US4940734A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the preparation of porous polymer beads
Assignee: Wyeth Holdings LLC
•
Filing: 1988-11-23
•
Granted: 1990-07-10
•
Expires: 2008-11-23
Abstract
Abstract Isotropic porous polymer beads having controllable surface porosity and large pore diameters from about 0.002 to about 5 microns are produced from solutions of an acrylonitrile polymer or a copolymer by a thermally-induced phase separation process including intensively shearing the polymer solution into small droplets. The use of mixed solvent non-solvent combinations as solvents for the polymers, and preferably reducing the polymer content in solution to below 10 percent produces high pore content, substantially spherical beads having a morphology ideally suited to the chromatography of large molecules, such as proteins, and for enzyme-binding.
Inventors
- 👤 David A. Ley
- 👤 Laura J. Hiscock
- 👤 Michael T. Cooke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 10:38
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/12; B; B01; B01J; B01J20/00; B01J20/22; B01J20/26; C08J9/00; C08J9/28; C08J2333/00; C08J2333/18; C08J2333/20
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
140 words
A process for the preparation of porous polymer beads with controllable surface porosity wherein said beads are substantially nonswellable in water and have substantially uniform pores of not substantially greater than about 5 microns in diameter, said process comprising (i) heating and mixing an acrylonitrile homopolymer or copolymer thereof with a mixture comprising a solvent and a non-solvent for the polymer to form a homogeneous solution having a polymer solids concentration range of from 0.5 to less than 20 percent: (ii) breaking the homogeneous solution into droplets using a high shearing technique; (iii) cooling the droplets, optionally in the presence of an inert liquid, to bring about phase separation and solidification of the polymer in the droplets; (iv) separating the solidified droplets from any inert liquid and removing the solvent non-solvent mixture from the solidified droplets to produce porous beads.
Claim 2
Dependent Claim
140 words
A process for the preparation of porous polymer beads with controllable surface porosity wherein said beads are substantially nonswellable in water and have substantially uniform pores of not substantially greater than about 5 microns in diameter, said process comprising (i) heating and mixing an acrylonitrile homopolymer or copolymer thereof with a mixture comprising a solvent and a non-solvent for the polymer to form a homogeneous solution having a polymer solids concentration range of from 0.5 to less than 20 percent: (ii) breaking the homogeneous solution into droplets using a high shearing technique; (iii) cooling the droplets, optionally in the presence of an inert liquid, to bring about phase separation and solidification of the polymer in the droplets; (iv) separating the solidified droplets from any inert liquid and removing the solvent non-solvent mixture from the solidified droplets to produce porous beads.
Claim 3
Dependent Claim
36 words
A process as defined in claim 1 wherein step (i) further comprises dispersing the solution in a hot inert liquid and step (ii) comprises breaking the homogeneous dispersion into droplets by use of a static mixer.
Claim 4
Dependent Claim
23 words
A process as defined in claim 1 wherein step (ii) comprises breaking the homogeneous solution into droplets by use of an ultrasonic nozzle.
Claim 5
Dependent Claim
23 words
A process as defined in claim 1 wherein step (ii) comprises breaking the homogeneous solution into droplets by use of an atomization nozzle.
Claim 6
Dependent Claim
23 words
A process as defined in claim 1 wherein step (ii) comprises breaking the homogeneous solution into droplets through the use of laminar jets.
Claim 7
Dependent Claim
32 words
A process as defined in claim 1 wherein step (i) further comprises dispersing the solution in a hot inert liquid and step (ii) comprises breaking the homogeneous dispersion into droplets by homogenization.
Claim 8
Dependent Claim
41 words
A process as defined in claim 1 wherein said solvent comprises dimethyl sulfone, the non-solvent comprises urea, water, propylene glycol, ethylene glycol or a mixture thereof and step (i) is carried out at a temperature of at least about 130° C.
Claim 9
Dependent Claim
20 words
A process as defined in claim 1 wherein the inert liquid comprises mineral oil, kerosene, heptane, or a mixture thereof.
Claim 10
Dependent Claim
33 words
A process as defined in claim 1 wherein the inert liquid is extracted from the solidified droplets with a non-solvent for the polymer, said non-solvent comprising acetone, methanol, water, or a mixture thereof.
Claim 11
Dependent Claim
82 words
A process for the production of porous beads as defined in claim 1 wherein said polyacrylonitrile copolymer comprises an acrylonitrile copolymerized with a (C 2 -C 6 ) monoolefin, a vinylaromatic, a vinylaminoaromatic, a vinyl halide, a (C 1 -C 6 ) alkyl (meth)acrylate, a (meth)acrylamide, a vinyl pyrrolidone, a vinyl pyridine, a (C 1 -C 6 )hydroxyalkyl (meth)acrylate, a (meth)acrylic acid, an acrylamidomethylpropylsulfonic acid, an N-hydroxy- containing (C 1 -C 6 ) alkyl(meth)acrylamide, or a mixture of any of the foregoing.
Claim 12
Dependent Claim
25 words
A process as defined in claim 1 further comprising the step of at least partially filling the pores of said porous beads with a compound.
Claim 13
Dependent Claim
42 words
A process as defined in claim 11 wherein said compound is selected from the group consisting of a protein, an enzyme, a hormone, a peptide, a polysaccharide, a nucleic acid, a dye, a pigment or a mixture of any of the foregoing.
Claim 14
Dependent Claim
13 words
A process as defined in claim 12 wherein said compound comprises a protein.
Claim 15
Dependent Claim
26 words
A process as defined in claim 12 wherein the pore diameter of said porous beads is at least about 3 times the diameter of said compound.
Claim 16
Dependent Claim
34 words
A process as defined in claim 1 wherein the homogeneous solution of step (i) contains less than about 10 weight percent total polymer or copolymer solids and the porous polymer beads are substantially skinless.
Claim 17
Dependent Claim
22 words
The product of the process as defined in claim 1 wherein the pore volume is not substantially less than about 1.5 ml/g.
Claim 18
Dependent Claim
13 words
A product as defined in claim 16 wherein said beads are substantially spherical.
Claim 19
Dependent Claim
24 words
A product as defined in claim 16 wherein said beads comprise a copolymer of from about 45 to about 99.5 mole percent of acrylonitrile.
Claim 20
Dependent Claim
13 words
A product as defined in claim 16 wherein the beads are substantially isotropic.
Claim 21
Dependent Claim
10 words
A product of the process as defined in claim 15.
References Cited (Backward Citations)
US3938001A
Cited
US4110529A
Cited
US4094848A
Cited
US4247498A
Cited
US4519909A
Cited
US4486549A
Cited
US4594207A
Cited
US4666607A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-09 | 1994-01-08 | 1994-07-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-09 | 1998-01-08 | 1998-07-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-09 | 2002-01-08 | 2002-07-10 | $7700.00 | Window Closed / Lapsed |