Production of ceramic and ceramic-metal composite articles with surface coatings
Assignee: Lanxide Technology Co LP
•
Filing: 1986-09-16
•
Granted: 1990-08-14
•
Expires: 2006-09-16
Abstract
Abstract The invention comprises a method of making self-supporting ceramic and ceramic composite structures by the oxidation reaction of a body of molten parent metal precursor with a vapor-phase oxidant to form an oxidation reaction product. This reaction or growth is continued to form a thick, self-supporting ceramic or ceramic composite body. The body is recovered and in a separate subsequent operation, at least a poriton of a surface is coated with one or more materials in order to effect desired changes in the properties of the surface, e.g., hardness, corrosion resistance.
Inventors
- 👤 Marc S. Newkirk
- 👤 Adam J. Gesing
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 21:21
CPC Classifications
C; C04; C04B; C04B35/00; C04B41/00; C04B41/009; C04B35/622; C04B35/64; C04B35/65; C04B35/652; C04B41/45; C04B41/50; C04B41/5053; C04B41/51; C04B41/80; C04B41/81; C04B41/85; C04B41/87; C04B41/88; C22; C22C; C22C1/00; C22C1/10; C22C1/1036; C22C1/1057; C22C1/1063; C22C29/00; C22C29/12; F; F41; F41H; F41H5/00; F41H5/02; F41H5/04; F41H5/0414
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
287 words
A method for producing a self-supporting ceramic composite structure comprising (1) a ceramic matrix obtained by oxidation of a parent metal to form a polycrystalline material comprising an oxidation reaction product of said parent metal with a vapor-phase oxidant; and (2) at least one filler material embedded by said matrix, the method comprising the steps of: (a) positioning said parent metal adjacent to a permeable mass of filler and orienting said parent metal and said filler relative to each other so that formation of said oxidation reaction product will occur in a direction towards and into said mass of filler; (b) heating said parent metal to a temperature above its melting point but below the melting point of said oxidation reaction product to form a body of molten parent metal and reacting the molten parent metal with said oxidant at said temperature to form said oxidation reaction product, and at said temeprature maintaining at least a portion of said oxidation reaction product in contact with and extending between said body of molten metal and said oxidant, to draw molten metal through the oxidation reaction product towards the oxidant and towards and into the adjacent mass of filler so that fresh oxidation reaction product continues to form within the mass of filler at an interface between the oxidant and previously formed oxidation reaction product, and continuing said reacting for a time sufficient to embed at least a portion of the filler within said polycrystalline material; (c) recovering the self-supporting composite body; and (d) coating at least a portion of a surface of said recovered composite body with at least one material which effects a change in properties of said surface, and recovering the resulting coated ceramic composite body.
Claim 2
Independent Claim
287 words
A method for producing a self-supporting ceramic composite structure comprising (1) a ceramic matrix obtained by oxidation of a parent metal to form a polycrystalline material comprising an oxidation reaction product of said parent metal with a vapor-phase oxidant; and (2) at least one filler material embedded by said matrix, the method comprising the steps of: (a) positioning said parent metal adjacent to a permeable mass of filler and orienting said parent metal and said filler relative to each other so that formation of said oxidation reaction product will occur in a direction towards and into said mass of filler; (b) heating said parent metal to a temperature above its melting point but below the melting point of said oxidation reaction product to form a body of molten parent metal and reacting the molten parent metal with said oxidant at said temperature to form said oxidation reaction product, and at said temeprature maintaining at least a portion of said oxidation reaction product in contact with and extending between said body of molten metal and said oxidant, to draw molten metal through the oxidation reaction product towards the oxidant and towards and into the adjacent mass of filler so that fresh oxidation reaction product continues to form within the mass of filler at an interface between the oxidant and previously formed oxidation reaction product, and continuing said reacting for a time sufficient to embed at least a portion of the filler within said polycrystalline material; (c) recovering the self-supporting composite body; and (d) coating at least a portion of a surface of said recovered composite body with at least one material which effects a change in properties of said surface, and recovering the resulting coated ceramic composite body.
Claim 3
Dependent Claim
43 words
The method of claim 1, wherein said coating comprises at least one material selected from the group consisting of the elements aluminum, boron, carbon, cobalt, copper, chromium, germanium, hafnium, molybdenum, nickel, niobium, palladium, platinum, silicon, silver, tin, tantalum, titanium, vanadium, tungsten, and zirconium.
Claim 4
Dependent Claim
20 words
The method of claim 2, wherein said coating is applied to said surface by a process comprising chemical vapor deposition.
Claim 5
Dependent Claim
20 words
The method of claim 2, wherein said coating is applied to said surface by a process comprising physical vapor deposition.
