Assignee: Kolbenschmidt AG
•
Filing: 1989-10-25
•
Granted: 1990-10-09
•
Expires: 2009-10-25
Abstract
Abstract For some applications of slide layers, for example in connecting rod bearings of internal combustion engines, for individual sites of a formed piece, high load bearing capability are required while for other places of the same formed piece good embedding abilities are demanded. A composite material with a slide layer applied by cathode sputtering of a tightly cohesive matrix and an insoluble component distributed statistically in it, is adapted to these opposite demands in that the diameter of the particle of the insolutble material has gradients at predetermined sites, which extend parallel to the surface of the slide layer, and to which slide layer hardness gradients correspond. These gradients are generated during the cathode sputtering process in the substrate to be coated to form a growing slide layer having temperature gradients which are maintained and which extend parallel to the substrate surface.
Inventors
- 👤 Erich Bergmann
- 👤 Jurgen Braus
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:44
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/54; C23C14/541; F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/06; F16C33/14; F16C2223/00; F16C2223/30; F16C2223/60
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
109 words
A method of manufacturing a composite material, comprising the steps of: applying by cathode sputtering a slide layer surface of a mixture of particles deposited in a substantially predetermined distribution of at least one cohesive metallic material forming a matrix and at least one additional metallic material in the solid state, said additional metallic material defining particles, substantially insoluble in the matrix material; and, generating mean particle diameter gradients of said particles to provide locations of particles of small mean diameter, of high hardness and good load bearing ability, and to provide locations of particles of larger mean diameter with a lower degree of hardness, of good embedding capacity.
Claim 2
Independent Claim
109 words
A method of manufacturing a composite material, comprising the steps of: applying by cathode sputtering a slide layer surface of a mixture of particles deposited in a substantially predetermined distribution of at least one cohesive metallic material forming a matrix and at least one additional metallic material in the solid state, said additional metallic material defining particles, substantially insoluble in the matrix material; and, generating mean particle diameter gradients of said particles to provide locations of particles of small mean diameter, of high hardness and good load bearing ability, and to provide locations of particles of larger mean diameter with a lower degree of hardness, of good embedding capacity.
Claim 3
Dependent Claim
28 words
A method according to claim 1, wherein said step of generating mean particle diameter gradients comprises reducing coating temperatures at specific locations during said step of cathode sputtering.
Claim 4
Dependent Claim
23 words
A method according to claim 1, wherein said reduced temperatures are maintained so as to extend parallel to the surface of the substrate.
Claim 5
Dependent Claim
66 words
A method as stated in claim 2, wherein the reduced temperatures are generated in a manner such that the substrate to be coated is, during the cathode sputtering process, cooled in different locations to a different degree with the greatest cooling capability being produced in those sites, at which the slide layer is intended to have the smallest particle diameter and the highest degree of hardness.
Claim 6
Dependent Claim
39 words
A method of manufacturing a composite material according to claim 1, wherein said step of generating mean particle diameter gradients comprises increasing the coating rate over 0.2 μm/min. to provide said locations of locked particles of small mean diameter.
Claim 7
Dependent Claim
38 words
A method of manufacturing a composite material according to claim 1, wherein said step of generating a mean particle diameter comprises applying said metallic material forming a matrix and said additional metallic material on the substrate, timed sequentially.
Claim 8
Dependent Claim
44 words
A method according to claim 1, wherein said step of generating mean particle diameter gradients comprises applying said metallic material forming a matrix at a first temperature and applying said additional metallic material at a second temperature which is lower than said first temperature.
Claim 9
Dependent Claim
27 words
A method according to claim 1, wherein the temperature of the substrate to be coated and the growing slide layer is maintained between -10° and 190° C.
Claim 10
Dependent Claim
48 words
A method according to claim 1, wherein the temperature of the substrate to be coated and that of the slide layer at which the smallest particle diameter and the highest degree of hardness of the slide layer is to be obtained is maintained between -10° and 70° C.
Claim 11
Dependent Claim
17 words
A method as stated in claim 1, wherein different components of the slide layer are applied simultaneously.
Claim 12
Dependent Claim
24 words
A method according to claim 1, wherein different components of the slide layer are introduced into the slide layer over a period of time.
Claim 13
Dependent Claim
32 words
A method according to claim 1, wherein the metallic material forming matrix is applied before the additional metallic material and the temperature of the substrate is uniformly decreased during the coating process.
Claim 14
Dependent Claim
24 words
A method according to claim 1, wherein oxygen is supplied to the plasma during the cathode sputtering in the form of a gaseous substance.
Claim 15
Dependent Claim
20 words
A method according to claim 1, wherein oxygen is deposited as an oxide on the target used for cathode sputtering.
Claim 16
Independent Claim
160 words
A method of manufacturing a composite material, comprising the steps of: applying a slide layer surface to a substrate by cathode sputtering the slide layer surface being formed of a mixture of particles deposited in a substantially predetermined distribution of at least one cohesive metallic material forming a matrix and at least one additional metallic material in the solid state, said additional metallic material defining particles, substantially insoluble in the matrix material; and, generating mean particle diameter gradients of said particles to provide locations of locked particles of small mean diameter, of high hardness and good load bearing ability, and to provide locations of particles of larger mean diameter with a lower degree of hardness, of good embedding capacity wherein the temperature of the substrate and that of the growing slide layer at which the smallest particle diameter and the highest degree of hardness of the slide layer is to be obtained, is maintained between -10° and 70 ° C.
Claim 17
Independent Claim
160 words
A method of manufacturing a composite material, comprising the steps of: applying a slide layer surface to a substrate by cathode sputtering the slide layer surface being formed of a mixture of particles deposited in a substantially predetermined distribution of at least one cohesive metallic material forming a matrix and at least one additional metallic material in the solid state, said additional metallic material defining particles, substantially insoluble in the matrix material; and, generating mean particle diameter gradients of said particles to provide locations of locked particles of small mean diameter, of high hardness and good load bearing ability, and to provide locations of particles of larger mean diameter with a lower degree of hardness, of good embedding capacity wherein the temperature of the substrate and that of the growing slide layer at which the smallest particle diameter and the highest degree of hardness of the slide layer is to be obtained, is maintained between -10° and 70 ° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-10-08 | 1994-04-09 | 1994-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-10-08 | 1998-04-09 | 1998-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-10-08 | 2002-04-09 | 2002-10-09 | $7700.00 | Window Closed / Lapsed |