Method and apparatus for determining throwing power of an electroplating solution
Assignee: Shipley Co Inc
•
Filing: 1989-11-20
•
Granted: 1990-06-12
•
Expires: 2009-11-20
Abstract
Abstract A composition for electroplating copper onto a conductive surface comprising a solution soluble copper salt and an acid electrolyte, said copper salt being present in a concentration of from about 1 to 10 grams per liter of solution and said acid being present in a concentration whereby the acid to copper ratio preferably varies between about 30 to 1 and 50 to 1. The composition is especially useful for the plating of walls of cylindrical openings having a ratio of height to diameter of at least 10 to 1 and a length of at least 0.100 inches.
Inventors
- 👤 Roger F. Bernards
- 👤 Gordon Fisher
- 👤 Wade Sonnenberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 13:14
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/40; H05K3/42; C; C25; C25D; C25D3/00; C25D3/02; C25D3/38; H05K2203/00; H05K2203/16; H05K2203/162
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
100 words
A device for measuring the throwing power of an electroplating solution, said device comprising two anodes and a cathode suspended in a chamber adapted to contain a plating solution, said cathode being suspended between said anodes and comprising two flat electrode portions in electrical contact with each other, in parallel relationship to each other and spaced apart from each other to define a space adapted to contain plating solution, each of said flat electrode portions having electrode portions electrically isolated from a center electrode, and means for measuring the current on said first electrode portions and center electrode during plating.
Claim 2
Independent Claim
100 words
A device for measuring the throwing power of an electroplating solution, said device comprising two anodes and a cathode suspended in a chamber adapted to contain a plating solution, said cathode being suspended between said anodes and comprising two flat electrode portions in electrical contact with each other, in parallel relationship to each other and spaced apart from each other to define a space adapted to contain plating solution, each of said flat electrode portions having electrode portions electrically isolated from a center electrode, and means for measuring the current on said first electrode portions and center electrode during plating.
Claim 3
Dependent Claim
18 words
The device of claim 1 where each flat electrode portion contains two edge electrodes and one center electrode.
Claim 4
Dependent Claim
15 words
The device of claim 1 where said flat electrode portions are perpendicular to the anodes.
Claim 5
Dependent Claim
13 words
The device of claim 1 where said cathode is centered between said anodes.
Claim 6
Independent Claim
190 words
A method for maximizing throwing power of an electroplating solution, said method comprising the steps of: i. placing a sample of a test plating solution having a first acid to metal ratio within a device having two anodes and a cathode suspended into the plating solution, said cathode comprising two flat electrode portions in electrical contact with each other, in parallel relationship to each other and spaced apart from each other to define a space containing said plating solution, each of said flat electrode portions having first electrode portions and a center electrode electrically separated from said first electrode portions; ii. plating metal from said test plating solution while measuring the current on said first electrode portions and center electrode during plating and forming a ratio of said currents; iii. repeating the process for test plating solutions having differing acid to plating metal ratios and selecting a test solution having a ratio of current densities ranging between eighty percent of the maximum ratio and the maximum ratio; and iv. maintaining plating solution within said device during electroplating while periodically adjusting the acid to metal ratio to maintain said selected ratio.
Claim 7
Independent Claim
190 words
A method for maximizing throwing power of an electroplating solution, said method comprising the steps of: i. placing a sample of a test plating solution having a first acid to metal ratio within a device having two anodes and a cathode suspended into the plating solution, said cathode comprising two flat electrode portions in electrical contact with each other, in parallel relationship to each other and spaced apart from each other to define a space containing said plating solution, each of said flat electrode portions having first electrode portions and a center electrode electrically separated from said first electrode portions; ii. plating metal from said test plating solution while measuring the current on said first electrode portions and center electrode during plating and forming a ratio of said currents; iii. repeating the process for test plating solutions having differing acid to plating metal ratios and selecting a test solution having a ratio of current densities ranging between eighty percent of the maximum ratio and the maximum ratio; and iv. maintaining plating solution within said device during electroplating while periodically adjusting the acid to metal ratio to maintain said selected ratio.
Claim 8
Dependent Claim
14 words
The method of claim 5 where the plating solution is a copper plating solution.
Claim 9
Dependent Claim
21 words
The method of claim 6 where the dissolved copper content varies from about 1 to 10 grams per liter of solution.
Claim 10
Dependent Claim
25 words
The method of claim 5 where the ratio of acid, expressed as sulfuric acid, to copper varies between 30 to 1 and 70 to 1.
Claim 11
Dependent Claim
17 words
The method of claim 8 where the ratio varies between 45 to 1 and 60 to 1.
Claim 12
Dependent Claim
16 words
The method of claim 5 where the acid is sulfuric acid and the metal is copper.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-06-11 | 1993-12-11 | 1994-06-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-06-11 | 1997-12-11 | 1998-06-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-06-11 | 2001-12-11 | 2002-06-12 | $7700.00 | Window Closed / Lapsed |