US4594207A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for the production of porous bodies with adjustable total pore volume, adjustable pore size and adjustable pore walls
Assignee: Membrana GmbH
•
Filing: 1983-02-10
•
Granted: 1986-06-10
•
Expires: 2003-02-10
Abstract
Abstract Porous bodies, particularly membranes in the form of hollow filaments, are produced by heating a polymer above the upper critical temperature Tc in a mixture of two compounds A and B, liquid and miscible at the dissolving temperature, whereby the employed mixture (polymer, compounds A and B) in liquid aggregate state displays a miscibility gap, the compound A is a solvent for the polymer and the compound B, which preferably is a non-solvent or a swelling agent for the polymer, raises the phase separation temperature of a solution composed of the polymer and compound A. After the dissociation, the components A and/or B if necessary are extracted. Through use of non-toxic substances such as e.g. edible oil as compound A and castor oil as compound B, bodies are obtained which are non-toxic and unobjectionable for use in medical areas and in the foods industry, among others.
Inventors
- 👤 Christoph Josefiak
- 👤 Friedbert Wechs
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 11:51
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/28; B; B01; B01D; B01D69/00; B01D69/08; B01D71/00; B01D71/06; B01D71/26; B01D71/261; B01D71/262; B29; B29C; B29C67/00; B29C67/20; B29C67/202; C08J2201/00; C08J2201/04; C08J2201/052
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
134 words
Method for the production of porous bodies, shaped and non-shaped, with adjustable total pore volume, adjustable pore size and adjustable pore walls, comprising dissolving a polymer through heating above the upper critical temperature T c in a mixture of two compounds A and B, liquid and miscible at the dissolving temperature, the pore volume, pore size and pore walls being adjustable by varying the relative proportions of compounds A and B in the mixture, the employed mixture of polymer, compound A and compound B displaying in liquid aggregate state a miscibility gap, the compound A being a solvent for the polymer and the compound B acting to raise the phase separation temperature of a solution composed of a polymer and the compound A and bringing it to dissociation and setting by means of cooling.
Claim 2
Dependent Claim
134 words
Method for the production of porous bodies, shaped and non-shaped, with adjustable total pore volume, adjustable pore size and adjustable pore walls, comprising dissolving a polymer through heating above the upper critical temperature T c in a mixture of two compounds A and B, liquid and miscible at the dissolving temperature, the pore volume, pore size and pore walls being adjustable by varying the relative proportions of compounds A and B in the mixture, the employed mixture of polymer, compound A and compound B displaying in liquid aggregate state a miscibility gap, the compound A being a solvent for the polymer and the compound B acting to raise the phase separation temperature of a solution composed of a polymer and the compound A and bringing it to dissociation and setting by means of cooling.
Claim 3
Dependent Claim
16 words
Method according to claim 1, wherein a non-solvent for the polymer is employed as compound B.
Claim 4
Dependent Claim
38 words
Method according to claim 1, wherein a compound B is used having a dissolving temperature with regard to the polymer lying at least 50° C. higher than the dissolving temperature of compound A with regard to the polymer.
Claim 5
Dependent Claim
36 words
Method according to claim 3, using a compound B having a dissolving temperature with regard to the polymer lying at least 100° C. higher than the dissolving temperature of compound A with regard to the polymer.
Claim 6
Dependent Claim
17 words
Method according to claim 1, wherein as compound B a swelling agent for the polymer is employed.
Claim 7
Dependent Claim
24 words
Method according to claim 1, using a polymer and a compound A which form a system displaying in liquid aggregate state a miscibility gap.
Claim 8
Dependent Claim
11 words
Method according to claim 1, wherein as polymer, polyolefin is used.
Claim 9
Dependent Claim
11 words
Method according to claim 7, wherein as polymer, polypropylene is used.
Claim 10
Dependent Claim
16 words
Method according to claim 7, wherein as compound A, edible oil or edible fat is used.
Claim 11
Dependent Claim
49 words
Method according to claim 9, wherein as compound B, a compound miscible with edible oil or edible fat is used, which compound is a non-solvent for the polymer or the dissolving ability of which compound for the polymer is considerably less than that of edible oil or edible fat.
