High surface area metal oxide foams and method of producing the same
Assignee: Cabot Corp
•
Filing: 1988-03-07
•
Granted: 1990-06-26
•
Expires: 2008-03-07
Abstract
Abstract The present invention includes metal oxide foam particles and a method of making the same. A decomposable metal salt feed solution is injected into a hot atomizing gas. The mixture of hot atomizing gas and feed solution is maintained in the reactor until the feed solution converts to metal oxide foam particles. The metal oxide foam particles have a high specific surface area.
Inventors
- 👤 Merrill Jordan, deceased
- 👤 Steven R. Reznek
- 👤 Matthew Neville
- 👤 Brian A. Soucy
- 👤 Bruce E. Mackay
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 21:12
CPC Classifications
C; C01; C01G; C01G25/00; C01G25/02; C01B; C01B13/00; C01B13/14; C01B13/34; C01F; C01F7/00; C01F7/02; C01F7/30; C01F7/32; C01G23/00; C01G23/04; C01G23/047; C01P; C01P2004/00; C01P2004/01; C01P2004/03; C01P2004/04; C01P2006/00; C01P2006/12; C01P2006/13
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
118 words
A method for producing metal oxide foam particles in a reactor, the reactor including a burner section and a reaction section, said method comprising: injecting, in the burner section, a decomposable metal salt containing feed solution into a gas traveling through the burner section, the gas having a Mach number sufficient to kinetically atomize the decomposable metal salt containing feed solution; and maintaining, in the reaction section, the gas and the injected decomposable metal salt containing feed solution until the injected decomposable metal salt containing feed solution converts to metal oxide foam particles; wherein the temperature of the gas as the decomposable metal salt containing feed solution is injected therein during said injecting step is at least 700K.
Claim 2
Independent Claim
118 words
A method for producing metal oxide foam particles in a reactor, the reactor including a burner section and a reaction section, said method comprising: injecting, in the burner section, a decomposable metal salt containing feed solution into a gas traveling through the burner section, the gas having a Mach number sufficient to kinetically atomize the decomposable metal salt containing feed solution; and maintaining, in the reaction section, the gas and the injected decomposable metal salt containing feed solution until the injected decomposable metal salt containing feed solution converts to metal oxide foam particles; wherein the temperature of the gas as the decomposable metal salt containing feed solution is injected therein during said injecting step is at least 700K.
Claim 3
Dependent Claim
34 words
The method as recited in claim 1 wherein the gas having a Mach number sufficient to kinetically atomize the decomposable metal salt containing feed solution has a Mach number of at least Mach 0.2.
Claim 4
Dependent Claim
46 words
The method as recited in claim 1 wherein the decomposable metal salt of the decomposable metal salt containing feed solution is selected from the group consisting of aluminum nitrate, aluminum sulfate, aluminum chloride, titanium sulfate, titanium chloride, zirconium nitrate, zirconium sulfate, zirconium chloride and mixtures thereof.
Claim 5
Dependent Claim
61 words
The method as recited in claim 1 wherein the decomposable metal salt containing feed solution includes a sufficient amount of a surface area stabilizer salt solution to produce metal oxide foam particles according to the formula M 1--x S x wherein M is the metal oxide, S is a surface area stabilizer salt and X ranges between zero and twenty percent.
Claim 6
Dependent Claim
29 words
The method as recited in claim 4 wherein S is selected from the group consisting of strontium oxide, barium oxide, zirconium oxide, cesium oxide, lanthanum oxide and mixtures thereof.
Claim 7
Dependent Claim
76 words
The method as recited in claim 1 wherein the temperature of at least 700K. of the gas as the decomposable metal salt containing feed solution is injected therein during said injecting step and the residence time in the reaction section during said maintaining step of the gas and the injected decomposable metal salt containing feed solution are sufficient to produce metal oxide foam particles with a specific surface area of at least 25 m 2 /g.
Claim 8
Dependent Claim
46 words
The method as recited in claim 1 wherein during said maintaining step no heat is added to the reaction section or developed therein from a chemical reaction other than from the conversion of the decomposable metal salt containing feed solution to the metal oxide foam particles.
