US4938807A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for production of grain oriented electrical steel sheet having high flux density
Assignee: Nippon Steel Corp
•
Filing: 1989-01-25
•
Granted: 1990-07-03
•
Expires: 2009-01-25
Abstract
Abstract Disclosed is a process for the preparation of a grain oriented silicon steel about sheet having a high flux density, which comprises hot-rolling a slab comprising 1.5 to 4.8% by weight of Si, 0.012 to 0.050% by weight of Al, 0.0010 to 0.0120% by weight of N, 0.0020 to 0.0150% by weight of Ti, up to 0.45% by weight of Mn and up to 0.012% by weight of at least one member selected S and Se, which satisfies the requirement 0.06 to 0.6 of Ti/N (at % ratio) and Mn/(S+Se)≧4.0 (weight ratio) with the balance comprising Fe and unavoidable impurities, to cold-rolling, performing decarburization annealing, coating an annealing separator on the steel sheet surface, then performing finish annealing, and performing a nitriding treatment of the steel sheet during the period of from the point of termination of final cold rolling to the point of initiation of secondary recrystallization at the finish annealing step.
Inventors
- 👤 Nobuyuki Takahashi
- 👤 Yozo Suga
- 👤 Katsuro Kuroki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 06:02
CPC Classifications
C; C21; C21D; C21D8/00; C21D8/12; C21D8/1244; C21D8/1255; C22; C22C; C22C38/00; C22C38/02
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
195 words
A process for the preparation of a grain oriented silicon steel sheet having a high flux density, which comprises heating a slab at a slab heating temperature of lower than 1200? C., said slab comprising 1.5 to 4.8% by weight of Si, 0.012 to 0.050% by weight of Al, 0.0010 to 0.0120% by weight of N, 0.002 to 0.0150% by weight of Ti, up ro 0.45% by weight of Mn and up to 0.012% by weight of at lest one member selected from S and Se, which satisfies the requirement of 0.06 to 0.6 of Ti/N (at % ratio) and Mn/(S+Se)≧4.0 (weight ratio), with the balance comprising Fe and unavoidable impurities, not-rolling the slab, performing cold rolling once or at least twice to obtain a final thickness, performing decarburization annealing in a wet hydrogen or wet hydrogen/nitrogen mixed atmosphere, coating an annealing separator on the st®el sheet surface, performing finish annealing for secondary recrystallization and purification of the steel sheet, and performing a nitriding treatment of the steel sheet during the period of from the point of termination of final cold rolling to the point of initiation of secondary recrystallization at the finish annealing step.
Claim 2
Dependent Claim
195 words
A process for the preparation of a grain oriented silicon steel sheet having a high flux density, which comprises heating a slab at a slab heating temperature of lower than 1200? C., said slab comprising 1.5 to 4.8% by weight of Si, 0.012 to 0.050% by weight of Al, 0.0010 to 0.0120% by weight of N, 0.002 to 0.0150% by weight of Ti, up ro 0.45% by weight of Mn and up to 0.012% by weight of at lest one member selected from S and Se, which satisfies the requirement of 0.06 to 0.6 of Ti/N (at % ratio) and Mn/(S+Se)≧4.0 (weight ratio), with the balance comprising Fe and unavoidable impurities, not-rolling the slab, performing cold rolling once or at least twice to obtain a final thickness, performing decarburization annealing in a wet hydrogen or wet hydrogen/nitrogen mixed atmosphere, coating an annealing separator on the st®el sheet surface, performing finish annealing for secondary recrystallization and purification of the steel sheet, and performing a nitriding treatment of the steel sheet during the period of from the point of termination of final cold rolling to the point of initiation of secondary recrystallization at the finish annealing step.
Claim 3
Dependent Claim
23 words
A process according to claim 1, wherein the nitriding treatment is carried out during the temperature elevation period at the final annealing step.
Claim 4
Dependent Claim
19 words
A process according to claim 2, wherein the compound having a nitriding capacity is incorporated i the annealing separator.
Claim 5
Dependent Claim
24 words
A process according to claim 2, wherein a gas having a nitriding capacity is incorporated in an atmosphere gas at the final annealing step.
Claim 6
Dependent Claim
29 words
A process according to claim 1, wherein the nitriding treatment is performed in an atmosphere of a gas having a nitriding capacity after soaking at the decarburization annealing step.
Claim 7
Dependent Claim
37 words
A process according to claim 1 wherein after decarburization annealing, the nitriding treatment is performed by positioning a heat treating furnace after a decarburization annealing furnace, and providing said heat treating furnace with a nitriding gaseous atmosphere.
References Cited (Backward Citations)
US3159511A
Cited
JPS4851852A
Cited
JPS5113469A
Cited
JPS5113461A
Cited
JPS5120716A
Cited
US4171994A
Cited
JPS5319913A
Cited
JPS5745818A
Cited
JPS5956522A
Cited
JPS6240315A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-02 | 1994-01-01 | 1994-07-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-02 | 1998-01-01 | 1998-07-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-02 | 2002-01-01 | 2002-07-03 | $7700.00 | Window Closed / Lapsed |