Low temperature sealing adhesive composition
Assignee: Building Materials Corp of America
•
Filing: 1988-12-30
•
Granted: 1990-05-08
•
Expires: 2008-12-30
Abstract
Abstract An adhesive composition for roofing such as shingles is disclosed which is composed of a hard asphaltic bitumen fraction having a penetration number at 77° F. of from 0 to 30 dmm and a softening point of from about 150° to 220° F. and an elastomeric composition composed of a thermoplastic elastomer and a plasticizer wherein the overall adhesive composition has a penetration number of from 30 to 100 dmm at 130° F. and a softening point of 140° to 230° F. The inventive composition is self-sealing and exhibits excellent squash resistance, low temperature properties and resistance to blowoff. The composition can be used with shingles as well as other types of roofing coverings.
Inventors
- 👤 Adem Chich
- 👤 Steven S. Lalwani
- 👤 Steven C. Bettoli
- 👤 Louis L. Grube
- 👤 Alfredo A. Bondoc
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 20:48
CPC Classifications
C; C09; C09J; C09J195/00
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
165 words
An adhesive composition comprising: (a) a hard asphaltic bitumen fraction having a penetration number at 77° F. of from 0 to 30 dmm and a softening point of from about 150° to 220° F., and (b) an elastomeric composition comprising a thermoplastic elastomer and a plasticizer, said plasticizer having a flash point equal to or greater than 250° F. and a boiling point equal to or greater than 250° F. and being present in an amount from about 1 to 80 percent by weight of the elastomeric composition; wherein the amount of plasticizer in the adhesive composition is such that the mixture has a penetration number of from 30 to 100 dmm at 130° F. and a softening point of 140° to 230° F. and wherein the amount of bitumen fraction is about 99 to 80 percent by weight and the amount of elastomeric composition is from about 1 to 20 percent by weight, based on the total amount of the bitumen and elastomeric composition.
Claim 2
Dependent Claim
165 words
An adhesive composition comprising: (a) a hard asphaltic bitumen fraction having a penetration number at 77° F. of from 0 to 30 dmm and a softening point of from about 150° to 220° F., and (b) an elastomeric composition comprising a thermoplastic elastomer and a plasticizer, said plasticizer having a flash point equal to or greater than 250° F. and a boiling point equal to or greater than 250° F. and being present in an amount from about 1 to 80 percent by weight of the elastomeric composition; wherein the amount of plasticizer in the adhesive composition is such that the mixture has a penetration number of from 30 to 100 dmm at 130° F. and a softening point of 140° to 230° F. and wherein the amount of bitumen fraction is about 99 to 80 percent by weight and the amount of elastomeric composition is from about 1 to 20 percent by weight, based on the total amount of the bitumen and elastomeric composition.
Claim 3
Dependent Claim
24 words
The adhesive composition of claim 1 wherein the asphaltic fraction is propane cut bitumen, a petroleum bottoms asphalt modified by oxidation and mixtures thereof.
Claim 4
Dependent Claim
22 words
The adhesive composition of claim 1 wherein the thermoplastic elastomer is selected from the group consisting of styrene-butadiene-styrene, styrene-ethylene-butylene-styrene, and ethylene propylene.
Claim 5
Dependent Claim
26 words
The adhesive composition of claim 1 wherein the plasticizer is selected from the group consisting of petroleum derived oils, phthalate esters, phthalate esters derivatives, and mellitates.
Claim 6
Dependent Claim
28 words
The adhesive composition of claim 1 wherein the amount of plasticizer is from about 10 to 70 percent by weight based on the weight of the elastomeric composition.
Claim 7
Dependent Claim
30 words
The adhesive composition of claim 1 wherein the amount of elastomeric composition is from about 2 to 14 percent by weight based on the total weight of the adhesive composition.
Claim 8
Dependent Claim
20 words
The adhesive composition of claim 1 wherein the amount of bitumen fraction is from about 98 to 86% by weight.
Claim 9
Dependent Claim
19 words
The adhesive composition of claim 1 wherein additional plasticizer other than that contained in the elastomeric composition is present.
Claim 10
Dependent Claim
29 words
The adhesive composition of claim 8 wherein the amount of additional plasticizer is from about 1.25 to 20% by weight based on the total weight of the adhesive composition.
Claim 11
Dependent Claim
11 words
The adhesive composition of claim 1 which further comprises a filler.
Claim 12
Dependent Claim
26 words
The adhesive composition of claim 10 wherein the amount of filler is from about 5 to 50% based on the total weight of the adhesive composition.
Claim 13
Dependent Claim
21 words
The adhesive composition of claim 10 wherein the softening point of the adhesive composition is from about 160° to 230° F.
Claim 14
Dependent Claim
30 words
A method for preparing the adhesive composition of claim 1 comprising heating the asphaltic bitumen fraction to a molten state and admixing the elastomeric composition into the molten bitumen fraction.
Claim 15
Dependent Claim
21 words
The method of claim 13 wherein the bitumen fraction is heated to a temperature of from about 300° to 380° F.
Claim 16
Dependent Claim
21 words
The method of claim 13 wherein prior to adding the elastomeric composition, additional plasticizer is added to the molten bitumen fraction.
Claim 17
Dependent Claim
21 words
The method of claim 13 wherein the thermoplastic elastomer is selected from the group consisting of styrene-butadiene-styrene, styrene-ethylene-butylene-styrene, and ethylene propylene.
Claim 18
Dependent Claim
25 words
The method of claim 16 wherein the plasticizer is selected from the group consisting of petroleum derived oils, phthalate esters, phthalate esters derivatives, and mellitates.
Claim 19
Dependent Claim
31 words
The method of claim 15 wherein the amount of additional plasticizer added is sufficient to increase the penetration number of the asphalt fraction to 40 dmm or above at 130° F.
Claim 20
Dependent Claim
68 words
An adhesive composition comprising: (a) about 60 weight percent of a bituminous fraction selected from the group consisting of propane extracted asphalt resin or oxidized bitumen; (b) about 30 weight percent of limestone; (c) about 8 weight percent of a thermoplastic rubber of styrene-butadiene block copolymer containing from about 20 to 55 percent by weight plasticizer; and (d) about 2 percent by weight of a phthalate ester plasticizer.
Claim 21
Dependent Claim
68 words
An adhesive composition comprising: (a) about 60 weight percent of a bituminous fraction selected from the group consisting of propane extracted asphalt resin or oxidized bitumen; (b) about 30 weight percent of limestone; (c) about 8 weight percent of a thermoplastic rubber of styrene-butadiene block copolymer containing from about 20 to 55 percent by weight plasticizer; and (d) about 2 percent by weight of a phthalate ester plasticizer.
References Cited (Backward Citations)
US4385142A
Cited
US4824880A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-07 | 1993-11-06 | 1994-05-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-07 | 1997-11-06 | 1998-05-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-07 | 2001-11-06 | 2002-05-08 | $7700.00 | Window Closed / Lapsed |