Modified thermoplastic and a method for the manufacture of the thermoplastic
Assignee: Tetra Laval Holdings and Finance SA
•
Filing: 1989-05-22
•
Granted: 1990-08-14
•
Expires: 2009-05-22
Abstract
Abstract The prerequisites for the injection moulding from thermoplastic material of container lids with a tear-up opening arrangement which is to function well on opening as well as on reclosing are improved through the use of a modified thermoplastic containing inert filler in a quantity of 10-15% of the weight of the mixture. Such a modified thermoplastic is manufactured by the heating of a thermoplastic,known in itself, e.g. polyethylene, to melting temperature with simultaneous admixture of the filler,and the mixture is mechanically processed for a good distribution of the filler in the melted plastic mass which thereafter is cooled to form the modified thermoplastics.
Inventors
- 👤 Klas A. Rosen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 06:35
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/20; C08K; C08K3/00; C08K3/01; C08K3/013; C08K3/18; C08K3/24; C08K3/26; C08K3/34; Y; Y10; Y10S; Y10S220/00; Y10S220/14; Y10S220/16; Y10T; Y10T428/00; Y10T428/26
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
43 words
A modified thermoplastic injection molded container lid comprising an injection molded thermoplastic lid having an opening arrangement of the tear-up type, the modified thermoplastic containing inert inorganic filler dispersed in the thermoplastic in an amount of 10-15% of the weight of the mixture.
Claim 2
Dependent Claim
43 words
A modified thermoplastic injection molded container lid comprising an injection molded thermoplastic lid having an opening arrangement of the tear-up type, the modified thermoplastic containing inert inorganic filler dispersed in the thermoplastic in an amount of 10-15% of the weight of the mixture.
Claim 3
Dependent Claim
24 words
A modified thermoplastic lid in accordance with claim 1, wherein the filler consists of particles of an average grain size of substantially 10 μm.
Claim 4
Dependent Claim
31 words
A modified thermoplastic lid in accordance with claim 1, wherein the filler is a member selected from the group consisting of mica, talc, chalk, gypsum, wollastonite and clay and combinations thereof.
Claim 5
Dependent Claim
17 words
A modified thermoplastic lid in accordance with claim 1, further comprising a wetting agent for the filler.
Claim 6
Dependent Claim
24 words
A modified thermoplastic lid in accordance with claim 4, wherein the wetting agent constitutes between 0.5 and 2% of the weight of the material.
Claim 7
Dependent Claim
17 words
A modified thermoplastic lid in accordance with claim 1, wherein the thermoplastic is constituted of polyolefin material.
Claim 8
Dependent Claim
25 words
A modified thermoplastic lid in accordance with claim 6, wherein the polyolefin material is a member selected from the group consisting of polyethylene and polypropylene.
Claim 9
Dependent Claim
14 words
A modified thermoplastic lid in accordance with claim 1, wherein said thermoplastic is polyethylene.
Claim 10
Independent Claim
92 words
A method for preparation of a modified thermoplastic injection moulded thermoplastic container lid provided with tear-up, reclosable opening arrangements, the method comprising the steps of: heating the thermoplastic to its melting temperature; adding an inorganic filler to the thermoplastic; mechanically processing the thermoplastic and filler to distribute the filler in the thermoplastic; and cooling the mixture of thermoplastic and filler to form the modified thermoplastic, the amount of filler added to the thermoplastic being controlled so that the mixture includes filler in an amount of 10-15% of the weight of the mixture.
Claim 11
Independent Claim
92 words
A method for preparation of a modified thermoplastic injection moulded thermoplastic container lid provided with tear-up, reclosable opening arrangements, the method comprising the steps of: heating the thermoplastic to its melting temperature; adding an inorganic filler to the thermoplastic; mechanically processing the thermoplastic and filler to distribute the filler in the thermoplastic; and cooling the mixture of thermoplastic and filler to form the modified thermoplastic, the amount of filler added to the thermoplastic being controlled so that the mixture includes filler in an amount of 10-15% of the weight of the mixture.
Claim 12
Dependent Claim
34 words
A method in accordance with claim 9, further comprising the step of wetting the filler through the addition of a dispersing agent, the dispersing agent being added either separately or together with the filler.
Claim 13
Dependent Claim
26 words
A method in accordance with claim 10, wherein the quantity of dispersing agent added to the filler amounts of 0.5-2% of the weight of the material.
Claim 14
Dependent Claim
24 words
The method in accordance with claim 10, further comprising the step of heating the filler prior to addition of the filler to the thermoplastic.
References Cited (Backward Citations)
GB499333A
Cited
US3342901A
Cited
GB1447304A
Cited
US4473167A
Cited
US4120844A
Cited
US4255367A
Cited
GB2033821A
Cited
EP0016389A1
Cited
US4552689A
Cited
US4480065A
Cited
US4708623A
Cited
US4812247A
Cited
US4570818A
Cited
US4734450A
Cited
US4705818A
Cited
DE3519053A1
Cited
US4687129A
Cited
US4761451A
Cited
US4739900A
Cited
US4724978A
Cited
US4724977A
Cited
US4883193A
Cited
US4865216A
Cited
JPH054139A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-08-13 | 1994-02-12 | 1994-08-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-08-13 | 1998-02-12 | 1998-08-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-08-13 | 2002-02-12 | 2002-08-14 | $7700.00 | Window Closed / Lapsed |