Aluminum nitride powder and a process for the preparation thereof
Assignee: Hoechst AG
•
Filing: 1989-06-09
•
Granted: 1990-05-08
•
Expires: 2009-06-09
Abstract
Abstract An aluminum nitride powder has a crystallite size of 40 to 150 nm, measured by powder diffractometry and evaluated by the method of Scherrer, a primary particle size of 0.1 to 0.5 μm, a specific surface according to BET of 5 to 50 m 2 /g and a degree of whiteness of more than 91%, measured using light of a 400 to 700 nm wavelength against barium sulfate analytical reagent as standard of whitness. To prepare this aluminum nitride powder, metallic aluminum and monoamminealuminum chloride [AlCl 3 (NH 3 )] are first molten together in an inert gas atmosphere at temperatures above 125° C. and allowed to react with one another with evolution of hydrogen. 8 to 20 g of ammonia are then introduced per hour per mol of monoamminealuminum chloride into the aluminum-containing monoamminealuminum chloride melt at temperatures between 250° and 400° C., aluminum nitride being precipitated as a solid until the conversion of the aluminum is complete. The temperature of the melt is finally raised to more than 400° C.
Inventors
- 👤 Dieter Peters
- 👤 Gero Heymer
- 👤 Christian May
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:43
CPC Classifications
C; C01; C01B; C01B21/00; C01B21/06; C01B21/072; C01P; C01P2002/00; C01P2002/60; C01P2004/00; C01P2004/60; C01P2004/62; C01P2006/00; C01P2006/12; C01P2006/60
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
101 words
A process for the preparation of aluminum nitride powder, which comprises melting metallic aluminum and monoamminealuminum chloride [AlCL 3 (NH 3 )] together in an inert gas atmosphere at temperatures above 125° C. and allowing these to react with one another with evolution of hydrogen; 8 to 20 g of ammonia are introduced per hour per mol of monoamminealuminum chloride into the aluminum-containing monoamminealuminum chloride melt at temperatures between 250° and 400° C., aluminum nitride being precipitated as a solid until the conversion of the aluminum is complete, the temperature of the melt being finally raised to more then 400° C.
Claim 2
Dependent Claim
101 words
A process for the preparation of aluminum nitride powder, which comprises melting metallic aluminum and monoamminealuminum chloride [AlCL 3 (NH 3 )] together in an inert gas atmosphere at temperatures above 125° C. and allowing these to react with one another with evolution of hydrogen; 8 to 20 g of ammonia are introduced per hour per mol of monoamminealuminum chloride into the aluminum-containing monoamminealuminum chloride melt at temperatures between 250° and 400° C., aluminum nitride being precipitated as a solid until the conversion of the aluminum is complete, the temperature of the melt being finally raised to more then 400° C.
Claim 3
Dependent Claim
80 words
The process as claimed in claim 1, wherein the amount of metallic aluminum added to the monoamminealuminum chloride melt is such that the molar ratio of aluminum to monoamminealuminum chloride is 0.5 to 1.2, and in that passage of ammonia into the melt containing solid metallic aluminum is maintained until all of the metallic aluminum added to the melt is taken up by the melt with simultaneous precipitation of aluminum nitride and has reacted with the ammonia forming aluminum nitride.
Claim 4
Dependent Claim
34 words
The process as claimed in claim 2, wherein the amount of metallic aluminum added to the monoamminealuminum chloride melt is such that the molar ratio of aluminum to monoamminealuminum chloride is 0.9 to 1.1.
Claim 5
Dependent Claim
48 words
The process as claimed in claim 2, wherein 30 to 70 mol % of the monoamminealuminum chloride in the reaction system is replaced by aluminum chloride or ammonium chloride or mixtures thereof while maintaining a molar ratio of total aluminum to total monoamminealuminum chloride of (0.5 to 1.2):1.
