Method for preparing polyester-polyepoxide compositions of high melt viscosity
Assignee: General Electric Co
•
Filing: 1989-03-13
•
Granted: 1990-06-12
•
Expires: 2009-03-13
Abstract
Abstract Polyesters, especially poly(ethylene terephthalate) and poly(butylene terephthalate), having a substantial proportion of free carboxylic acid groups are caused to react with polyepoxy compounds, especially poly(O- or N-epoxyalkyl-substituted) cyclic amides, imides and amidates and preferably triglycidyl isocyanurate, in the presence of various amines or salts as catalysts. The preferred catalysts are fatty acid salts such as sodium sterate. The products have very high melt viscosities and are useful in such operations as blow molding.
Inventors
- 👤 Linda L. McCracken
- 👤 Kelvin T. Okamoto
- 👤 Choong Y. Han
- 👤 Sterling B. Brown
- 👤 Michael G. Minnick
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 11:56
CPC Classifications
C; C08; C08L; C08L63/00
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
117 words
A method for preparing a branched polymer which comprises effecting reaction between (A) at least one thermoplastic polyester having a substantial proportion of free carboxylic acid groups and (B) at least one polyepoxy compound in the presence of (C) at least one catalyst compound selected from the group consisting of (1) primary alkylamines in which the alkyl group contains at least about 8 carbon atoms and (2) salts free from direct carbon-phosphorus bonds and containing at least one of alkali and alkaline earth metal cations and halide anions; said catalyst being employed in an amount effective to afford a product having a higher melt viscosity than that of a corresponding product from reagents A and B alone.
Claim 2
Independent Claim
117 words
A method for preparing a branched polymer which comprises effecting reaction between (A) at least one thermoplastic polyester having a substantial proportion of free carboxylic acid groups and (B) at least one polyepoxy compound in the presence of (C) at least one catalyst compound selected from the group consisting of (1) primary alkylamines in which the alkyl group contains at least about 8 carbon atoms and (2) salts free from direct carbon-phosphorus bonds and containing at least one of alkali and alkaline earth metal cations and halide anions; said catalyst being employed in an amount effective to afford a product having a higher melt viscosity than that of a corresponding product from reagents A and B alone.
Claim 3
Dependent Claim
67 words
A method according to claim 1 wherein the polepoxy compound is a poly(O- or N-epoxyalkyl-substituted) cyclic amide, imide or imidate and the polyester comprises the structural units of the formula ##STR3## wherein each R 1 is independently a divalent aliphatic, alicyclic or aromatic radical containing about 2-10 carbon atoms and each R 2 is independently a divalent aliphatic, alicyclic or aromatic radical containing about 2-10 carbon atoms.
Claim 4
Dependent Claim
36 words
A method according to claim 2 wherein the polyepoxy compound contains a single triazine, barbiturate, hydantoin, uracil, pyromellitic diimide, piperazinedione or parabanate moiety and the epoxyalkyl groups therein are bonded directly to oxygen or nitrogen atoms.
Claim 5
Dependent Claim
40 words
A method according to claim 3 wherein the polyepoxy compound is triglycidyl isocyanurate and the polyester is a poly(ethylene terephthalate) or a poly(butylene terephthalate) having a carboxylic acid end group concentration in the range of about 10-100 microequivalents per gram.
Claim 6
Dependent Claim
30 words
A method according to claim 4 wherein about 0.05-3.0 parts by weight of polyepoxy compound and about 0.01-0.5 part by weight of catalyst is employed per 100 parts of polyester.
Claim 7
Dependent Claim
18 words
A method according to claim 5 wherein the catalyst comprises a primary alkylamine containing about 10-20 carbon atoms.
Claim 8
Dependent Claim
30 words
A method according to claim 5 wherein the catalyst is potassium bromide, lithium iodide, lithium fluoride, sodium acetate, sodium caproate, sodium benzoate, sodium ascorbate, sodium dihydrogen phosphate or dodecyltrimethylammonium bromide.
