Process and apparatus for manufacturing diaphragms
Assignee: Kolbenschmidt AG
•
Filing: 1989-04-18
•
Granted: 1990-10-09
•
Expires: 2009-04-18
Abstract
Abstract In a process of manufacturing diaphragms, a layer of a difficulty flowable metal powder is applied to a support, a wire net is rolled onto the powder layer and the latter is compacted at the same time and the metal powder is fired at 800° to 1500° C. in an oxidizing atmosphere. In order to impart to the diaphragms a constant thickness, strength and density, the metal powder is uniformly distributed and applied as regards its bulk volume to the support and the powder layer is moved under a distributing roller rotating opposite to the direction in which the powder is fed.
Inventors
- 👤 Heinz Wullenweber
- 👤 Peter Kohl
- 👤 Herbert Jung
- 👤 Jorgen Borchardt
- 👤 Wolfgang Bickle
- 👤 Jurgen Braus
- 👤 Hans-Joachim Hiedemann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 22:55
CPC Classifications
C; C25; C25B; C25B13/00; C25B13/04; B; B22; B22F; B22F3/00; B22F3/10; B22F3/11; B22F3/1103; B22F3/1118; B22F3/18; C25B13/05; C25B13/07
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
159 words
In a process for the manufacture of a diaphragm having a thickness of from 0.3 to 3.0 mm and comprising a carrier and a porous ceramic layer having a thickness of from 0.1 to 2.8 mm joined to the carrier, the improvement wherein the carrier is formed by applying a powder layer to a support by feeding a metal powder in a first feed direction onto the support, wherein the powder is flowable with difficulty and consists of irregularly shaped particles, moving the applied powder layer under a distributing roller rotating in a direction opposite to the first feed direction to impart a uniform thickness to the powder layer, rolling or pressing a wire net onto the uniform thickness powder layer and compacting the uniform thickness powder layer by 30 to 60% at the same time and firing the compacted powder layer and net in an oxidizing atmosphere of from 800° to 1500° C. for 1 to 30 minutes.
Claim 2
Dependent Claim
159 words
In a process for the manufacture of a diaphragm having a thickness of from 0.3 to 3.0 mm and comprising a carrier and a porous ceramic layer having a thickness of from 0.1 to 2.8 mm joined to the carrier, the improvement wherein the carrier is formed by applying a powder layer to a support by feeding a metal powder in a first feed direction onto the support, wherein the powder is flowable with difficulty and consists of irregularly shaped particles, moving the applied powder layer under a distributing roller rotating in a direction opposite to the first feed direction to impart a uniform thickness to the powder layer, rolling or pressing a wire net onto the uniform thickness powder layer and compacting the uniform thickness powder layer by 30 to 60% at the same time and firing the compacted powder layer and net in an oxidizing atmosphere of from 800° to 1500° C. for 1 to 30 minutes.
Claim 3
Dependent Claim
75 words
The process according to claim 1, further comprising applying and uniformly distributing a second layer of the same metal powder by feeding the metal powder onto the wire net in a second feed direction, moving the second metal powder layer under a distributing roller rotating in a direction opposite the second feed direction to impart a uniform thickness to the second metal powder layer and compacting the uniform thickness second metal powder layer by rolling.
Claim 4
Dependent Claim
16 words
The process according to claim 1, wherein the metal powder is applied in a dry form.
Claim 5
Dependent Claim
18 words
The process according to claim 2, wherein the first and second feed directions are opposite to each other.
Claim 6
Dependent Claim
180 words
In a process for the manufacture of a diaphragm having a thickness of from 0.3 to 3.0 mm and comprising a carrier and a porous ceramic layer having a thickness of from 0.1 to 2.8 mm joined to the carrier, the improvement wherein the carrier is formed by applying a wire net onto a support, applying a powder layer onto the wire net on the support by feeding a metal powder in a first feed direction onto the wire net, wherein the powder is flowable with difficulty and consists of irregularly shaped particles, moving the applied powder layer under a distributing roller rotating in a direction opposite to the first feed direction to impart a uniform thickness to the powder layer, joining the uniform thickness metal powder layer to the wire net by rolling or pressing the uniform thickness metal powder layer while compacting the uniform thickness powder layer by 30 to 60% at the same time and firing the compacted powder layer and net in an oxidizing atomosphere of from 800° to 1500° C. for 1 to 30 minutes.
Claim 7
Dependent Claim
180 words
In a process for the manufacture of a diaphragm having a thickness of from 0.3 to 3.0 mm and comprising a carrier and a porous ceramic layer having a thickness of from 0.1 to 2.8 mm joined to the carrier, the improvement wherein the carrier is formed by applying a wire net onto a support, applying a powder layer onto the wire net on the support by feeding a metal powder in a first feed direction onto the wire net, wherein the powder is flowable with difficulty and consists of irregularly shaped particles, moving the applied powder layer under a distributing roller rotating in a direction opposite to the first feed direction to impart a uniform thickness to the powder layer, joining the uniform thickness metal powder layer to the wire net by rolling or pressing the uniform thickness metal powder layer while compacting the uniform thickness powder layer by 30 to 60% at the same time and firing the compacted powder layer and net in an oxidizing atomosphere of from 800° to 1500° C. for 1 to 30 minutes.
Claim 8
Dependent Claim
86 words
The process according to claim 5, further comprising turning over the wire net and powder layer and applying and uniformly distributing a second layer of the same metal powder by feeding the metal powder onto the turned over wire net in a second feed direction, moving the second metal powder layer under a distributing roller rotating in a direction opposite the second feed direction to impart a uniform thickness to the second metal powder layer and compacting the uniform thickness second metal powder layer by rolling.
Claim 9
Dependent Claim
16 words
The process according to claim 5, wherein the metal powder is applied in a dry form.
Claim 10
Dependent Claim
18 words
The process according to claim 6, wherein the first and second feed directions are opposite to each other.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-08 | 1994-04-09 | 1994-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-08 | 1998-04-09 | 1998-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-08 | 2002-04-09 | 2002-10-09 | $7700.00 | Window Closed / Lapsed |