Process for preparation of perfluorinated copolymer
Assignee: Tokuyama Corp
•
Filing: 1989-04-14
•
Granted: 1990-08-14
•
Expires: 2009-04-14
Abstract
Abstract Disclosed is a process for the preparation of a perfluorinated copolymer having a predetermined ratio of monomer units, which comprises copolymerizing 99.5 to 50 mole % of (I) tetrafluoroethylene with 0.5 to 50 mole % of (II) a monomer represented by the following general formula: CF.sub.2 =CFOCH.sub.2 C.sub.n F.sub.l X.sub.m H.sub.(2n+1-l-m) (II) wherein X stands for --Cl or --Br, n is an integer of at least 0, l is an integer of from 0 to (2n+1), m is 0 or 1, and the relation of l+m≦2n+1 is established, in the state where both the monomers are dissolved at a predetermined monomer ratio in an organic solvent, to thereby form a copolymer comprising units of the monomers at a ratio substantially equal to said predetermined monomer ratio, and fluorinating said copolymer with molecular fluorine. The heat resistance is highly improved in the copolymer obtained according to this process without degradation of other physical properties, and generation of hydrogen fluoride by heat is hardly caused. Since the molar ratio between the starting monomers can be substantially maintained in the formed copolymer, the composition of the copolymer can be easily controlled.
Inventors
- 👤 Akihiko Nakahara
- 👤 Yuji Iseki
- 👤 Kouichi Murata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 10:28
CPC Classifications
C; C08; C08F; C08F214/00; C08F214/18; C08F214/26; C08F214/262; C08F8/00; C08F8/18; C08F8/20; C08F8/22
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
118 words
A process for the preparation of a perfluorinated copolymer, which comprises copolymerizing (I) tetrafluoroethylene with (II) a monomer represented by the following general formula: CF.sub.2 ═CFOCH.sub.2 C.sub.n F.sub.l X.sub.m H.sub.(2n+1-l-m)(II) wherein X stands for --Cl or --Br, n is an integer of at least 0, l is an integer of from 0 to (2n+1), m is 0 or 1, and the relation of l+m≦2n+1 is established, at a predetermined monomer molar ratio (I)/(II) of from 99.5/0.5 to 50/50 in the state where both the monomers are dissolved in an organic solvent, to thereby form a copolymer comprising units of the monomers at a ratio substantially equal to said predetermined monomer ratio, and fluorinating said copolymer with molecular fluorine.
Claim 2
Dependent Claim
118 words
A process for the preparation of a perfluorinated copolymer, which comprises copolymerizing (I) tetrafluoroethylene with (II) a monomer represented by the following general formula: CF.sub.2 ═CFOCH.sub.2 C.sub.n F.sub.l X.sub.m H.sub.(2n+1-l-m)(II) wherein X stands for --Cl or --Br, n is an integer of at least 0, l is an integer of from 0 to (2n+1), m is 0 or 1, and the relation of l+m≦2n+1 is established, at a predetermined monomer molar ratio (I)/(II) of from 99.5/0.5 to 50/50 in the state where both the monomers are dissolved in an organic solvent, to thereby form a copolymer comprising units of the monomers at a ratio substantially equal to said predetermined monomer ratio, and fluorinating said copolymer with molecular fluorine.
Claim 3
Dependent Claim
47 words
A copolymerization process according to claim 1, wherein at the start of the copolymerization, the pressure of the tetrafluoroethylene (I) in the gas phase zone in a polymerization reaction vessel is adjusted to a predetermined level within the range of from 1 to 100 kg/cm 2 G.
Claim 4
Dependent Claim
65 words
A copolymerization process according to claim 1, wherein the monomer (II) is a fluorine-containing alkylvinyl ether represented by the following general formula: CF.sub.2 CF--O--CH.sub.2 C.sub.n F.sub.l X.sub.m H.sub.(2n+1-l-m) wherein X stands for --Cl or --Br, n is an integer of from 0 to 10, l is an integer of from 2n to 2n+1, m is 0 or 1, and the relation of l+m≦2n+1, is established.
Claim 5
Dependent Claim
45 words
A copolymerization process according to claim 3, wherein the monomer (II) is a fluorine-containing alkylvinyl ether represented by the following general formula: CF.sub.2 ═CFOCH.sub.2 (CF.sub.2).sub.p Y wherein Y stands for --H, --F, --Cl or --Br, and p is an integer of from 1 to 5.
Claim 6
Dependent Claim
32 words
A copolymerization process according to claim 1, wherein the monomer (II) is used in an amount of 0.1 to 30 parts by weight per 100 parts by weight of the organic solvent.
Claim 7
Dependent Claim
16 words
A copolymerization process according to claim 1, wherein the organic solvent is chlorofluorocarbon or perfluoro compound.
Claim 8
Dependent Claim
42 words
A copolymerization process according to claim 1, wherein the copolymerization of the monomers (I) and (II) is carried out in a mixed solvent comprising the organic solvent and water in an amount 0.3 to 10 times the amount of the organic solvent.
Claim 9
Dependent Claim
139 words
A process for the preparation of a perfluorinated copolymer, which comprises copolymerizing (I) tetrafluoroethylene with (II) a fluorine-containing alkylvinyl ether represented by the following general formula: CF.sub.2 ═CFOCH.sub.2 (CF.sub.2).sub.p Y wherein Y represents --H, --F, --Cl or --Br and p is an integer of from 1 to 5, at a predetermined molar ratio (I)/(II) of from 99.5/0.5 to 50/50 in the state where both the monomers are dissolved in an organic solvent, at a temperature of about 0° to about 100° C. under a pressure of 1 to 100 kg/cm 2 gauge, to thereby form a copolymer comprising the monomers (I) and (II) at a ratio substantially equal to said predetermined monomer ratio, and fluorinating the copolymer with molecular fluorine at a temperature from room temperature to 100° C. under a pressure of 1 to 20 kg/cm 2 gauge.
Claim 10
Dependent Claim
139 words
A process for the preparation of a perfluorinated copolymer, which comprises copolymerizing (I) tetrafluoroethylene with (II) a fluorine-containing alkylvinyl ether represented by the following general formula: CF.sub.2 ═CFOCH.sub.2 (CF.sub.2).sub.p Y wherein Y represents --H, --F, --Cl or --Br and p is an integer of from 1 to 5, at a predetermined molar ratio (I)/(II) of from 99.5/0.5 to 50/50 in the state where both the monomers are dissolved in an organic solvent, at a temperature of about 0° to about 100° C. under a pressure of 1 to 100 kg/cm 2 gauge, to thereby form a copolymer comprising the monomers (I) and (II) at a ratio substantially equal to said predetermined monomer ratio, and fluorinating the copolymer with molecular fluorine at a temperature from room temperature to 100° C. under a pressure of 1 to 20 kg/cm 2 gauge.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-08-13 | 1994-02-12 | 1994-08-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-08-13 | 1998-02-12 | 1998-08-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-08-13 | 2002-02-12 | 2002-08-14 | $7700.00 | Window Closed / Lapsed |