Assignee: Kimberly Clark Worldwide Inc
•
Filing: 1988-04-14
•
Granted: 1990-05-08
•
Expires: 2008-04-14
Abstract
Abstract A surface-segregatable, melt-extrudable thermoplastic composition suitable for processing by melt extrusion to form a fiber or film having a differential, increasing concentration of an additive from the center of the fiber or film to the surface thereof, which differential, increasing concentration imparts to the surface of the fiber or film at least one desired characteristic which otherwise would not be present, which composition includes at least one thermoplastic polymer and at least one defined additive. During formation of the fiber or film, the additive rapidly segregates in a controllable manner toward the newly-formed surface of the fiber or film, thereby resulting in a controllable differential concentration of the polymeric material, which concentration increases with increasing distance from the center of the fiber or film to its surface. The weight ratio of the polymer to the additive is in the range of from about 1 to about 1,000. The preferred polymer is a polyolefin such as polyethylene and polypropylene. The thermoplastic composition is useful in the preparation of fibers or films which have at least one surface characteristic which is different from that of the polymer component of the thermoplastic composition. The thermoplastic composition is particularly useful in the formation of nonwoven webs which are used in the construction of such disposable absorbent products as diapers, feminine care products, incontinence products, and the like.
Inventors
- 👤 Ronald S. Nohr
- 👤 J. Gavin MacDonald
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 23:59
CPC Classifications
C; C08; C08L; C08L101/00; A; A61; A61L; A61L15/00; A61L15/16; A61L15/22; A61L15/225; C08J; C08J5/00; C08J5/18; C08K; C08K5/00; C08K5/0008; C08K5/54; C08K5/541; C08K5/5415; C08K5/5419; C08L23/00; C08L23/02; C08L83/00; C08L83/04; D; D01; D01F; D01F1/00; D01F1/02; D01F1/10; D04; D04H; D04H1/00; D04H1/40; D04H1/54; D04H1/56; C08G; C08G77/00; C08G77/04; C08G77/045; C08G77/14; C08G77/18; C08G77/22; C08G77/26
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
215 words
A surface-segregatable, melt-extrudable thermoplastic composition which comprises at least one thermoplastic polyolefin and at least one siloxane-containing additive having at least two moieties, A and B, in which: (A) said additive is compatible with said polyolefin at melt extrusion temperatures but is incompatible at temperatures below melt extrusion temperatures, but each of moiety A and moiety B, if present as separate compounds, would be incompatible with said polyolefin at melt extrusion temperatures and at temperatures below melt extrusion temperatures; (B) moiety B has at least one functional group which is a poly(oxyalkylene) moiety which is end-capped by a C 1 -C 4 alkyl group; (C) the molecular weight of said additive is in the range of from about 400 to about 15,000; and (D) the weight ratio of said polyolefin to said additive is in the range of from about 1 to about 1,000; with the proviso that said additive cannot be a compound having the general formula, ##STR29## in which each R independently is a monovalent organic group selected from the group consisting of alkyl groups; R 1 is a monovalent organic group containing at least one ethyleneoxy group, vicinal epoxy group, or amino group; and a and b, which can be the same or different, each have a value of at least 1.
Claim 2
Dependent Claim
215 words
A surface-segregatable, melt-extrudable thermoplastic composition which comprises at least one thermoplastic polyolefin and at least one siloxane-containing additive having at least two moieties, A and B, in which: (A) said additive is compatible with said polyolefin at melt extrusion temperatures but is incompatible at temperatures below melt extrusion temperatures, but each of moiety A and moiety B, if present as separate compounds, would be incompatible with said polyolefin at melt extrusion temperatures and at temperatures below melt extrusion temperatures; (B) moiety B has at least one functional group which is a poly(oxyalkylene) moiety which is end-capped by a C 1 -C 4 alkyl group; (C) the molecular weight of said additive is in the range of from about 400 to about 15,000; and (D) the weight ratio of said polyolefin to said additive is in the range of from about 1 to about 1,000; with the proviso that said additive cannot be a compound having the general formula, ##STR29## in which each R independently is a monovalent organic group selected from the group consisting of alkyl groups; R 1 is a monovalent organic group containing at least one ethyleneoxy group, vicinal epoxy group, or amino group; and a and b, which can be the same or different, each have a value of at least 1.
Claim 3
Dependent Claim
69 words
The thermoplastic composition of claim 1, in which said moiety A comprises at least one tetrasubstituted disiloxanylene group, optionally associated with one or more groups selected from the group consisting of trisubstituted silyl and trisubstituted siloxy groups, the substituents of all such groups being independently selected from the group consisting of monovalent alkyl, cycloalkyl, aryl, and heterocyclic groups, each of which may be substituted or unsubstituted, and moiety B.
