Method for forming functional deposited films by means of microwave plasma chemical vapor deposition method
Assignee: Canon Inc
•
Filing: 1988-12-21
•
Granted: 1990-09-18
•
Expires: 2008-12-21
Abstract
Abstract An improved method for forming a functional deposited film by introducing a raw material gas into a substantially enclosed reaction chamber containing a substrate onto which the functional deposited film is to be deposited and coupling microwave energy from a source of microwave energy thereinto to thereby form a glow discharge plasma causing decomposition of the raw material gas whereby forming the functional deposited film on the substrate, the improvement comprising supplying microwave of a power equivalent to 1.1 times or more over that of microwave with which the deposition rate for the decomposed products from the raw material gas being deposited onto the substrate to be saturated to the raw material gas in the reaction chamber and regulating the inner pressure of the reaction chamber to a vacuum of 10 m Torr or less. According to the method of this invention, there can be formed a desired functional deposited film having a wealth of many practically applicable characteristics and having an improved response speed against photocurrent at an improved deposition rate with a raw material gas utilization efficiency of hundred percent or nearly hundred percent. And the method of this invention makes it possible to mass-produce various functional elements comprising such deposited film usable in electrophotographic photosensitive member, photosensor, thin-film transistor, solar cell, etc. on an industrial scale thereby enabling low cost production.
Inventors
- 👤 Keishi Saitoh
- 👤 Junichiro Hashizume
- 👤 Shigehira Iida
- 👤 Tetsuya Takei
- 👤 Takayoshi Arai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 01:01
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/44; C23C16/50; C23C16/511; Y; Y10; Y10S; Y10S148/00; Y10S148/045; Y10S148/065
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
231 words
A microwave plasma chemical vapor deposition process for the formation of a functional deposited film on a plurality of substrates by means of a microwave plasma chemical vapor deposition conducted in a substantially enclosed film-forming chamber, said film-forming chamber comprising a circumferential wall having an end portion thereof hermetically provided with a microwave introducing window to which a waveguide extending from a microwave power source is connected, said film-forming chamber having a discharge space and a plurality of rotatable cylindrical substrate holders therein, each of said substrate holders being capable of having one of said substrates positioned thereon, said substrate holders being substantially concentrically arranged in said film-forming chamber so as to circumscribe said discharge space, said film-forming chamber being provided with means for supplying a film-forming raw material gas into said discharge space and means for evacuating said film-forming chamber, comprising: (a) generating a plasma by microwave glow discharge in said film-forming raw material gas to form said functional deposited film while rotating each of said cylindrical substrate holders; (b) maintaining the gaseous pressure of said discharge space at a value in the range of 0.1 to 1 mTorr; and (c) applying into said discharge space a microwave power from 1.1 to 5 times the minimum microwave power required to maximize the deposition rate for a decomposed product produced from said film-forming raw material gas to form a deposited film.
Claim 2
Dependent Claim
231 words
A microwave plasma chemical vapor deposition process for the formation of a functional deposited film on a plurality of substrates by means of a microwave plasma chemical vapor deposition conducted in a substantially enclosed film-forming chamber, said film-forming chamber comprising a circumferential wall having an end portion thereof hermetically provided with a microwave introducing window to which a waveguide extending from a microwave power source is connected, said film-forming chamber having a discharge space and a plurality of rotatable cylindrical substrate holders therein, each of said substrate holders being capable of having one of said substrates positioned thereon, said substrate holders being substantially concentrically arranged in said film-forming chamber so as to circumscribe said discharge space, said film-forming chamber being provided with means for supplying a film-forming raw material gas into said discharge space and means for evacuating said film-forming chamber, comprising: (a) generating a plasma by microwave glow discharge in said film-forming raw material gas to form said functional deposited film while rotating each of said cylindrical substrate holders; (b) maintaining the gaseous pressure of said discharge space at a value in the range of 0.1 to 1 mTorr; and (c) applying into said discharge space a microwave power from 1.1 to 5 times the minimum microwave power required to maximize the deposition rate for a decomposed product produced from said film-forming raw material gas to form a deposited film.
Claim 3
Dependent Claim
42 words
The process according to claim 1, including supplying a film-forming raw material gas into the discharge space employing a gas feed pipe capable of supplying the film-forming raw material gas into the discharge space which is longitudinally installed in the film-forming chamber.
Claim 4
Dependent Claim
20 words
The process according to claim 2, including providing said gas feed pipe between a pair of the cylindrical substrate holders.
Claim 5
Dependent Claim
50 words
The process according to claim 1, including supplying a film-forming raw material gas into the discharge space employing a plurality of gas feed pipes being longitudinally installed in the film-forming chamber, each of said gas feed pipes being capable of supplying the film-forming raw material gas into the discharge space.
Claim 6
Dependent Claim
22 words
The process according to claim 4, including providing said plurality of gas feed pipes between each pair of the cylindrical substrate holders.
Claim 7
Dependent Claim
23 words
The process according to claim 1, including providing each of the substrates as a cylindrical substrate positioned on one of the substrate holders.
Claim 8
Dependent Claim
217 words
A microwave plasma chemical vapor deposition process for the formation of a functional deposited film on a surface of a substrate by means of a microwave plasma chemical vapor deposition conducted in a substantially enclosed film-forming chamber, said film-forming chamber comprising a circumferential wall having an end portion thereof hermetically provided with a microwave introducing window to which a waveguide extending from a microwave power source is connected, said film-forming chamber having a substantially cylindrical discharge space encircled by said substrate surface, said substrate being supported by substrate working means, said film-forming chamber being provided with means for supplying a film-forming raw material gas into said discharge space and means to evacuating said film-forming chamber, comprising: (a) generating a plasma by microwave glow discharge in said film-forming raw material gas in said discharge space to form said functional deposited film while moving said surface of substrate by said substrate working means; (b) maintaining the gaseous pressure of said discharge space at a value in the range of 0.1 to 1 mTorr; and (c) applying into said discharge space a microwave power from 1.1 to 5 times the minimum microwave power required to maximize the deposition rate for a decomposed product produced from said film-forming raw material gas to form a deposited film on said surface of substrate.
Claim 9
Dependent Claim
217 words
A microwave plasma chemical vapor deposition process for the formation of a functional deposited film on a surface of a substrate by means of a microwave plasma chemical vapor deposition conducted in a substantially enclosed film-forming chamber, said film-forming chamber comprising a circumferential wall having an end portion thereof hermetically provided with a microwave introducing window to which a waveguide extending from a microwave power source is connected, said film-forming chamber having a substantially cylindrical discharge space encircled by said substrate surface, said substrate being supported by substrate working means, said film-forming chamber being provided with means for supplying a film-forming raw material gas into said discharge space and means to evacuating said film-forming chamber, comprising: (a) generating a plasma by microwave glow discharge in said film-forming raw material gas in said discharge space to form said functional deposited film while moving said surface of substrate by said substrate working means; (b) maintaining the gaseous pressure of said discharge space at a value in the range of 0.1 to 1 mTorr; and (c) applying into said discharge space a microwave power from 1.1 to 5 times the minimum microwave power required to maximize the deposition rate for a decomposed product produced from said film-forming raw material gas to form a deposited film on said surface of substrate.
Claim 10
Dependent Claim
34 words
The process according to claim 7, including supplying a film-forming raw material gas into the discharge space employing a gas feed pipe capable of supplying the film-forming raw material gas into the discharge space.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-09-17 | 1994-03-19 | 1994-09-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-09-17 | 1998-03-19 | 1998-09-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-09-17 | 2002-03-19 | 2002-09-18 | $7700.00 | Window Closed / Lapsed |