Glass plate fusion for macro-gradient refractive index materials
Assignee: Integrated Solar Technologies Corp
•
Filing: 1988-11-03
•
Granted: 1990-05-29
•
Expires: 2008-11-03
Abstract
Abstract A glass block (10) comprises a plurality of intermediate glass plates (12i) stacked between a top plate (12t) and a bottom plate (12b). The top and bottom plate each have a selected composition, with a particular index of refraction and a softening temperature. The intermediate plates have compositions intermediate those of the top and bottom plates and are stacked so as to provide a gradient in composition from top to bottom. Heating the assembly at a fusion temperature fuses the plates together to form the glass block. After cooling down to room temperature, the glass block can be shaped to make lenses and other light directing devices. Such lenses have a gradient in the refractive index of at least about 0.085, and gradients approaching 0.5 are achievable. The thickness of the glass block along the optic axis is fairly unlimited, and thicknesses on the order of 10 mm and more are routinely achievable by the process of the invention.
Inventors
- 👤 James J. Hagerty
- 👤 David N. Pulsifer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:06
CPC Classifications
G; G02; G02B; G02B3/00; G02B3/0087; C; C03; C03B; C03B23/00; C03B23/20; C03B23/203
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
144 words
A process for fabricating a glass member having a varying index of refraction along an optic axis comprising (a) stacking a plurality of intermediate glass plates between a top plate and a bottom plate to form an assembly, said top plate comprising a glass of a first composition having a first selected index of refraction and a first softening temperature and said bottom plate comprising a glass of a second composition having a second selected index of refraction and a second softening temperature, said plurality of intermediate glass plates each comprising a composition intermediate that of said top and bottom plates and stacked to achieve a change in composition varying from said first composition to said second composition; (b) heating said assembly to a fusion temperature to fuse said plates to form a fused assembly; and (c) cooling said fused assembly to room temperature.
Claim 2
Dependent Claim
144 words
A process for fabricating a glass member having a varying index of refraction along an optic axis comprising (a) stacking a plurality of intermediate glass plates between a top plate and a bottom plate to form an assembly, said top plate comprising a glass of a first composition having a first selected index of refraction and a first softening temperature and said bottom plate comprising a glass of a second composition having a second selected index of refraction and a second softening temperature, said plurality of intermediate glass plates each comprising a composition intermediate that of said top and bottom plates and stacked to achieve a change in composition varying from said first composition to said second composition; (b) heating said assembly to a fusion temperature to fuse said plates to form a fused assembly; and (c) cooling said fused assembly to room temperature.
Claim 3
Dependent Claim
18 words
The process of claim 1, wherein said first softening temperature and second softening temperature are about the same.
Claim 4
Dependent Claim
15 words
The process of claim 1 wherein said glass plates are restricted from flowing during fusion.
Claim 5
Dependent Claim
34 words
The process of claim 3 wherein said glass plates are stacked in a mold comprising a material which is substantially inert with respect to the composition of said glass plates at said fusion temperature.
Claim 6
Dependent Claim
15 words
The process of claim 1 wherein from five to eight glass plates are vertically stacked.
Claim 7
Dependent Claim
9 words
The process of claim 1, including stacking plates laterally.
Claim 8
Dependent Claim
18 words
The process of claim 6 wherein said lateral plates all have the same composition at a given level.
Claim 9
Dependent Claim
17 words
The process of claim 1 wherein each glass plate ranges from about 1.8 to 3.0 mm thick.
Claim 10
Dependent Claim
20 words
The process of claim 1 wherein said index of refraction varies by at least about 0.085 along said optic axis.
Claim 11
Dependent Claim
22 words
The process of claim 1 wherein said glass member has a thickness of at least about 10 mm along said optic axis.
Claim 12
Dependent Claim
23 words
The process of claim 1 wherein said fusion temperature is approximately twice the maximum softening temperature of any glass plate of said assembly.
Claim 13
Dependent Claim
27 words
The process of claim 11 wherein said heating of said assembly is maintained at said fusion temperature for a time ranging from about 1.5 to 8 hours.
Claim 14
Dependent Claim
30 words
The process of claim 1 wherein said cooling said fused assembly includes annealing said assembly at a temperature below the maximum softening temperature of any glass plate of said assembly.
Claim 15
Dependent Claim
20 words
The process of claim 11 wherein said cooling takes a period of time ranging from about 15 to 60 hours.
Claim 16
Dependent Claim
30 words
A fused glass block having an optic axis and a smoothly varying refractive index providing a change in index of refraction of at least about 0.085 along said optic axis.
Claim 17
Dependent Claim
30 words
A fused glass block having an optic axis and a smoothly varying refractive index providing a change in index of refraction of at least about 0.085 along said optic axis.
Claim 18
Dependent Claim
24 words
The fused glass block of claim 15 wherein said glass member has a thickness of at least about 10 mm along said optic axis.
References Cited (Backward Citations)
US1943521A
Cited
US2216965A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-28 | 1993-11-27 | 1994-05-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-28 | 1997-11-27 | 1998-05-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-28 | 2001-11-27 | 2002-05-29 | $7700.00 | Window Closed / Lapsed |