Catalyst for the hydroisomerization and hydrocracking of waxes to produce liquid hydrocarbon fuels and process for preparing the catalyst

Claim 2

A particulate fluorided Group VIII metal-on-alumina catalyst having: (a) a Group VIII metal concentration ranging from about 0.1 to about 2 weight percent; (b) a bulk fluoride concentration ranging from about 2 to about 10 weight percent, wherein the fluoride concentration is less than about 3.0 weight percent at the outer surface layer to a depth less than one one hundredth of an inch, provided the surface fluoride concentration is less than the bulk fluoride concentration; (c) an aluminum fluoride hydroxide hydrate level greater than 60 where an aluminum fluoride hydroxide hydrate level of 100 corresponds to the X-ray diffraction peak height at 5.66Å for a Reference Standard; and (d) a N/Al ratio less than about 0.005.

Claim 3

The catalyst composition of claim 1 wherein said Group VIII metal is platinum.

Claim 4

The catalyst of claim 2 wherein the aluminum chloride hydroxide hydrate level is greater than 80.

Claim 5

The catalyst of claim 3 wherein the fluoride concentration at the surface of the catalyst is less than about 1.0 weight percent.

Claim 6

The catalyst of claim 4 wherein the N/Al ratio of the catalyst is less than 0.002.

Claim 7

The catalyst of claim 5 wherein the fluoride concentration ranges from about 5 to about 8 percent, based on the total weight of the catalyst composition.

Claim 8

The catalyst of claim 2 wherein the aluminum fluoride hydroxide hydrate level is at least about 100.

Claim 9

The catalyst of claim 6 wherein the aluminum fluoride hydroxide level is at least about 100.

Claim 10

The catalyst of claim 8 wherein the fluoride concentration at the surface of the catalyst is less than about 0.5 weight percent.

Claim 11

A process for the preparation of a particulate fluorided platinum alumina catalyst composition from a calcined platinum-on-alumina composition containing from about 0.1 to about 2 weight percent platinum, based on the total weight of the catalyst composition, which comprises: (a) contacting the calcined platinum-on-alumina composition with an aqueous HF solution containing from about 10 percent to about 20 percent hydrogen fluoride and having a pH below 3.5 to distribute fluoride within the interior of the alumina component and to produce a fluorided platinum alumina catalyst composition containing from about 2 to about 10 percent fluoride, based on the total weight on the catalyst composition, wherein a distinct inner ring of fluoride is formed; (b) drying the fluorided platinum alumina catalyst composition at a temperature not in excess of 650° F., and (c) recovering a catalyst composition having an aluminum fluoride hydroxide hydrate level greater than 60, a fluoride concentration less than about 3.0 weight percent at the outer surface to a depth less than one one hundredth of an inch, and a N/Al ratio less than about 0.005.

Claim 12

A process for the preparation of a particulate fluorided platinum alumina catalyst composition from a calcined platinum-on-alumina composition containing from about 0.1 to about 2 weight percent platinum, based on the total weight of the catalyst composition, which comprises: (a) contacting the calcined platinum-on-alumina composition with an aqueous HF solution containing from about 10 percent to about 20 percent hydrogen fluoride and having a pH below 3.5 to distribute fluoride within the interior of the alumina component and to produce a fluorided platinum alumina catalyst composition containing from about 2 to about 10 percent fluoride, based on the total weight on the catalyst composition, wherein a distinct inner ring of fluoride is formed; (b) drying the fluorided platinum alumina catalyst composition at a temperature not in excess of 650° F., and (c) recovering a catalyst composition having an aluminum fluoride hydroxide hydrate level greater than 60, a fluoride concentration less than about 3.0 weight percent at the outer surface to a depth less than one one hundredth of an inch, and a N/Al ratio less than about 0.005.

Claim 13

The process of claim 10 wherein the fluorided platinum alumina catalyst composition is dried at a temperature not exceeding about 500° F.

Claim 14

The process of claim 11 wherein the recovered catalyst has an aluminum fluoride hydroxide hydrate level greater than 80.

Claim 15

The process of claim 12 wherein the fluorided platinum alumina catalyst composition is dried at a temperature not exceeding about 300° F.

Claim 16

The process of claim 13 wherein the recovered catalyst has an aluminum fluoride hydroxide hydrate level of at least about 100.