Method of producing composite oxide superconducting wires using a powder bath
Assignee: Kanto Yakin Kogyo Co Ltd
•
Filing: 1989-02-03
•
Granted: 1990-06-26
•
Expires: 2009-02-03
Abstract
Abstract A superconductive substance is formed into fine wires readily without producing surface defects on the wires and correctly with a predetermined even diametric thickness. Highly refractory metallic core is heated to a predetermined temperature higher than the eutectic point of powders which constitute the superconductive substance, and passed through said powders whereby the powders which make contact with the core melt and adhere to the core with a predetermined uniform thickness, forming a fine wire made from the superconductive substance.
Inventors
- 👤 Susumu Takahashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 09:13
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0801; Y; Y10; Y10S; Y10S505/00; Y10S505/725; Y10S505/739; Y10S505/74
Claims Analysis
Total Claims: 2
Claim 1
Independent Claim
278 words
A method for producing a composite oxide superconductive wire, comprising, providing a bath containing a powder mixture of the constituent powders, which produce a rare earth alkaline earth copper oxide superconductive substance, said constituent powders comprising either a mixture of Y 2 O 3 , BaCO 3 and CuO in a stoichiometric ratio to form YBa 2 Cu 3 O x , wherein x is in the range of approximately 6.5 to 7.2, or a mixture of La, Ba and CuO in a stoichiometric ratio to form (La, Ba) 2 Cu O 4 , providing a fine, Mo wire of a desired diameter and having a melting point which is higher than the eutectic point of the constituent powders of said superconductive substance, heating said wire to a predetermined temperature higher than the eutectic point of said constituent powders; passing said heated fine wire through the constituent powders, whereby the powders which have been melted by coming into contact with the heated fine wire, melt and adhere to the wire to form a precursor oxide film of the superconductive substance on the wire at a predetermined diametric thickness; subjecting the wire and the film thereon to a heat treatment under an oxygen atmosphere for annealing to form an oxide film of the superconductive substance on the wire; and passing the annealed wire through a molten bath containing a coating material selected from the group consisting of copper, aluminum, lead, or alloys thereof, the temperature of said bath being lower than the melting point of the annealed wire, including the film of the superconductive substance thereon, whereby a protective coating is additionally formed over the film of superconductive substance.
Claim 2
Independent Claim
278 words
A method for producing a composite oxide superconductive wire, comprising, providing a bath containing a powder mixture of the constituent powders, which produce a rare earth alkaline earth copper oxide superconductive substance, said constituent powders comprising either a mixture of Y 2 O 3 , BaCO 3 and CuO in a stoichiometric ratio to form YBa 2 Cu 3 O x , wherein x is in the range of approximately 6.5 to 7.2, or a mixture of La, Ba and CuO in a stoichiometric ratio to form (La, Ba) 2 Cu O 4 , providing a fine, Mo wire of a desired diameter and having a melting point which is higher than the eutectic point of the constituent powders of said superconductive substance, heating said wire to a predetermined temperature higher than the eutectic point of said constituent powders; passing said heated fine wire through the constituent powders, whereby the powders which have been melted by coming into contact with the heated fine wire, melt and adhere to the wire to form a precursor oxide film of the superconductive substance on the wire at a predetermined diametric thickness; subjecting the wire and the film thereon to a heat treatment under an oxygen atmosphere for annealing to form an oxide film of the superconductive substance on the wire; and passing the annealed wire through a molten bath containing a coating material selected from the group consisting of copper, aluminum, lead, or alloys thereof, the temperature of said bath being lower than the melting point of the annealed wire, including the film of the superconductive substance thereon, whereby a protective coating is additionally formed over the film of superconductive substance.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-06-25 | 1993-12-25 | 1994-06-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-06-25 | 1997-12-25 | 1998-06-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-06-25 | 2001-12-25 | 2002-06-26 | $7700.00 | Window Closed / Lapsed |