Abstract A method is disclosed for producing an aluminum oxide coated manganese activated zinc silicate phosphor which comprises forming a solution of Al +3 ions in water with the concentration of the aluminum being from about 0.01 to about 0.30 moles/l, adding manganese activated zinc silicate phosphor to the aluminum solution to form a slurry wherein the amount of phosphor is about 0.7 to about 1.0 moles per liter of slurry with agitation for a sufficient time to result in aluminum ions being adsorbed onto the surfaces of the particles of the phosphor, separating the resulting phosphor with adsorbed aluminum ions from the resulting liquor, drying the phosphor with the adsorbed aluminum ions, firing the resulting dried phosphor at a temperature of from about 750° C. to about 850° C. in an oxidizing atmosphere for a sufficient time to oxidize the adsorbed aluminum ions to aluminum oxide and forming a coating of aluminum oxide on the particles of the phosphor, the coated phosphor having an increase in maintenance in a fluorescent lamp at about 100 hours over the phosphor absent the coating.
A method for producing an aluminum oxide coated manganese activated zinc silicate phosphor, said method comprising: (a) forming a solution of Al +3 ions from aluminum nitrate in water with the concentration of said aluminum being from about 0.01 to about 0.30 moles/l. (b) adding manganese activated zinc silicate phosphor to said aluminum solution to form a slurry wherein the amount of said phosphor is about 0.7 to about 1.0 moles per liter of said slurry with agitation for a sufficient time to result in aluminum ions being adsorbed onto the surfaces of the particles of said phosphor; (c) separating the resulting phosphor with adsorbed aluminion ions from the resulting liquor; (d) drying said phosphor with said adsorbed aluminum ions; (e) firing the resulting dried phosphor at a temperature of from about 750° C. to about 850° C. in an oxidizing atmosphere for a sufficient time to oxidize the adsorbed aluminum ions to aluminum oxide and forming a coating of aluminum oxide on the particles of said phosphor, said coated phosphor having an increase in maintenance in a fluorescent lamp at about 100 hours over said phosphor absent said coating.
Claim 2
Independent Claim
190 words
A method for producing an aluminum oxide coated manganese activated zinc silicate phosphor, said method comprising: (a) forming a solution of Al +3 ions from aluminum nitrate in water with the concentration of said aluminum being from about 0.01 to about 0.30 moles/l. (b) adding manganese activated zinc silicate phosphor to said aluminum solution to form a slurry wherein the amount of said phosphor is about 0.7 to about 1.0 moles per liter of said slurry with agitation for a sufficient time to result in aluminum ions being adsorbed onto the surfaces of the particles of said phosphor; (c) separating the resulting phosphor with adsorbed aluminion ions from the resulting liquor; (d) drying said phosphor with said adsorbed aluminum ions; (e) firing the resulting dried phosphor at a temperature of from about 750° C. to about 850° C. in an oxidizing atmosphere for a sufficient time to oxidize the adsorbed aluminum ions to aluminum oxide and forming a coating of aluminum oxide on the particles of said phosphor, said coated phosphor having an increase in maintenance in a fluorescent lamp at about 100 hours over said phosphor absent said coating.