Pucker and shrink resistant flame retardant fabric formed of corespun yarns
Assignee: SPRINGS CREATIVE PRODUCTS GROUP Inc
•
Filing: 1989-03-15
•
Granted: 1990-05-22
•
Expires: 2009-03-15
Abstract
Abstract A fabric formed of yarns (10) having a core (11) formed of fire-resistant filaments and a sheath (12) formed of staple fibers and a cured, crosslinked composition applied to one surface of the fabric is provided. The composition comprises a first crosslinkable resin having an affinity for the fire-resistant filament core (11) and a second crosslinkable resin having an affinity for the staple fiber sheath (12) and for the first crosslinkable resin. The fabric because of the composition is pucker and shrink resistant, and the tensile strength and flexibility of the yarns and the aesthetic appeal of the fabric are maintained when the fabric is washed repeatedly.
Inventors
- 👤 Pamela J. Jaco
- 👤 Thomas W. Tolbert
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 12:00
CPC Classifications
D; D06; D06M; D06M13/00; D06M13/10; D06M13/184; D02; D02G; D02G3/00; D02G3/22; D02G3/38; D02G3/44; D02G3/443; D03; D03D; D03D15/00; D03D15/50; D03D15/513; D06M15/00; D06M15/19; D06M15/21; D06M15/263; D10; D10B; D10B2331/00; D10B2331/02; D10B2331/021; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24826; Y10T428/29; Y10T428/2913; Y10T428/2929; Y10T428/2933; Y10T428/2936; Y10T442/00; Y10T442/20; Y10T442/2008; Y10T442/2369; Y10T442/2385
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
69 words
A fabric formed of corespun yarns having a core formed of fire-resistant filaments and a sheath formed of staple fibers and a cured, crosslinked coating on said fabric and imparting pucker and shrink resistance to the fabric, said coating comprising a first crosslinkable resin having an affinity for said core filaments and a second crosslinkable resin having an affinity for said sheath fibers and for said first crosslinkable resin.
Claim 2
Dependent Claim
69 words
A fabric formed of corespun yarns having a core formed of fire-resistant filaments and a sheath formed of staple fibers and a cured, crosslinked coating on said fabric and imparting pucker and shrink resistance to the fabric, said coating comprising a first crosslinkable resin having an affinity for said core filaments and a second crosslinkable resin having an affinity for said sheath fibers and for said first crosslinkable resin.
Claim 3
Dependent Claim
53 words
A fabric according to claim 1 wherein said fire-resistant core filaments comprise a fiber selected from the group consisting of glass, metal, silica, ceramic, polyaramids and polybenzimidazole fibers, and said staple fibers comprise a fiber selected from the group consisting of cotton, rayon, wool, nylon, acrylic, modacrylic, polyester, acetate fibers and blends thereof.
Claim 4
Dependent Claim
38 words
A fabric according to claim 1 wherein said crosslinked coating comprises from about 1 to 17 percent by weight of said first crosslinkable resin and from about 1 to 17 percent by weight of said second crosslinkable resin.
Claim 5
Dependent Claim
61 words
A fabric according to claim 1 wherein said first crosslinkable resin comprises an aqueous self-crosslinking copolymer produced by emulsion polymerization of one or more ethylenically unsaturated monomers in the presence of a latent-crosslinking comonomer comprising an N-alkylolamide of an alpha, beta ethylenically unsaturated carboxylic acid having 3 to 10 carbon atoms and said second crosslinkable resin is a methylol derivative resin.
Claim 6
Dependent Claim
28 words
A fabric according to claim 4 wherein said ethylenically unsaturated monomer is selected from the group consisting of alkyl acrylates, alkyl methacrylates, acrylonitrile, acrylamide, styrene and vinyl acetate.
Claim 7
Dependent Claim
26 words
A fabric according to claim 4 wherein said aqueous self-crosslinking copolymer is a butyl acrylate/methyl methacrylate/n-methylol acrylamide copolymer and said methylol derivative is dimethylol dihydroxyethylene urea.
