Method of producing powder-metallurgical objects, specifically elongate objects such as rods, sections, tubes or the like
Assignee: Individual
•
Filing: 1989-02-06
•
Granted: 1990-05-08
•
Expires: 2009-02-06
Abstract
Abstract Method of producing powder-metallurgical objects, specifically elongate objects such as rods, sections, tubes or the like, wherein a powder of metal and/or metal alloys of great hardness, particularly tool steel or high-speed steel powder, is charged into a thin-walled capsule, said capsule is then sealed so as to be airtight, is heated, and subjected to isostatic compression to produce a blank which will then undergo hot-working, specifically extrusion, for the production of the finished product. In a first alternative, the airtight and sealed capsule is initially heated to a temperature higher than 1,000° C. Following through-heating of the capsule, the latter is maintained at an elevated temperature for a prolonged period. Then the capsule is slowly cooled and subjected to cold isostatic compression prior to final shaping. In a second alternative, the capsule is sealed so as to be airtight, and then subjected to an initial cold isostatic compression. Then the pressed blank is heated to a temperature higher than 1,000° C. Following through-heating of the pressed blank, the latter is maintained at an elevated temperature for a prolonged period of time, whereupon it is subjected to hot-working, specifically extrusion, either immediately or after a preceding cooling step.
Inventors
- 👤 Christer Aslund
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 22:21
CPC Classifications
B; B22; B22F; B22F5/00; B22F3/00; B22F3/20; B22F3/12; B22F3/1208
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
173 words
Method of producing powder-metallurgical objects, specifically elongate objects such as rods, sections, tubes or the like, wherein a powder of metal and/or metal alloys of great hardness, such as a tool or high-speed steel powder, is charged into a thin-walled capsule, said capsule is then sealed so as to be airtight to produce a blank which is to be extruded or otherwise hot-worked to form the finished product, comprising the steps following the airtight sealing of the capsule: (a) heating the airtight sealed blank to an elevated temperature higher than 1,000° C. until the capsule and powder is at the elevated temperature in the range from 1,100° C. to 1,200° C.; (b) maintaining the capsule at said elevated temperature for a defined length of time which is longer than said heating interval to heat the capsule and powder; (c) slowly cooling the capsule, and (d) after said cooling and prior to subjecting the capsule to hot-working, cold isostatic compressing said capsule to achieve a powder density higher than 75% of the theoretical density.
Claim 2
Dependent Claim
173 words
Method of producing powder-metallurgical objects, specifically elongate objects such as rods, sections, tubes or the like, wherein a powder of metal and/or metal alloys of great hardness, such as a tool or high-speed steel powder, is charged into a thin-walled capsule, said capsule is then sealed so as to be airtight to produce a blank which is to be extruded or otherwise hot-worked to form the finished product, comprising the steps following the airtight sealing of the capsule: (a) heating the airtight sealed blank to an elevated temperature higher than 1,000° C. until the capsule and powder is at the elevated temperature in the range from 1,100° C. to 1,200° C.; (b) maintaining the capsule at said elevated temperature for a defined length of time which is longer than said heating interval to heat the capsule and powder; (c) slowly cooling the capsule, and (d) after said cooling and prior to subjecting the capsule to hot-working, cold isostatic compressing said capsule to achieve a powder density higher than 75% of the theoretical density.
Claim 3
Dependent Claim
17 words
The method of claim 1 wherein said powder density is in the range of 78% to 80%.
Claim 4
Dependent Claim
43 words
The method according to claim 1 wherein said period of slowly cooking the capsule is substantially longer than the heating time and maintaining time, and said cooling time generally is in the range double to fourfold of the sum of the two times.
Claim 5
Dependent Claim
37 words
The method according to claim 1 wherein said capsule is maintained at said elevated temperature for a range of 1 to 2 hours, and said cooling time is generally in the range of 3 to 5 hours.
