Resin compositions and their manufacturing method
Assignee: Toray Industries Inc
•
Filing: 1987-09-01
•
Granted: 1990-05-08
•
Expires: 2007-09-01
Abstract
Abstract Resin compositions of (A) 50-95 percent by weight of a polyamide and (B) 5-50 percent by weight of a modified polyolefin containing in side chains 0.005-5 molar percent of functional groups expressed by formulas (I) and/or (II) below and 0.005-5 molar percent of functional groups expressed by formulas (III) and/or (IV) below provide molds having a high impact resistance and are applicable to automobile parts. ##STR1## Where R 1 represents hydrogen or methl and wherein R 2 , R 3 and R 4 represent hydrogen, aliphatic, alicyclic or aromatic residual groups having 1-30 carbon atoms.
Inventors
- 👤 Kazumasa Chiba
- 👤 Kazuhiko Kobayashi
- 👤 Osamu Ueno
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 12:41
CPC Classifications
C; C08; C08L; C08L77/00
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
149 words
A resin composition having improved flowability when discharged from an extruder comprising: (A) 50-95 percent by weight of a polyamide and (B) 5-50 percent by weight of a modified polyolefin containing in the side chain 0.02-4 molar percent based upon the weight of the modified polyolefin of functional groups (C) expressed by formulas selected from the group consisting of one or both of (I) and (II) and 0.04-1 molar percent based upon the weight of the modified polyolefin of functional groups (d) expressed by formulas selected from the group consisting of one or both of (III) and (IV) ##STR3## wherein R 1 represents a hydrogen atom or methyl group; R 2 , R 3 and R 4 represent respectively a hydrogen atom or an aliphatic, alicyclic or aromatic residual group having 1-30 carbon atoms; and M represents a hydrogen atom or a metal ion of a valence of 1-3.
Claim 2
Dependent Claim
149 words
A resin composition having improved flowability when discharged from an extruder comprising: (A) 50-95 percent by weight of a polyamide and (B) 5-50 percent by weight of a modified polyolefin containing in the side chain 0.02-4 molar percent based upon the weight of the modified polyolefin of functional groups (C) expressed by formulas selected from the group consisting of one or both of (I) and (II) and 0.04-1 molar percent based upon the weight of the modified polyolefin of functional groups (d) expressed by formulas selected from the group consisting of one or both of (III) and (IV) ##STR3## wherein R 1 represents a hydrogen atom or methyl group; R 2 , R 3 and R 4 represent respectively a hydrogen atom or an aliphatic, alicyclic or aromatic residual group having 1-30 carbon atoms; and M represents a hydrogen atom or a metal ion of a valence of 1-3.
Claim 3
Dependent Claim
14 words
A resin composition defined in claim 1 wherein the modified polyolefin is partially cross-linked.
Claim 4
Dependent Claim
29 words
A resin composition defined in claim 1 which is comprised of 55-93 percent by weight of the polyamide (A) and 7-45 percent by weight of the modified polyolefin (B).
Claim 5
Dependent Claim
29 words
A resin composition defined in claim 1 which is comprised of 60-90 percent by weight of the polyamide (A) and 10-40 percent by weight of the modified polyolefin (B).
Claim 6
Dependent Claim
39 words
A resin composition defined in claim 1 wherein R 2 in formula (I) is a functional group selected from the group consisting of one or more of the following: alkyl having 1-10 carbon atoms, phenyl, cyclohexyl and benzyl groups.
Claim 7
Dependent Claim
45 words
A resin composition defined in claim 1 wherein R 2 and R 4 in formula (II) are respectively selected from the group consisting of one or more of the following: a hydrogen atom and a functional group selected from alkyl groups having 1-10 carbon atoms.
Claim 8
Dependent Claim
40 words
A resin composition defined in claim 1 wherein the modified polyolefin (B) is selected from the group consisting of polyethylene, polypropylene, polybutene, poly(4-methylpenetene-1), ethylene/propylene copolymer, ethylene/butene-1 copolymer, ethylene/propylene/1,4-hexadiene copolymer, ethylene/propylene/5-ethylidenenorbornene copolymer, ethylene/propylene/5-ethyl-2,5-norbornadiene copolymer and ethylene/propylene/dicyclopentadiene copolymer having said functional groups.
Claim 9
Dependent Claim
33 words
A resin composition defined in claim 1 wherein the polyamide (A) is that chosen from polycaproamide, polyhexamethyleneadipamide, polyhexamethylenesebacamide, polyhexamethylenedodecamide, polyundecanamide, polydodecanamide, polyhexamethyleneisophthalamide, polyhexamethyleneterephthalamide, polytrimethylhexamethyleneterephthalamide, polybis(4-aminocyclohexyl)methanedodecamide, polymetaxylyleneadipamide, polyundecamethyleneterephthalamide, polydodecamethyleneterephthalamide and their copolymers and mixtures.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-07 | 1993-11-06 | 1994-05-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-07 | 1997-11-06 | 1998-05-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-07 | 2001-11-06 | 2002-05-08 | $7700.00 | Window Closed / Lapsed |