Claim 4
Dependent Claim
23 words
The thermoplastic composition of claim 1, in which the alkylene portion of said poly(oxyalkylene) moiety contains from 2 to about 6 carbon atoms.
Claim 5
Dependent Claim
137 words
A surface-segregatable, melt-extrudable thermoplastic composition which comprises at least one thermoplastic polymer and at least one additive having at least two moieties, A and B, in which: (A) said additive is compatible with said polymer at melt extrusion temperatures but is incompatible at temperatures below melt extrusion temperatures, but each of moiety A and moiety B, if present as separate compounds, would be incompatible with said polymer at melt extrusion temperatures and at temperatures below melt extrusion temperatures; (B) moiety B has at least one functional group which imparts to said additive at least one desired characteristic; (C) the molecular weight of said additive is in the range of from about 400 to about 15,000; and (D) the weight ratio of said polymer to said additive is in the range of from about 1 to about 1,000.
Claim 6
Dependent Claim
137 words
A surface-segregatable, melt-extrudable thermoplastic composition which comprises at least one thermoplastic polymer and at least one additive having at least two moieties, A and B, in which: (A) said additive is compatible with said polymer at melt extrusion temperatures but is incompatible at temperatures below melt extrusion temperatures, but each of moiety A and moiety B, if present as separate compounds, would be incompatible with said polymer at melt extrusion temperatures and at temperatures below melt extrusion temperatures; (B) moiety B has at least one functional group which imparts to said additive at least one desired characteristic; (C) the molecular weight of said additive is in the range of from about 400 to about 15,000; and (D) the weight ratio of said polymer to said additive is in the range of from about 1 to about 1,000.
Claim 7
Dependent Claim
22 words
The thermoplastic composition of claim 4, in which a characteristic of said moiety B is wettability by water or other polar solvents.
Claim 8
Dependent Claim
15 words
The thermoplastic composition of claim 5, in which said moiety B is a poly(oxyalkylene) moiety.
Claim 9
Dependent Claim
23 words
The thermoplastic composition of claim 6, in which the alkylene portion of said poly(oxyalkylene) moiety contains from 2 to about 6 carbon atoms.
Claim 10
Dependent Claim
17 words
The thermoplastic composition of claim 4, in which a characteristic of said moiety B is enhanced hydrophobicity.
Claim 11
Dependent Claim
14 words
The thermoplastic composition of claim 8, in which said moiety B is a perfluorohydrocarbon.
Claim 12
Dependent Claim
15 words
The thermoplastic composition of claim 9, in which said moiety B is a perfluoroalkyl group.
Claim 13
Dependent Claim
18 words
The thermoplastic composition of claim 4, in which a characteristic of said moiety B is a buffering capacity.
Claim 14
Dependent Claim
15 words
The thermoplastic composition of claim 11, in which said buffering capacity is against hydrogen ions.
Claim 15
Dependent Claim
14 words
The thermoplastic composition of claim 12, in which said moiety B is an amine.
Claim 16
Dependent Claim
15 words
The thermoplastic composition of claim 13, in which said moiety B is an aliphatic amine.
Claim 17
Dependent Claim
18 words
The thermoplastic composition of claim 4, in which a characteristic of said moiety B is ultraviolet light absorption.
Claim 18
Dependent Claim
15 words
The thermoplastic composition of claim 15, in which said moiety B is a 2-(substituted-phenyl)benzotriazolyl group.
Claim 19
Dependent Claim
17 words
The thermoplastic composition of claim 4, in which a characteristic of said moiety B is light stabilization.
Claim 20
Dependent Claim
15 words
The thermoplastic composition of claim 17, in which said moiety B is a tetraalkylpiperidyl group.
Claim 21
Dependent Claim
211 words
A surface-segregatable, melt-extrudable thermoplastic composition which comprises at least one thermoplastic polymer and at least one siloxane-containing additive having at least two moieties, A and B, in which: (A) said additive is compatible with said polymer at melt extrusion temperatures but is incompatible at temperatures below melt extrusion temperatures, but each of moiety A and moiety B, if present as separate compounds, would be incompatible with said polymer at melt extrusion temperatures and at temperatures below melt extrusion temperatures; (B) moiety B has at least one functional group selected from the group consisting of benzotriazolyl, polyalkylpiperidyl, perfluorohydrocarbon, and amino groups; (C) the molecular weight of said additive is in the range of from about 400 to about 15,000; and (D) the weight ratio of said polymer to said additive is in the range of from about 1 to about 1,000; with the proviso that said additive cannot be a compound having the general formula, ##STR30## in which each R independently is a monovalent organic group selected from the group consisting of alkyl groups; R 1 is a monovalent organic group containing at least one ethyleneoxy group, vicinal epoxy group, or amino group; and a and b, which can be the same or different, each have a value of at least 1.
