Superconductive oxide crystal and a production process thereof
Assignee: HUMIHIKO TAKEI
•
Filing: 1988-06-30
•
Granted: 1990-08-28
•
Expires: 2008-06-30
Abstract
Abstract This invention concerns a novel superconductive oxide crystal and a production process thereof, the novel superconductive oxide crystal comprising a superconductive oxide crystal composed of a rare earth element, an alkaline earth meal, copper, and oxygen, in which copper (II) oxide (CuO)) is dispersed like detached islands.
Inventors
- 👤 Humihiko Takei
- 👤 Hiroyuki Takeya
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 07:20
CPC Classifications
C; C30; C30B; C30B29/00; C30B29/10; C30B29/16; C30B29/22; C30B29/225; C01; C01G; C01G3/00; C01G3/006; C04; C04B; C04B35/00; C04B35/01; C04B35/45; C04B35/4504; C30B11/00; C30B9/00; Y; Y10; Y10S; Y10S505/00; Y10S505/725
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
111 words
A process for the production of a superconductive oxide crystal comprising the steps of: mixing a copper compound with a first complex oxide powder, said first complex oxide powder comprising a rare earth element, an alkaline earth metal, copper and oxygen in proportions corresponding substantially to the theoretical composition of a superconductive oxide crystal; heating the mixture of said copper compound with said first complex oxide powder at a temperature in the range of from 950° C. to 1400° C. in an oxygen-containing atmosphere while contacting said mixture of said copper compound and said first complex oxide powder with a second oxide, said second oxide comprising substantially a rare earth oxide.
Claim 2
Dependent Claim
111 words
A process for the production of a superconductive oxide crystal comprising the steps of: mixing a copper compound with a first complex oxide powder, said first complex oxide powder comprising a rare earth element, an alkaline earth metal, copper and oxygen in proportions corresponding substantially to the theoretical composition of a superconductive oxide crystal; heating the mixture of said copper compound with said first complex oxide powder at a temperature in the range of from 950° C. to 1400° C. in an oxygen-containing atmosphere while contacting said mixture of said copper compound and said first complex oxide powder with a second oxide, said second oxide comprising substantially a rare earth oxide.
Claim 3
Dependent Claim
22 words
The process according to claim 1, wherein said first complex oxide powder is calcined prior to being mixed with said copper compound.
Claim 4
Dependent Claim
36 words
The process according to either one of claim 1 or 2, wherein said copper compound is selected from the group consisting of copper oxide and a compound convertible into CuO upon heating in an oxygen-containing atmosphere.
Claim 5
Dependent Claim
23 words
The process according to claim 3, wherein said compound convertible into CuO upon heating in an oxygen-containing atmosphere is an organic copper compound.
Claim 6
Dependent Claim
47 words
The process according to either one of claims 1 or 2 wherein said copper compound is mixed with said first oxide powder in an amount of 25-400 parts by weight, converted into copper (II) oxide (CuO), per 100 parts by weight of said first complex oxide powder.
Claim 7
Dependent Claim
43 words
The process according to claim 3 wherein said copper compound is mixed with said first complex oxide powder in an amount of 25-400 parts by weight, converted into copper (II) oxide (CuO), per 100 parts by weight of said first complex oxide powder.
Claim 8
Dependent Claim
43 words
The process according to claim 4 wherein said copper compound is mixed with said first complex oxide powder in an amount of 25-400 parts by weight, converted into copper (II) oxide (CuO), per 100 parts by weight of said first complex oxide powder.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-08-27 | 1994-02-26 | 1994-08-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-08-27 | 1998-02-26 | 1998-08-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-08-27 | 2002-02-26 | 2002-08-28 | $7700.00 | Window Closed / Lapsed |