Claim 6
Dependent Claim
34 words
The method of claim 1, wherein said coating comprises at least one carbide selected from the group consisting of the carbides of boron, chromium, hafnium, molybdenum, niobium, silicon, tantalum, titanium, vanadium, tungsten, and zirconium.
Claim 7
Dependent Claim
20 words
The method of claim 5, wherein said coating is applied to said surface by a process comprising chemical vapor deposition.
Claim 8
Dependent Claim
20 words
The method of claim 5, wherein said coating is applied to said surface by a process comprising physical vapor deposition.
Claim 9
Dependent Claim
33 words
The method of claim 1, wherein said coating comprises at least one nitride selected from the group consisting of the nitrides of aluminum, boron, hafnium, niobium, tantalum, silicon, titanium, vanadium, tungsten, and zirconium.
Claim 10
Dependent Claim
20 words
The method of claim 8, wherein said coating is applied to said surface by a process comprising chemical vapor deposition.
Claim 11
Dependent Claim
20 words
The method of claim 8, wherein said coating is applied to said surface by a process comprising physical vapor deposition.
Claim 12
Dependent Claim
31 words
The method of claim 1, wherein said coating comprises at least one oxide selected from the group consisting of the oxides of aluminum, chromium, silicon, tantalum, tin, titanium, zinc, and zirconium.
Claim 13
Dependent Claim
20 words
The method of claim 11, wherein said coating is applied to said surface by a process comprising chemical vapor deposition.
Claim 14
Dependent Claim
20 words
The method of claim 11, wherein said coating is applied to said surface by a process comprising physical vapor deposition.
Claim 15
Independent Claim
210 words
A method for producing a self-supporting ceramic composite body by oxidation reaction of a molten parent metal with an oxidant to form an oxidation reaction product, and continuing said oxidation reaction for a time sufficient to permit said oxidation reaction product to infiltrate and embed at least one filler material to produce said ceramic composite body, said ceramic composite body comprising said oxidation reaction product and an interconnected, metal-containing component, which component is at least partially interconnected and is at least partially accessible from an external surface of the ceramic composite body, the improvement comprising: (A) contacting at least a portion of said external surface of said ceramic composite body with a foreign metal different from said parent metal, so as to create a concentration gradient between said two metals; (B) allowing sufficient time for interdiffusion of said two metals whereby a portion of said interconnected, metal-containing component is at least partially displaced in said ceramic composite body by said foreign metal; (C) recovering said ceramic composite body; (D) selectively coating at least a portion of a surface of said foreign metal component in said recovered body with at least one element which effects a change in properties of said surface; and (E) recovering the resulting coated ceramic composite body.
Claim 16
Independent Claim
210 words
A method for producing a self-supporting ceramic composite body by oxidation reaction of a molten parent metal with an oxidant to form an oxidation reaction product, and continuing said oxidation reaction for a time sufficient to permit said oxidation reaction product to infiltrate and embed at least one filler material to produce said ceramic composite body, said ceramic composite body comprising said oxidation reaction product and an interconnected, metal-containing component, which component is at least partially interconnected and is at least partially accessible from an external surface of the ceramic composite body, the improvement comprising: (A) contacting at least a portion of said external surface of said ceramic composite body with a foreign metal different from said parent metal, so as to create a concentration gradient between said two metals; (B) allowing sufficient time for interdiffusion of said two metals whereby a portion of said interconnected, metal-containing component is at least partially displaced in said ceramic composite body by said foreign metal; (C) recovering said ceramic composite body; (D) selectively coating at least a portion of a surface of said foreign metal component in said recovered body with at least one element which effects a change in properties of said surface; and (E) recovering the resulting coated ceramic composite body.
Claim 17
Dependent Claim
49 words
The method of claim 14, wherein said foreign metal comprises iron, said element comprises carbon, and said coating is applied in step (D) by heating said ceramic composite body in an atmosphere comprising a hydrocarbon gas for a period of about 5-30 hours at a temperature of 800°-1000° C.
Claim 18
Dependent Claim
47 words
The method of claim 14, wherein said foreign metal comprises iron, said element comprises nitrogen, and said coating is applied in step (D) by heating said ceramic composite body in an atmosphere comprising anhydrous ammonia for a period of 5-80 hours at a temperature of 500°-600° C.
Claim 19
Dependent Claim
61 words
The method of claim 14, wherein said foreign metal comprises iron, said elements comprise both carbon and nitrogen, and said coating is applied in step (D) by heating said ceramic composite body in an atmosphere comprising a hydrocarbon gas admixed with a minor proportion of anhydrous ammonia, for a period of 1 to 5 hours at a temperature of 800°-1000° C.