Claim 8
Dependent Claim
109 words
A woven fabric formed of interwoven warp and weft corespun yarns having a fiberglass filament core and a staple cotton fiber sheath and a cured, crosslinked coating on the fabric and imparting pucker and shrink resistance to the fabric, said coating comprising an aqueous self-crosslinking copolymer produced by emulsion polymerization of one or more ethylenically unsaturated monomers in the presence of a latent-crosslinking comonomer comprising an N-alkylolamide of an alpha, beta ethylenically unsaturated carboxylic acid having 3 to 10 carbons atoms having an affinity for said fiberglass filament core and a methylol derivative resin having an affinity for said staple cotton fiber sheath and for said aqueous self-crosslinking copolymer.
Claim 9
Dependent Claim
109 words
A woven fabric formed of interwoven warp and weft corespun yarns having a fiberglass filament core and a staple cotton fiber sheath and a cured, crosslinked coating on the fabric and imparting pucker and shrink resistance to the fabric, said coating comprising an aqueous self-crosslinking copolymer produced by emulsion polymerization of one or more ethylenically unsaturated monomers in the presence of a latent-crosslinking comonomer comprising an N-alkylolamide of an alpha, beta ethylenically unsaturated carboxylic acid having 3 to 10 carbons atoms having an affinity for said fiberglass filament core and a methylol derivative resin having an affinity for said staple cotton fiber sheath and for said aqueous self-crosslinking copolymer.
Claim 10
Dependent Claim
38 words
A fabric according to claim 7 wherein said crosslinked coating comprises from about 1 to 17 percent by weight of said aqueous self-crosslinking copolymer and from about 1 to 17 percent by weight of said methylol derivative resin.
Claim 11
Dependent Claim
28 words
A fabric according to claim 7 wherein said ethylenically unsaturated monomer is selected from the group consisting of alkyl acrylates, alkyl methacrylates, acrylonitrile, acrylamide, styrene and vinyl acetate.
Claim 12
Dependent Claim
25 words
A fabric according to claim 7 wherein said aqueous self-crosslinking copolymer is butyl acrylate/methyl methacrylate/n-methylol acrylamide and said methylol derivative resin is dimethylol dihydroxyethylene urea.
Claim 13
Dependent Claim
107 words
A woven fabric formed of interwoven warp and weft corespun yarns having a fiberglass filament core and a rayon fiber sheath and a cured, crosslinked coating on the fabric and imparting pucker and shrink resistance to the fabric, said coating comprising an aqueous self-crosslinking copolymer produced by emulsion polymerization of one or more ethylenically unsaturated monomers in the presence of a latent-crosslinking comonomer comprising an N-alkylolamide of an alpha, beta ethylenically unsaturated carboxylic acid having 3 to 10 carbon atoms having an affinity for said fiberglass filament core and a methylol derivative resin having an affinity for said rayon fiber sheath and for said aqueous self-crosslinking copolymer.
Claim 14
Dependent Claim
107 words
A woven fabric formed of interwoven warp and weft corespun yarns having a fiberglass filament core and a rayon fiber sheath and a cured, crosslinked coating on the fabric and imparting pucker and shrink resistance to the fabric, said coating comprising an aqueous self-crosslinking copolymer produced by emulsion polymerization of one or more ethylenically unsaturated monomers in the presence of a latent-crosslinking comonomer comprising an N-alkylolamide of an alpha, beta ethylenically unsaturated carboxylic acid having 3 to 10 carbon atoms having an affinity for said fiberglass filament core and a methylol derivative resin having an affinity for said rayon fiber sheath and for said aqueous self-crosslinking copolymer.
Claim 15
Dependent Claim
38 words
A fabric according to claim 11 wherein said crosslinked coating comprises from about 1 to 17 percent by weight of said aqueous self-crosslinking copolymer and from about 1 to 17 percent by weight of said methylol derivative resin.
Claim 16
Dependent Claim
28 words
A fabric according to claim 11 wherein said ethylenically unsaturated monomer is selected from the group consisting of alkyl acrylates, alkyl methacrylates, acrylonitrile, acrylamide, styrene and vinyl acetate.
Claim 17
Dependent Claim
25 words
A fabric according to claim 11 wherein said aqueous self-crosslinking copolymer is butyl acrylate/methyl methacrylate/n-methylol acrylamide and said methylol derivative resin is dimethylol dihydroxyethylene urea.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-21 | 1993-11-20 | 1994-05-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-21 | 1997-11-20 | 1998-05-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-21 | 2001-11-20 | 2002-05-22 | $7700.00 | Window Closed / Lapsed |