Claim 9
Independent Claim
117 words
A method for producing alumina containing foamed particles in a reactor, the reactor including a burner section and a reaction section, said method comprising: injecting, in the burner section a decomposable aluminum salt containing feed solution into an gas traveling through the burner section, the gas having a Mach number sufficient to kinetically atomize the decomposable aluminum salt containing feed solution; and maintaining, in the reaction section, the gas and the injected decomposable aluminum salt containing feed solution until the injected decomposable aluminum salt containing feed solution converts to alumina foam particles; wherein the temperature of the gas as the decomposable aluminum salt containing feed solution is injected therein during said injecting step is at least 700K.
Claim 10
Independent Claim
117 words
A method for producing alumina containing foamed particles in a reactor, the reactor including a burner section and a reaction section, said method comprising: injecting, in the burner section a decomposable aluminum salt containing feed solution into an gas traveling through the burner section, the gas having a Mach number sufficient to kinetically atomize the decomposable aluminum salt containing feed solution; and maintaining, in the reaction section, the gas and the injected decomposable aluminum salt containing feed solution until the injected decomposable aluminum salt containing feed solution converts to alumina foam particles; wherein the temperature of the gas as the decomposable aluminum salt containing feed solution is injected therein during said injecting step is at least 700K.
Claim 11
Dependent Claim
34 words
The method as recited in claim 8 wherein the gas having a Mach number sufficient to kinetically atomize the decomposable aluminum salt containing feed solution has a Mach number of at least Mach 0.2.
Claim 12
Dependent Claim
34 words
The method as recited in claim 8 wherein the decomposable aluminum salt of the decomposable aluminum salt containing feed solution is selected from the group consisting of aluminum nitrate, aluminum sulfate and aluminum chloride.
Claim 13
Dependent Claim
58 words
The method as recited in claim 8 wherein the decomposable aluminum salt containing feed solution includes a sufficient amount of a surface area stabilizing salt solution to produce alumina foam particles according to the formula M 1-x S x wherein M is alumina, S is a surface area stabilizer salt and X ranges between zero and twenty percent.
Claim 14
Dependent Claim
29 words
The method as recited in claim 11 wherein S is selected from the group consisting of strontium oxide, barium oxide, zirconium oxide, cesium oxide, lanthanum oxide and mixtures thereof.
Claim 15
Dependent Claim
30 words
The method as recited in claim 8 wherein during said maintaining step the temperature of the gas and the injected decomposable aluminum salt containing feed solution is at least 1200K.
Claim 16
Dependent Claim
36 words
The method as recited in claim 8 wherein during said maintaining step the residence time in the reaction section of the gas and the injected decomposable aluminum salt containing feed solution is less than thirty-five milliseconds.
Claim 17
Dependent Claim
75 words
The method as recited in claim 8 wherein the temperature of at least 700K. of the gas as the decomposable aluminum salt containing feed solution is injected therein during said injecting step and the residence time in the reaction section during said maintaining step of the gas and the injected decomposable aluminum salt containing feed solution are sufficient to produce alumina foam particles with a specific surface area of at least 25 m 2 /g.
Claim 18
Dependent Claim
45 words
The method as recited in claim 8, wherein during said maintaining step no heat is added to the reaction section or developed therein from a chemical reaction other than from the conversion of the aluminum salt containing feed solution to the metal oxide foam particle.
References Cited (Backward Citations)
US3172753A
Cited
US3161468A
Cited
US3273962A
Cited
US4018881A
Cited
US3961036A
Cited
US4048290A
Cited
US4179408A
Cited
US4292290A
Cited
US4331645A
Cited
JPS58176127A
Cited
JPS59227724A
Cited
JPS6016819A
Cited
JPS60131826A
Cited
US4755373A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-06-25 | 1993-12-25 | 1994-06-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-06-25 | 1997-12-25 | 1998-06-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-06-25 | 2001-12-25 | 2002-06-26 | $7700.00 | Window Closed / Lapsed |