Claim 12
Dependent Claim
13 words
Method according to claim 10, wherein as compound B, castor oil is used.
Claim 13
Dependent Claim
13 words
Method according to claim 9, wherein as compound A, soy oil is used.
Claim 14
Dependent Claim
14 words
Method according to claim 9, wherein as compound A, palm seed oil is used.
Claim 15
Dependent Claim
18 words
Method according to claim 1, wherein said solution is shaped into membranes in the form of hollow filaments.
Claim 16
Dependent Claim
18 words
Method according to claim 1, wherein the solution is shaped into membranes in the form of flat foils.
Claim 17
Dependent Claim
92 words
Method according to claim 14, wherein the solution is extruded into a spinning tube which contains compound A as bath liquid, whereby the bath liquid in the spinning tube possesses a temperature below the phase separation temperature and the membrane and the compound A are led through the spinning tube in the same direction with about the same or only insignificantly different linear velocity, the membrane is then withdrawn from the spinning tube under slight tension, and the formed hollow filament structure, after its solidification, if necessary is extracted with a solvent.
Claim 18
Dependent Claim
110 words
Method according to claim 14, wherein the solution is extruded into a spinning tube which contains as bath liquid a mixture of compound A and compound B in the same relative ratio amounts as are present in the solution being extruded, whereby the bath liquid in the spinning tube possesses a temperature below the phase separation temperature and the membrane and the bath liquid are led through the spinning tube in the same direction with about the same or only insignificantly different linear velocity, the membrane is then withdrawn from the spinning tube under slight tension and the formed hollow filament structure, after its solidification, is extracted with a solvent.
Claim 19
Dependent Claim
27 words
Method according to claim 16, wherein between outlet surface of an employed hollow filament nozzle and liquid surface in the spinning tube, an air space is maintained.
Claim 20
Dependent Claim
27 words
Method according to claim 17, wherein between outlet surface of an employed hollow filament nozzle and liquid surface in the spinning tube, an air space is maintained.
Claim 21
Dependent Claim
31 words
Method according to claim 1, wherein the liquid compound A additionally contains one or more further solvents and the compound B is employed in mixture with one or more further compounds.
Claim 22
Dependent Claim
25 words
Method according to claim 1, wherein 5-90% by weight polymer is dissolved in 10-95% by weight of the mixture of liquid compounds A and B.
Claim 23
Dependent Claim
27 words
Method according to claim 21, wherein 15-30% by weight of polymer is dissolved in 85-70% by weight of the mixture of the liquid compounds A and B.
Claim 24
Dependent Claim
37 words
Method according to claim 1, wherein the mixture of A and B is composed of 60-90% by weight of a solvent for the polymer and 10-40% by weight of a non-solvent or swelling agent for the polymer.
Claim 25
Dependent Claim
13 words
Method according to claim 1, further comprising the step of shaping the solution.
Claim 26
Dependent Claim
13 words
Method according to claim 1, further comprising th step of extracting compound A.
Claim 27
Dependent Claim
13 words
Method according to claim 1, further comprising the step of extracting compound B.
Claim 28
Dependent Claim
15 words
Method according to claim 1, further comprising the step of extracting compounds A and B.
References Cited (Backward Citations)
US1707164A
Cited
GB385653A
Cited
US2214442A
Cited
US2419277A
Cited
US2658879A
Cited
US2777824A
Cited
US2959570A
Cited
US3017372A
Cited
US3017238A
Cited
US3159592A
Cited
US3322611A
Cited
US3582393A
Cited
US3669740A
Cited
US3915912A
Cited
US3940405A
Cited
US4107115A
Cited
US4073733A
Cited
US4035459A
Cited
US4322381A
Cited
US4332765A
Cited
US4315880A
Cited
US4323534A
Cited
US4490431A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-06-09 | 1989-12-09 | 1990-06-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-06-09 | 1993-12-09 | 1994-06-10 | $3760.00 | Window Closed / Lapsed |