Claim 22
Dependent Claim
211 words
A surface-segregatable, melt-extrudable thermoplastic composition which comprises at least one thermoplastic polymer and at least one siloxane-containing additive having at least two moieties, A and B, in which: (A) said additive is compatible with said polymer at melt extrusion temperatures but is incompatible at temperatures below melt extrusion temperatures, but each of moiety A and moiety B, if present as separate compounds, would be incompatible with said polymer at melt extrusion temperatures and at temperatures below melt extrusion temperatures; (B) moiety B has at least one functional group selected from the group consisting of benzotriazolyl, polyalkylpiperidyl, perfluorohydrocarbon, and amino groups; (C) the molecular weight of said additive is in the range of from about 400 to about 15,000; and (D) the weight ratio of said polymer to said additive is in the range of from about 1 to about 1,000; with the proviso that said additive cannot be a compound having the general formula, ##STR30## in which each R independently is a monovalent organic group selected from the group consisting of alkyl groups; R 1 is a monovalent organic group containing at least one ethyleneoxy group, vicinal epoxy group, or amino group; and a and b, which can be the same or different, each have a value of at least 1.
Claim 23
Dependent Claim
69 words
The thermoplastic composition of claim 19, in which said moiety A comprises at least one tetrasubstituted disiloxanylene group, optionally associated with one or more groups selected from the group consisting of trisubstituted silyl and trisubstituted siloxy groups, the substituents of all such groups being independently selected from the group consisting of monovalent alkyl, cycloalkyl, aryl, and heterocyclic groups, each of which may be substituted or unsubstituted, and moiety B.
Claim 24
Dependent Claim
17 words
The thermoplastic composition of claim 19, in which a characteristic of said moiety B is enhanced hydrophobicity.
Claim 25
Dependent Claim
14 words
The thermoplastic composition of claim 21, in which said moiety B is a perfluorohydrocarbon.
Claim 26
Dependent Claim
15 words
The thermoplastic composition of claim 22, in which said moiety B is a perfluoroalkyl group.
Claim 27
Dependent Claim
18 words
The thermoplastic composition of claim 19, in which a characteristic of said moiety B is a buffering capacity.
Claim 28
Dependent Claim
15 words
The thermoplastic composition of claim 24, in which said buffering capacity is against hydrogen ions.
Claim 29
Dependent Claim
14 words
The thermoplastic composition of claim 25, in which said moiety B is an amine.
Claim 30
Dependent Claim
15 words
The thermoplastic composition of claim 26, in which said moiety B is an aliphatic amine.
Claim 31
Dependent Claim
18 words
The thermoplastic composition of claim 19, in which a characteristic of said moiety B is ultraviolet light absorption.
Claim 32
Dependent Claim
15 words
The thermoplastic composition of claim 28, in which said moiety B is a 2-(substituted-phenyl)benzotriazolyl group.
Claim 33
Dependent Claim
17 words
The thermoplastic composition of claim 19, in which a characteristic of said moiety B is light stabilization.
Claim 34
Dependent Claim
15 words
The thermoplastic composition of claim 30, in which said moiety B is a tetraalkylpiperidyl group.
References Cited (Backward Citations)
US32514A
Cited
US3360421A
Cited
US3629308A
Cited
US3620821A
Cited
US3766115A
Cited
US3929509A
Cited
US3867188A
Cited
CA1049682A
Cited
US3973068A
Cited
US4070218A
Cited
US4150013A
Cited
US4480009A
Cited
US4499149A
Cited
US4426203A
Cited
US4444563A
Cited
US4563190A
Cited
USRE32514E
Cited
US4698388A
Cited
US4500659A
Cited
US4446090A
Cited
US4578414A
Cited
US4672005A
Cited
US4535113A
Cited
US4645691A
Cited
US4585830A
Cited
US4745142A
Cited
US4659777A
Cited
US4689362A
Cited
EP0713492A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-07 | 1993-11-06 | 1994-05-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-07 | 1997-11-06 | 1998-05-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-07 | 2001-11-06 | 2002-05-08 | $7700.00 | Window Closed / Lapsed |