Zeolitic copper catalyst

Claim 2

A zeolitic copper composition having enhanced resistance to loss of catalytic activity on exposure to steam at high temperature, said composition comprising a copper-loaded crystalIine zeolite incorporated in a silica-alumina or an alumina binder, with said zeolite characterized by a silica to alumina ration of 20:1 to about 100:1, a pore size of about 5 to 13 Angstroms, and a copper content of at least 2 wt % to about 130 wt % of said zeolitic alumina, said copper-loaded zeolite being intimately associated with a steam stabilizing amount of an inorganic compound selected from the group consisting of titanium compounds, zirconium compounds and mixtures thereof.

Claim 3

The composition of claim 1 wherein said crystalline zeolite has the crystal structure of ZSM-5, ZSM-11, ZSM-12, ZSM-22, ZSM-23, ZSM-35, ZSM-38, ZSM-48, mordenite, dealuminated Y or Zeolite Beta.

Claim 4

The composition described in claim 2 wherein said crystalline zeolite has the structure of ZSM-5 and said copper-loaded zeolite is incorporated with a silica-alumina binder.

Claim 5

The composition described in claim 2 wherein said crystalline zeolite has the structure of ZSM-5 and said composition is coated on a monolith.

Claim 6

The composition described in claim 2 containing about 1 to 20 wt % of titanium or zirconium or mixture thereof.

Claim 7

The composition described in claim 3 containing about 1 to 20 wt % of titanium or zirconium or mixture thereof.

Claim 8

The composition described in claim 4 containing about 1 to 20 wt % of titanium or zirconium or mixture thereof.

Claim 9

A zeolitic copper catalyst having enhanced resistance to loss of activity on exposure to steam at high temperature, said catalyst comprising a crystalline zeolite incorporated in a silica-alumina or an alumina binder, with said zeolite having in the dehydrated state the composition in terms of mole ratio of oxides: 0.03-2.0 CuO:0-0.9 M.sub.2/n O:Al.sub.2 O.sub.3 :20-100 SiO.sub.2 :bXO.sub.2 wherein M is at least one cation other than a copper cation and having a valence of "n", and bXO 2 is a steam stabilizing amount of an inorganic titanium or zirconium compound or a mixture thereof, said crystalline zeolite having the crystal structure of ZSM-5, ZSM-11, ZSM-12, ZSM-22, ZSM-23, ZSM-35, ZSM-38, ZSM-48, mordenite, dealuminated Y or Zeolite Beta.

Claim 10

A zeolitic copper catalyst having enhanced resistance to loss of activity on exposure to steam at high temperature, said catalyst comprising a crystalline zeolite incorporated in a silica-alumina or an alumina binder, with said zeolite having in the dehydrated state the composition in terms of mole ratio of oxides: 0.03-2.0 CuO:0-0.9 M.sub.2/n O:Al.sub.2 O.sub.3 :20-100 SiO.sub.2 :bXO.sub.2 wherein M is at least one cation other than a copper cation and having a valence of "n", and bXO 2 is a steam stabilizing amount of an inorganic titanium or zirconium compound or a mixture thereof, said crystalline zeolite having the crystal structure of ZSM-5, ZSM-11, ZSM-12, ZSM-22, ZSM-23, ZSM-35, ZSM-38, ZSM-48, mordenite, dealuminated Y or Zeolite Beta.

Claim 11

The composition described in claim 8 wherein said zeolite has the crystal structure of ZSM-5.

Claim 12

In a method for preparing a zeolitic copper catalyst incorporated in a silica-alumina or an alumina binder, which method comprises contacting a crystalline zeolite having the crystal structure of ZSM-5 and a silica to alumina ratio of 20:1 to about 100:1 with an aqueous solution of divalent copper cations under conditions effective to exchange at least 50 percent of the framework alumina tetrahedra with said copper-containing cation, and drying said copper exchanged zeolite, the improvement which comprises: impregnating said zeolite with a stream-stabilizing amount of a soluble titanium or soluble zirconium compound; and, calcining said composition.

Claim 13

In a method for preparing a zeolitic copper catalyst incorporated in a silica-alumina or an alumina binder, which method comprises contacting a crystalline zeolite having the crystal structure of ZSM-5 and a silica to alumina ratio of 20:1 to about 100:1 with an aqueous solution of divalent copper cations under conditions effective to exchange at least 50 percent of the framework alumina tetrahedra with said copper-containing cation, and drying said copper exchanged zeolite, the improvement which comprises: impregnating said zeolite with a stream-stabilizing amount of a soluble titanium or soluble zirconium compound; and, calcining said composition.

Claim 14

The improved method described in claim 10 wherein said step of contacting said zeolite with divalent copper cations precedes said step of impregnation with a soluble titanium or soluble zirconium compound.

Claim 15

The improved method described in claim 10 wherein said zeolite is impregnated with an aqueous solution containing both said divalent copper cations and said steam stabilizing amount of soluble titanium or soluble zirconium compound.

Claim 16

The method of claim 10 wherein said aqueous solution is a solution of cupric acetate or cupric nitrate and said soluble titanium or zirconium compound is provided by titanium tetramethoxide or zirconium acetate.

Claim 17

The method of claim 12 wherein said aqueous solution is a solution of cupric acetate or cupric nitrate and said soluble titanium or zirconium compound is provided by titanium tetramethoxide or zirconium acetate.