Process for reinforced yarn with glass fiber core
Assignee: United States, AGRICULTURE THE, Secretary of, Department of
•
Filing: 1983-08-26
•
Granted: 1985-09-17
•
Expires: 2003-08-26
Abstract
Abstract A unique process for producing torque-free or balanced yarns of staple fibers with glass filament cores is disclosed. Staple fiber roving is fed through a drafting system. Glass filament is fed into the center of the staple fiber just prior to entering the front rolls of the drafting system. Sufficient twist is applied to the fiber around the glass filament using the ring spinning process and two or more of these yarns are ply twisted in the opposite direction of the spinning direction to firmly lock the staple fiber to the glass filament. The twist multiplier range for spinning is between 3.0 to 3.5 and for plying is betwen 3.5 and 4.5. Cotton fiber is the principle fiber used with a glass filament core. The resulting yarn can be tied by knotting onto existing loom beam ends when breaks occur during weaving without shearing of the yarns.
Inventors
- 👤 Clarence O. Graham, Jr.
- 👤 Charles L. Shepard
- 👤 George F. Ruppenicker, Jr.
- 👤 Russell M. H. Kullman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 23:01
CPC Classifications
D; D02; D02G; D02G3/00; D02G3/22; D02G3/36; D02G3/367; D02G3/02; D02G3/16; D02G3/18; D02G3/182; D02G3/185
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
133 words
A process for producing knottable torque-free or balanced yarn comprising: (a) feeding staple fiber roving through a drafting system to form a drafted strand of staple fiber; (b) feeding glass filament yarn to the front rolls of the drafting system and placing the filament into the center of the drafted strand of staple fiber just prior to entering the front rolls; (c) spinning the staple fiber around the glass filament core with a twist multiplier of from about 3.0 to 3.5 to assure proper adhesion of fiber to filament, and form a single yarn; (d) ply twisting two or more of said single yarns in a direction opposite from the spinning direction to firmly lock the staple fiber wrap to the smooth filament glass core and thus produce a torque-free or balanced yarn.
Claim 2
Dependent Claim
133 words
A process for producing knottable torque-free or balanced yarn comprising: (a) feeding staple fiber roving through a drafting system to form a drafted strand of staple fiber; (b) feeding glass filament yarn to the front rolls of the drafting system and placing the filament into the center of the drafted strand of staple fiber just prior to entering the front rolls; (c) spinning the staple fiber around the glass filament core with a twist multiplier of from about 3.0 to 3.5 to assure proper adhesion of fiber to filament, and form a single yarn; (d) ply twisting two or more of said single yarns in a direction opposite from the spinning direction to firmly lock the staple fiber wrap to the smooth filament glass core and thus produce a torque-free or balanced yarn.
Claim 3
Dependent Claim
48 words
The process of claim 1 including a step of guiding the glass filament yarn from a spool or bobbin to the front rolls of the drafting system and placing the filament into the center of the drafted strand of staple fiber just prior to entering the front rolls.
Claim 4
Dependent Claim
11 words
The process of claim 2 wherein the staple fiber is cotton.
Claim 5
Dependent Claim
18 words
The process of claim 3 including an additional step of condensing the staple fibers within the drafting system.
Claim 6
Dependent Claim
29 words
The process of claim 3 wherein the spun yarn has an actual cotton count of 18.9/1 and the yarn diameter is equivalent to 22/1 yarn spun from 100% cotton.
Claim 7
Dependent Claim
37 words
The process of claim 5 wherein the 22/1 spun yarn has a glass filament core ply twisted with 13.6 turns/inch of "Z" twist to produce a nominal 22/2 yarn that contained approximately 36% glass and 64% cotton.
Claim 8
Dependent Claim
14 words
The fiber wrapped filament glass core yarn produced by the process of claim 1.
Claim 9
Dependent Claim
14 words
The fiber wrapped filament glass core yarn produced by the process of claim 2.
Claim 10
Dependent Claim
14 words
The fiber wrapped filament glass core yarn produced by the process of claim 3.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-09-16 | 1989-03-18 | 1989-09-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-09-16 | 1993-03-18 | 1993-09-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-09-16 | 1997-03-18 | 1997-09-17 | $7700.00 | Window Closed / Lapsed |