US4929514A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Thin film media for high density longitudinal magnetic recording
Assignee: HP Inc
•
Filing: 1988-03-22
•
Granted: 1990-05-29
•
Expires: 2008-03-22
Abstract
Abstract A magnetic thin film materials system (10, 10') is provided, comprising a thin magnetic film (16) formed on a non-magnetic underlayer (14) formed on a substrate (12). In particular, the magnetic film comprises a composition consisting essentially of CoCrPt, with Cr ranging from about 10 to 20 at %, Pt ranging from about 1 to 20 at % and the balance Co. The underlayer consists essentially of chromium. The magnetic layer ranges in thickness from about 200 to 1,200 Å, while the non-magnetic underlayer ranges in thickness from about 500 to 5,000 Å. The platinum control film coercivity, while chromium provides corrosion resistance. In addition, chromium controls the recorded magnetic transition noise properties. An increase in Cr content in these alloys beyond about 10 at % increases the corrosion resistance and unexpectedly lowers the transition noise significantly. Coercivities of from about 500 to greater than 2,000 Oe and magnetization-thickness products from 1 to 6×10 -3 emu/cm 2 are attained by the magnetic recording system of the invention. A thin carbon wear layer (18) (about 200 to 800 Å) is provided over the magnetic layer, with an optional thin chromium adhesion layer (20) (0 to about 500 Å) interposed therebetween.
Inventors
- 👤 Bangalore R. Natarajan
- 👤 Robert G. Walmsley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 23:39
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/64; G11B5/65; G11B5/656; G11B5/73; G11B5/72; G11B5/722; G11B5/727; G11B5/7368; G11B5/7373; G11B5/739; G11B5/73911; G11B5/73913; G11B5/73917; G11B5/73919; G11B5/73921; H; H01; H01F; H01F10/00; H01F10/08; H01F10/10; H01F10/12; H01F10/16; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10S428/922; Y10S428/9265; Y10S428/928; Y10T; Y10T428/00; Y10T428/12; Y10T428/12465; Y10T428/12493; Y10T428/12535; Y10T428/12542; Y10T428/12576; Y10T428/12611; Y10T428/12771; Y10T428/12806; Y10T428/12826; Y10T428/12847; Y10T428/12854; Y10T428/12861; Y10T428/12944
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
106 words
A magnetic film of an alloy of cobalt, platinum, and chromium formed on a layer of chromium, said layer of chromium having a thickness of about 1,500 to 3,000 Å, and consisting essentially of about 1 to 20 at% platinum, about 10 to 20 at% chromium, and the balance cobalt, in which the coercivity of said film is primarily proportional to the percentage of platinum in said alloy and the saturation magnetization-thickness product of said alloy is primarily proportional to Cr and Pt content and the film thickness thereof, said alloy evidencing improved corrosion resistance and signal-to-noise ratio "compared to a cobalt-platinum alloy containing no chromium".
Claim 2
Dependent Claim
106 words
A magnetic film of an alloy of cobalt, platinum, and chromium formed on a layer of chromium, said layer of chromium having a thickness of about 1,500 to 3,000 Å, and consisting essentially of about 1 to 20 at% platinum, about 10 to 20 at% chromium, and the balance cobalt, in which the coercivity of said film is primarily proportional to the percentage of platinum in said alloy and the saturation magnetization-thickness product of said alloy is primarily proportional to Cr and Pt content and the film thickness thereof, said alloy evidencing improved corrosion resistance and signal-to-noise ratio "compared to a cobalt-platinum alloy containing no chromium".
Claim 3
Dependent Claim
17 words
The magnetic film of claim 1 wherein said platinum concentration ranges from about 3 to 10 at%.
Claim 4
Dependent Claim
14 words
The magnetic film of claim 2 wherein said platinum concentration is about 4 at%.
Claim 5
Dependent Claim
17 words
The magnetic film of claim 1 wherein said chromium concentration ranges from about 14 to 16 at%.
Claim 6
Dependent Claim
14 words
The magnetic film of claim 4 wherein said chromium concentration is about 15 at%.
Claim 7
Dependent Claim
17 words
The magnetic film of claim 1 wherein said film thickness ranges from about 200 to 1,200 Å.
Claim 8
Dependent Claim
17 words
The magnetic film of claim 6 wherein said film thickness ranges from about 500 to 1,000 Å.
Claim 9
Dependent Claim
14 words
The magnetic film of claim 7 wherein said film is about 600 Å thick.
Claim 10
Dependent Claim
15 words
The magnetic film of claim 1 wherein said chromium layer is about 2,000 Å thick.
Claim 11
Dependent Claim
95 words
A magnetic recording disc comprising a substrate member having a layer of chromium formed on said substrate, a magnetic layer of cobalt, platinum, and chromium formed on said chromium layer and consisting essentially of about 1 to 20 at% platinum, about 10 to 20 at% chromium, and the balance cobalt, said chromium layer interacting with said magnetic layer to permit adjustment of the magnetic and noise properties thereof, and a wear layer disposed over said magnetic layer, said magnetic layer evidencing improved corrosion resistance and signal-to-noise ratio "compared to a cobalt-platinum alloy containing no chromium".