Claim 6
Dependent Claim
51 words
The method of claim 1 wherein said capsule is located within a furnace during said heating and maintaining of said elevated temperature, turning said furnace off after said maintaining period, and holding said capsule in said furnace for a sufficient period to cool the capsule to ambient temperature in the furnace.
Claim 7
Dependent Claim
22 words
The method of claim 1, characterized in that the cold-isostatic compression takes place at a pressure of about 4,500 to 5,500 bar.
Claim 8
Dependent Claim
22 words
The method of claim 1 wherein said powder includes a carbon percentage in the range of at least to 0.5% by weight.
Claim 9
Dependent Claim
18 words
The method of claim 7 wherein said carbon is in the range of 1.1% to 2.5% by weight.
Claim 10
Dependent Claim
29 words
The method of claim 1 wherein said powder has a mean particle size which corresponds generally to at least 125μ and includes a maximum particle size not exceeding 800μ.
Claim 11
Dependent Claim
20 words
The method of claim 1 wherein said charged capsule has a length/diameter ratio corresponding to the approximate range of 4-5:1.
Claim 12
Independent Claim
158 words
A method of producing powder-metallurgical objects, including elongate objects such as rods, sections, tubes or the like, wherein a powder of metal and/or metal alloys of great hardness such as tool steel or high-speed steel powder is charged into a thin-walled capsule, the capsule is then sealed so as to be airtight to produce a blank which will subsequentially be hot-worked such as extruded to form the finished product, comprising the processing steps applied to the airtight capsule of: (a) subjecting the sealed blank to cold isostatic compression and establishing a powder density in the range of substantially 70 to 75% of the theoretical density; (b) heating the compressed blank for a time period to heat the blank to a temperature higher than 1,000° C.; (c) maintaining said heated pressed blank at a temperature greater than 1,000° C. for a defined period longer than said time period, and (d) subsequently hot working the pressed blank immediately without cooling.
Claim 13
Independent Claim
158 words
A method of producing powder-metallurgical objects, including elongate objects such as rods, sections, tubes or the like, wherein a powder of metal and/or metal alloys of great hardness such as tool steel or high-speed steel powder is charged into a thin-walled capsule, the capsule is then sealed so as to be airtight to produce a blank which will subsequentially be hot-worked such as extruded to form the finished product, comprising the processing steps applied to the airtight capsule of: (a) subjecting the sealed blank to cold isostatic compression and establishing a powder density in the range of substantially 70 to 75% of the theoretical density; (b) heating the compressed blank for a time period to heat the blank to a temperature higher than 1,000° C.; (c) maintaining said heated pressed blank at a temperature greater than 1,000° C. for a defined period longer than said time period, and (d) subsequently hot working the pressed blank immediately without cooling.
Claim 14
Dependent Claim
19 words
The method of claim 11 wherein said blank is heated to a range of 1,100° C. to 1,200° C.
Claim 15
Dependent Claim
21 words
The method of claim 11 wherein said cold-isostatic compression includes a pressure in the range from approximately 4,500 to 5,500 bar.
Claim 16
Dependent Claim
32 words
The method of claim 11 including said period of maintaining the through-heated pressed blank at the elevated temperature equal to at least in the range of 1 hour to roughly 4 hours.
Claim 17
Dependent Claim
24 words
The method of claim 11 wherein said powder has a carbon constant of at least 0.5% by weight and less than 2.5% by weight.
Claim 18
Dependent Claim
25 words
The method of claim 11 wherein said powder has a mean particle size of about 125μ and includes a maximum particle size not exceeding 800μ.
Claim 19
Dependent Claim
20 words
The method of claim 11 wherein said capsule has length/diameter ratio corresponds approximately to the range of 4 to 5:1.
References Cited (Backward Citations)
US4050143A
Cited
US4401723A
Cited
US4460541A
Cited
US4427626A
Cited
US4388054A
Cited
US4710345A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-05-07 | 1993-11-06 | 1994-05-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-05-07 | 1997-11-06 | 1998-05-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-05-07 | 2001-11-06 | 2002-05-08 | $7700.00 | Window Closed / Lapsed |