Heat-shrinkable laminated film
Assignee: Kureha Corp
•
Filing: 1989-02-28
•
Granted: 1990-10-16
•
Expires: 2009-02-28
Abstract
Abstract A heat-shrinkable laminated film suitable for a packaging film, having at least two layers of a mixed aliphatic polyamide resin layer (A) of 55 to 90 wt. % of an aliphatic polyamide resin with a crystalline melting point of 175° to 240° C. and 45 to 10 wt % of an aliphatic polyamide resin with a crystalline melting point of from not less than 120° C. to less than 175° C.; and a mixed resin layer (B) of a saponified ethylene-vinyl acetate copolymer as the main constituent. These laminated films have excellent gas barrier properties, stretchability, uniform heat-shrinkability and useful dimensional stability.
Inventors
- 👤 Yoshiharu Nishimoto
- 👤 Kengo Yamazaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 23:22
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/28; B32B7/00; B32B7/04; B32B7/12; B32B27/06; B32B27/08; B32B27/32; B32B27/34; B32B2307/00; B32B2307/70; B32B2307/732; B32B2307/734; B32B2307/736; B32B2377/00; B32B2439/00; B32B2439/70; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/31504; Y10T428/31725; Y10T428/31739; Y10T428/31743; Y10T428/31746
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
111 words
A heat-shrinkable laminated film of at least two layers comprising: a mixed aliphatic polyamide resin layer (A) comprising 55 to 90 wt % of an aliphatic polyamide resin having a crystalline melting point of 175° to 240° C. and 45 to 10 wt % of an aliphatic polyamide resin having a crystalline melting point of from not less than 120° C. to less than 175° C., and a mixed resin layer (B) comprising 70 to 90% of a saponified ethylene-vinyl acetate copolymer and 30 to 1 wt % of a resin selected from the group consisting of a polyester elastomer, a polyamide elastomer, an ethylene-vinyl carboxylate copolymer and an ethylene-acrylate copolymer.
Claim 2
Dependent Claim
111 words
A heat-shrinkable laminated film of at least two layers comprising: a mixed aliphatic polyamide resin layer (A) comprising 55 to 90 wt % of an aliphatic polyamide resin having a crystalline melting point of 175° to 240° C. and 45 to 10 wt % of an aliphatic polyamide resin having a crystalline melting point of from not less than 120° C. to less than 175° C., and a mixed resin layer (B) comprising 70 to 90% of a saponified ethylene-vinyl acetate copolymer and 30 to 1 wt % of a resin selected from the group consisting of a polyester elastomer, a polyamide elastomer, an ethylene-vinyl carboxylate copolymer and an ethylene-acrylate copolymer.
Claim 3
Dependent Claim
46 words
The heat-shrinkable laminated film according to claim 1, wherein said aliphatic polyamide resin having a crystalline melting point of 175° to 240° C. is one selected from the group consisting of nylon 6, nylon 69, nylon 610, nylon 612, nylon 6-66, nylon 6-69 and nylon 6-12.
Claim 4
Dependent Claim
47 words
The heat-shrinkable laminated film according to claim 1, wherein said aliphatic polyamide resin having a crystalline melting point of from not less than 120° C. to less than 175° C. is one selected from the group consisting of nylon 6-69, nylon 6-12, nylon 6-66-610 and nylon 6-66-610-12.
Claim 5
Dependent Claim
28 words
The heat-shrinkable laminated film according to claim 1, wherein the thickness of said layer (A) is 1.1 to 3 times as large as that of said layer (B).
Claim 6
Dependent Claim
16 words
The heat-shrinkable laminated film according to claim 1, further comprising at least one olefin resin layer.
Claim 7
Dependent Claim
31 words
The heat-shrinkable laminated film according to claim 5, further comprising an adhesive layer disposed between said olefin layer and said layer (A) or between said olefin layer and said layer (B).
Claim 8
Dependent Claim
103 words
The heat-shrinkable laminated film according to claim 5, wherein said olefin resin is one selected from a group consisting of a copolymer of ethylene and a vinyl ester monomer, a copolymer of ethylene and a monomer selected from an aliphatic unsaturated carboxylic acid and an aliphatic unsaturated carboxylate, an ionomer resin, a linear low-density polyethylene, a mixed resin of a linear low-density polyethylene and an ethylene vinyl acetate copolymer, a very low-density polyethylene, a mixed resin of a very low-density polyethylene and a small amount of linear low-density polyethylene, and a mixed resin of a crystalline propylene-ethylene random copolymer and a polypropylene elastomer.
References Cited (Backward Citations)
JPS52115880A
Cited
JPS56136365A
Cited
US4361628A
Cited
US4695491A
Cited
US4764406A
Cited
EP0216094A1
Cited
US4818588A
Cited
EP0252597A2
Cited
US4735855A
Cited
US4734327A
Cited
EP0277839A2
Cited
EP0278695A1
Cited
US4784863A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-15 | 1994-04-16 | 1994-10-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-15 | 1998-04-16 | 1998-10-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-15 | 2002-04-16 | 2002-10-16 | $7700.00 | Window Closed / Lapsed |