from the exposed surface of the first semiconductor region; (e) activating the diffused gold by heating the semiconductor substrate to a second predetermined temperature that is higher than the first predetermined temperature; and (f) forming an electrode in electrical connection to the first semiconductor region.
Claim 11
Independent Claim
227 words
A method of fabricating a semiconductor device capable of high-speed switching operation, which method comprises: (a) providing a semiconductor substrate comprising a first region of a first conductivity type exposed at part a first of a pair of opposite main faces of the substrate, and a second region of a second conductivity type, opposite to the first conductivity type, disposed contiguous to the first region and exposed at the first main face of the substrate so as to surround the first region, the first and second regions creating a pn-junction therebetween, the semiconductor substrate having an insulating covering on the first main face of the semiconductor substrate, the insulating covering having an aperture exposing part of the first semiconductor region; (b) forming a layer of gold at least on that part of the first semiconductor region which is exposed through the aperture in the insulating covering; (c) causing the diffusion of gold from the gold layer into the semiconductor substrate by heating the semiconductor substrate, with the insulating covering formed thereon, to a first predetermined temperature; (d) removing the remaining gold layer from the exposed surface of the first semiconductor region; (e) activating the diffused gold by heating the semiconductor substrate to a second predetermined temperature that is higher than the first predetermined temperature; and (f) forming an electrode in electrical connection to the first semiconductor region.
References Cited (Backward Citations)
US3184347A
Cited
US3473976A
Cited
US3440113A
Cited
US3645808A
Cited
US3864174A
Cited
US3941625A
Cited
US3943013A
Cited
JPS5455372A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-15 | 1994-04-16 | 1994-10-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-15 | 1998-04-16 | 1998-10-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-15 | 2002-04-16 | 2002-10-16 | $7700.00 | Window Closed / Lapsed |