Claim 9
Dependent Claim
26 words
A method according to claim 4 wherein the catalyst is an alkali metal salt of an aliphatic carboxylic acid containing at least about 10 carbon atoms.
Claim 10
Dependent Claim
30 words
A method according to claim 8 wherein about 0.1-3.0 parts by weight of polyepoxy compound and about 0.01-0.10 part by weight of catalyst is employed per 100 parts of polyester.
Claim 11
Dependent Claim
12 words
A method according to claim 9 wherein the catalyst is sodium stearate.
Claim 12
Dependent Claim
94 words
A composition comprising (A) at least one thermoplastic polyester having a substantial proportion of free carboxylic acid groups, (B) at least one poly(O- or N-epoxyalkyl-substituted) cyclic amide, imide or imidate, and any reaction products thereof, and (C) a catalytically effective amount to increase melt viscosity of at least one compound selected from the group consisting of (1) primary alkylamines in which the alkyl group contains at least about 8 carbon atoms and (2) salts free from direct carbon-phosphorous bonds and containing at least one of alkali and alkaline earth metal cations and halide anions.
Claim 13
Dependent Claim
94 words
A composition comprising (A) at least one thermoplastic polyester having a substantial proportion of free carboxylic acid groups, (B) at least one poly(O- or N-epoxyalkyl-substituted) cyclic amide, imide or imidate, and any reaction products thereof, and (C) a catalytically effective amount to increase melt viscosity of at least one compound selected from the group consisting of (1) primary alkylamines in which the alkyl group contains at least about 8 carbon atoms and (2) salts free from direct carbon-phosphorous bonds and containing at least one of alkali and alkaline earth metal cations and halide anions.
Claim 14
Dependent Claim
52 words
A composition according to claim 1 wherein the polyesters comprises structural units of the formula ##STR4## wherein each R 1 is independently a divalent alipahtic, alicyclic or aromatic radical containing about 2-10 carbon atoms and each R 2 is independently a divalent aliphatic, alicyclic or aromatic radical containing about 2-10 carbon atoms.
Claim 15
Dependent Claim
36 words
A composition according to claim 12 wherein the polyepoxy compound contains a single triazine, barbiturate, hydantoin, uracil, pyromellitic diimide, piperazinedione or parabanate moiety and the epoxyalkyl groups therein are bonded directly to oxygen or nitrogen atoms.
Claim 16
Dependent Claim
40 words
A composition according to claim 13 wherein the polyepoxy compound is triglycidyl isocyanurate and the polyester is a poly(ethylene terephthalate) or a poly(butylene terephthalate) having a carboxylic acid end group concentration in the range of about 10-100 microequivalents per gram.
Claim 17
Dependent Claim
30 words
A composition according to claim 14 wherein about 0.05-3.0 parts by weight of polyepoxy compound and about 0.01-0.10 part by weight of catalyst is employed per 100 parts of polyester.
Claim 18
Dependent Claim
18 words
A composition according to claim 15 wherein the catalyst comprises a primary alkylamine containing about 10-20 carbon atoms.
Claim 19
Dependent Claim
30 words
A composition according to claim 15 wherein the catalyst is potassium bromide, lithium iodide, lithium fluoride, sodium acetate, sodium caproate, sodium benzoate, sodium ascorbate, sodium dihydrogen phosphate or dodecyltrimethylammonium bromide.
Claim 20
Dependent Claim
26 words
A composition according to claim 14 wherein the catalyst is an alkali metal salt of an aliphatic carboxylic acid containing at least about 10 carbon atoms.
Claim 21
Dependent Claim
30 words
A composition according to claim 18 wherein about 0.05-3.0 parts by weight of polyepoxy compound and about 0.01-0.10 part by weight of catalyst is employed per 100 parts of polyester.
Claim 22
Dependent Claim
12 words
A composition according to claim 19 wherein the catalyst is sodium stearate.
References Cited (Backward Citations)
US4101601A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-06-11 | 1993-12-11 | 1994-06-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-06-11 | 1997-12-11 | 1998-06-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-06-11 | 2001-12-11 | 2002-06-12 | $7700.00 | Window Closed / Lapsed |