Claim 6
Dependent Claim
58 words
The process as claimed in claim 1, wherein only so much ammonia is added per unit of time that the ammonia concentration in the evolving hydrogen is less than 0.3% and the excess of ammonia in the melt after all of the aluminum has reacted is not more than 0.5 mol of ammonia per mol of monoamminealuminum chloride.
Claim 7
Dependent Claim
33 words
The process as claimed in claim 5, wherein the excess ammonia from the melt after all of the aluminum has reacted is less than 0.2 mol of ammonia per mol of monoamminealuminum chloride.
Claim 8
Dependent Claim
50 words
The process as claimed in claim 1, wherein so much ammonia is introduced into the monoamminealuminum chloride melt after all of the aluminum has reacted that 1 to 3 mol of ammonia are taken up per mol of the monoamminealuminum chloride used, before the temperature is raised above 400° C.
Claim 9
Dependent Claim
35 words
The process as claimed in claim 7, wherein so much ammonia is introduced into the monoamminealuminum chloride melt that 1.5 to 2.5 mol of ammonia are taken up per mol of the monoamminealuminum chloride used.
Claim 10
Dependent Claim
20 words
The process as claimed in claim 1, wherein the aluminum is used in the form of rods, blocks or shot.
Claim 11
Dependent Claim
28 words
The process as claimed in claim 1, wherein ammonia is introduced into the aluminum-containing monoamminealuminum chloride melt at temperatures between 280° and 360° C., ammonium nitride being precipitated.
Claim 12
Dependent Claim
29 words
The process as claimed in claim 1, wherein 12 to 15 g of ammonia are introduced per hour per mol of monoamminealuminum chloride into the aluminum-containing monoamminealuminum chloride melt.
Claim 13
Dependent Claim
22 words
The process as claimed in claim 1, wherein the temperature is raised to 420°-600° C. after all of the aluminum has reacted.
Claim 14
Dependent Claim
21 words
The process as claimed in claim 1, wherein the precipitated aluminum nitride is separated from the monoamminealuminum chloride melt by filtration.
Claim 15
Dependent Claim
21 words
The process as claimed in claim 13, wherein the separated aluminum nitride is annealed at temperatures between 400° to 1500° C.
Claim 16
Dependent Claim
23 words
The process as claimed in claim 14, wherein the annealing is carried out in an inert gas or ammonia atmosphere or mixtures thereof.
Claim 17
Dependent Claim
20 words
The process as claimed in claim 1, wherein the molten monoamminealuminum chloride is distilled off from the precipitated aluminum nitride.
Claim 18
Dependent Claim
39 words
The process as claimed in claim 16, wherein the removal by distillation of the monoamminealuminum chloride is carried out in vacuo or in an inert gas atmosphere with the formation of aluminum nitride agglomerates having d 50 >10 μm.
Claim 19
Dependent Claim
35 words
The process as claimed in claim 16, wherein the removal by distillation of the monoamminealuminum chloride is carried out in an ammonia atmosphere with the formation of aluminum nitride agglomerates having d 50 <10 μm.
Claim 20
Dependent Claim
17 words
The process as claimed in claim 18, wherein aluminum nitride agglomerates form having d 50 <5 μm.
Claim 21
Dependent Claim
21 words
The process as claimed in claim 16, wherein the separated aluminum nitride is annealed at temperatures between 400° and 1500° C.
Claim 22
Dependent Claim
23 words
The process as claimed in claim 20, wherein the annealing is carried out in an inert gas or ammonia atmosphere or mixtures thereof.
References Cited (Backward Citations)
JPS54126697A
Cited
US4610857A
Cited
JPS616104A
Cited
US4612045A
Cited
JPS6191008A
Cited
US4680278A
Cited
JPS6355108A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-07 | 1993-11-06 | 1994-05-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-07 | 1997-11-06 | 1998-05-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-07 | 2001-11-06 | 2002-05-08 | $7700.00 | Window Closed / Lapsed |