Claim 20
Independent Claim
283 words
A method for producing a self-supporting ceramic composite body by oxidation of a parent metal, which comprises: (a) heating said parent metal to a temperature above its melting point, but below the melting point of an oxidation reaction product, to form a body of molten parent metal, reacting said molten parent metal with a vapor-phase oxidant at such temperature to form oxidation reaction product; (b) maintaining the temperature so as to keep the metal molten, and progressively drawing molten metal through the oxidation reaction product to permit oxidation reaction product to infiltrate and embed at least one filler material and to permit fresh oxidation reaction product to continue to form at an interface between the oxidant and previously formed oxidation reaction product; (c) continuing said reaction for a time sufficient to produce said ceramic composite body comprising said oxidation reaction product and an interconnected, metal-containing component, which component is at least partially interconnected and at least partially accessible from an external surface of the ceramic composite body; (d) contacting at least a portion of said external surface of said ceramic composite body with a foreign metal different from said parent metal, so as to create a concentration gradient between said two metals; (e) allowing sufficient time for interdiffusion of said two metals whereby a portion of said interconnected, metal-containing component is at least partially displaced in said ceramic composite body by said foreign metal; (f) recovering said ceramic composite body; (g) selectively coating at least a portion of a surface of said foreign metal component in said ceramic composite body with at least one element which effects a change in properties of said surface; and (h) recovering the resulting coated ceramic composite body.
Claim 21
Independent Claim
283 words
A method for producing a self-supporting ceramic composite body by oxidation of a parent metal, which comprises: (a) heating said parent metal to a temperature above its melting point, but below the melting point of an oxidation reaction product, to form a body of molten parent metal, reacting said molten parent metal with a vapor-phase oxidant at such temperature to form oxidation reaction product; (b) maintaining the temperature so as to keep the metal molten, and progressively drawing molten metal through the oxidation reaction product to permit oxidation reaction product to infiltrate and embed at least one filler material and to permit fresh oxidation reaction product to continue to form at an interface between the oxidant and previously formed oxidation reaction product; (c) continuing said reaction for a time sufficient to produce said ceramic composite body comprising said oxidation reaction product and an interconnected, metal-containing component, which component is at least partially interconnected and at least partially accessible from an external surface of the ceramic composite body; (d) contacting at least a portion of said external surface of said ceramic composite body with a foreign metal different from said parent metal, so as to create a concentration gradient between said two metals; (e) allowing sufficient time for interdiffusion of said two metals whereby a portion of said interconnected, metal-containing component is at least partially displaced in said ceramic composite body by said foreign metal; (f) recovering said ceramic composite body; (g) selectively coating at least a portion of a surface of said foreign metal component in said ceramic composite body with at least one element which effects a change in properties of said surface; and (h) recovering the resulting coated ceramic composite body.
Claim 22
Independent Claim
16 words
The method of claims 1, 14 or 18, wherein said composite body reacts with said coating.
Claim 23
Dependent Claim
36 words
The method of claim 14, or claim 18, wherein said foreign metal comprises at least one material selected from the group consisting of chromium, iron, manganese, molybdenum, nickel, niobium, silicon, titanium, tungsten, vanadium, and alloys thereof.
Claim 24
Dependent Claim
45 words
The method of claim 14, or claim 18, wherein said element comprises at least one material selected from the group consisting of aluminum, boron, carbon, cobalt, copper, chromium, germanium, hafnium, molybdenum, nitrogen, nickel, niobium, palladium, platinum, silicon, silver, tin, tantalum, titanium, vanadium, tungsten, and zirconium.
Claim 25
Independent Claim
30 words
The method of claims 1, 14 or 18, wherein said coating comprises at least one boride selected from the group consisting of borides of aluminum, titanium, silicon, zirconium, and hafnium.
References Cited (Backward Citations)
US2741822A
Cited
US3031340A
Cited
US3255027A
Cited
US3298842A
Cited
US3296002A
Cited
US3419404A
Cited
US3473987A
Cited
US3421863A
Cited
US3437468A
Cited
US3789096A
Cited
US3473938A
Cited
US3538231A
Cited
US3608170A
Cited
US3770488A
Cited
US3864154A
Cited
US3868267A
Cited
US3969553A
Cited
US3973977A
Cited
EP0116809A1
Cited
EP0155831A2
Cited
US4713360A
Cited
EP0169067A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-08-13 | 1994-02-12 | 1994-08-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-08-13 | 1998-02-12 | 1998-08-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-08-13 | 2002-02-12 | 2002-08-14 | $7700.00 | Window Closed / Lapsed |