Claim 12
Dependent Claim
95 words
A magnetic recording disc comprising a substrate member having a layer of chromium formed on said substrate, a magnetic layer of cobalt, platinum, and chromium formed on said chromium layer and consisting essentially of about 1 to 20 at% platinum, about 10 to 20 at% chromium, and the balance cobalt, said chromium layer interacting with said magnetic layer to permit adjustment of the magnetic and noise properties thereof, and a wear layer disposed over said magnetic layer, said magnetic layer evidencing improved corrosion resistance and signal-to-noise ratio "compared to a cobalt-platinum alloy containing no chromium".
Claim 13
Dependent Claim
28 words
The disc of claim 10 wherein said substrate consists essentially of a member selected from the group consisting of aluminum, NiP-coated aluminum, alumina-coated aluminum, glass, ceramic, and silicon.
Claim 14
Dependent Claim
44 words
The disc of claim 10 wherein said chromium layer ranges in thickness from about 1,500 to 3,000 Å, said magnetic layer ranges in thickness from about 200 to 1,200 Å, and said thin wear layer ranges in thickness from about 200 to 800 Å.
Claim 15
Dependent Claim
31 words
The disc of claim 12 wherein said magnetic layer ranges in thickness from about 500 to 1,000 Å, and said wear layer ranges in thickness from about 200 to 500 Å.
Claim 16
Dependent Claim
36 words
The disc of claim 10 wherein said wear layer comprises a material selected from the group consisting of carbon, and the oxides, nitrides, and carbides of silicon, titanium, tantalum, niobium, hafnium, zirconium, vanadium, molybdenum, and tungsten.
Claim 17
Dependent Claim
20 words
The disc of claim 10 further provided with an adhesion layer interposed between said magnetic layer and said wear layer.
Claim 18
Dependent Claim
26 words
The disc of claim 15 wherein said adhesion layer comprises a material selected from the group consisting of chromium, titanium, zirconium, hafnium, vanadium, molybdenum, and niobium.
Claim 19
Dependent Claim
17 words
The disc of claim 15 wherein said adhesion layer ranges in thickness up to about 500 Å.
Claim 20
Dependent Claim
27 words
The disc of claim 10 wherein said magnetic layer consists essentially of about 3 to 10 at% platinum, 14 to 16 at% chromium, and the balance cobalt.
Claim 21
Dependent Claim
127 words
A magnetic recording disc comprising a substrate member consisting essentially of NiP-coated aluminum having a layer of chromium ranging in thickness from about 1,500 to 3,000 Å formed on said substrate, a magnetic layer ranging in thickness from about 500 to 1,000 Å and consisting essentially of about 1 to 20 at% platinum, about 10 to 20 at% chromium and the balance cobalt formed on said chromium layer, said chromium layer interacting with said magnetic layer to permit adjustment of the magnetic and noise properties thereof, and a wear layer ranging in thickness from about 200 to 500 Å and consisting essentially of carbon disposed over said magnetic layer, said magnetic layer evidencing improved corrosion resistance and signal-to-noise ratio "compared to a cobalt-platinum alloy containing no chromium".
Claim 22
Dependent Claim
127 words
A magnetic recording disc comprising a substrate member consisting essentially of NiP-coated aluminum having a layer of chromium ranging in thickness from about 1,500 to 3,000 Å formed on said substrate, a magnetic layer ranging in thickness from about 500 to 1,000 Å and consisting essentially of about 1 to 20 at% platinum, about 10 to 20 at% chromium and the balance cobalt formed on said chromium layer, said chromium layer interacting with said magnetic layer to permit adjustment of the magnetic and noise properties thereof, and a wear layer ranging in thickness from about 200 to 500 Å and consisting essentially of carbon disposed over said magnetic layer, said magnetic layer evidencing improved corrosion resistance and signal-to-noise ratio "compared to a cobalt-platinum alloy containing no chromium".
Claim 23
Dependent Claim
31 words
The disc of claim 19 wherein said chromium layer is about 2,000 Å thick, said magnetic layer is about 600 Å thick, and said wear layer is about 400 Å thick.
Claim 24
Dependent Claim
27 words
The disc of claim 19 wherein said magnetic layer consists essentially of about 3 to 10 at% platinum, 14 to 16 at% chromium, and the balance cobalt.
Claim 25
Dependent Claim
23 words
The disc of claim 21 wherein said magnetic layer consists essentially of about 4 at% platinum, 15 at% chromium, and the balance cobalt.
Claim 26
Independent Claim
75 words
A method of reducing noise and improving corrosion resistance in a magnetic recording disc comprising a substrate, a chromium layer ranging in thickness from about 1,500 to 3,000 Å and formed on said substrate, a magnetic layer formed on said chromium layer, and a wear layer formed over said magnetic layer, comprising forming as said magnetic layer a magnetic composition consisting essentially of cobalt, chromium, and platinum containing from about 10 to 20 at% chromium.
Claim 27
Independent Claim
75 words
A method of reducing noise and improving corrosion resistance in a magnetic recording disc comprising a substrate, a chromium layer ranging in thickness from about 1,500 to 3,000 Å and formed on said substrate, a magnetic layer formed on said chromium layer, and a wear layer formed over said magnetic layer, comprising forming as said magnetic layer a magnetic composition consisting essentially of cobalt, chromium, and platinum containing from about 10 to 20 at% chromium.
References Cited (Backward Citations)
JPS5988806A
Cited
US4610911A
Cited
US4774130A
Cited
US4652499A
Cited
US4654276A
Cited
US4789598A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-28 | 1993-11-27 | 1994-05-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-28 | 1997-11-27 | 1998-05-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-28 | 2001-11-27 | 2002-05-29 | $7700.00 | Window Closed / Lapsed |