Flame-retardant fillers in silane-grafted ethylene polymer process

Claim 2

A process for making a halogen-free fire-retardant crosslinked extruded product comprising first forming a halogen-free composition whose essential ingredients are: at least one filler; a compatible ethylene polymer base in which the filler is dispersed; a hydrolysable unsaturated silane; a free-radical grafting initiator; and a silanol condensation catalyst; said filler being a flame-retardant filler of the class that evolve substantial amounts of bound water on heating at temperatures above a value T d which value lies in the range 120°-250° C.; the ratio of filler to polymer being in the range of 3:1 to 1:2 by weight; and said initiator having a half-life of less than 10 minutes at a temperature 25° C. below the T d of said filler as determined by Differential Thermal Analysis using chlorobenzene as a solvent; second, and only after said ingredients have been mixed together, raising the temperature to a grafting temperature below said T d but at which said initiator decomposes to generate free-radicals that effect grafting of said silanes to said polymer; third extruding the mixture containing the grafted polymer from an extrusion die to form a shaped product; and fourth exposing said shaped product to water until it is crosslinked by hydrolytic condensation reactions of the grafted silane.

Claim 3

A process a claimed in claim 1 in which said grafting temperature is at least 25° C. below said T d value.

Claim 4

A process as claimed in claim 1 characterized by the use in combination of magnesium hydroxide as said flame-retardant filler and tertiary butyl per 2-ethyl hexanoate as said initiator.

Claim 5

A process as claimed in claim 1 characterized by the use in combination of a filler selected from the group consisting of gypsum, alumina trihydrate and magnesium hydroxide and a grafting initiator selected from the group consisting of Tertiary butyl per pivalate Tertiary amyl per pivalate Di (3,5,5 trimethyl hexanoyl) peroxide Bis (2 methyl benzoyl) peroxide Di normal octanoyl peroxide Di-decanoyl peroxide and Dilauroyl peroxide.

Claim 6

A process as claimed in claim 1 characterized by the use in combination of a filler selected from the group consisting of alumina trihydrate and magnesium hydroxide and a grafting initiator selected from the group consisting of Tertiary butyl per 2-ethyl hexanoate (TBPEH) Tertiary butyl per isobutyrate Tertiary butyl peroxy diethyl acetate Dibenzoyl peroxide

Claim 7

1 Di-tertiary butyl peroxy-3,3,5-trimethyl cyclohexane Tertiary butyl peroxide 3,5,5 trimethyl hexanoate Tertiary butyl peroxy isopropyl carbonate Tertiary butyl peracetate Tertiary butyl perbenzoate 1,1 Bis (tertiary butyl peroxy) cyclohexane Normal butyl 4,4 bis (tertiary butyl peroxy) valerate and 2,2 Bis (tertiary butyl peroxy) butane.

Claim 8

1 Di-tertiary butyl peroxy-3,3,5-trimethyl cyclohexane Tertiary butyl peroxide 3,5,5 trimethyl hexanoate Tertiary butyl peroxy isopropyl carbonate Tertiary butyl peracetate Tertiary butyl perbenzoate 1,1 Bis (tertiary butyl peroxy) cyclohexane Normal butyl 4,4 bis (tertiary butyl peroxy) valerate and 2,2 Bis (tertiary butyl peroxy) butane.

Claim 9

A process as claimed in claim 1 characterized by the use in combination of magnesium hydroxide as said filler and a grafting initiator selected from the group consisting of Dicumyl peroxide 2,5-Dimethyl 2,5-di (tertiay butylperoxy) hexane 1,4-Di (tertiary butylperoxy iso propyl) benzene Tertiary butyl cumyl peroxide and Di-tertiary butyl peroxide.

Claim 10

A halogen-free, fire retardant crosslinked extruded product comprising a flame-retardant filler of the class that evolve substantial amounts of bound water on heating at temperatures above a value T d which value lies in the range 120°-250° C., said filler being dispersed in a compatible ethylene polymer base and the ratio of said filler to said polymer being in the range from 3:1 to 1:2 by weight; said polymer being crosslinked by silane-condensation crosslinks, said product being made by first forming a composition comprising said filler, said polymer base, a hydrolysable unsaturated silane, a free-radical initiator having a half-life of less than 10 minutes at a temperature 25° C. below the T d of said filler as determined by Differential Thermal Analysis using chlorobenzene as solvent, and a silanol condensation catalyst; second, and only after said ingredients have been mixed together, raising the temperature to a grafting temperature below said T d but at which said initiator decomposes to generate free-radicals that effect grafting of said silane to said polymer; third extruding the mixture containing the grafted polymer from an extrusion die to form a shaped product; and fourth exposing said shaped product to water until it is crosslinked by hydrolytic condensation reactions of the grafted silane.

Claim 11

A halogen-free, fire retardant crosslinked extruded product comprising a flame-retardant filler of the class that evolve substantial amounts of bound water on heating at temperatures above a value T d which value lies in the range 120°-250° C., said filler being dispersed in a compatible ethylene polymer base and the ratio of said filler to said polymer being in the range from 3:1 to 1:2 by weight; said polymer being crosslinked by silane-condensation crosslinks, said product being made by first forming a composition comprising said filler, said polymer base, a hydrolysable unsaturated silane, a free-radical initiator having a half-life of less than 10 minutes at a temperature 25° C. below the T d of said filler as determined by Differential Thermal Analysis using chlorobenzene as solvent, and a silanol condensation catalyst; second, and only after said ingredients have been mixed together, raising the temperature to a grafting temperature below said T d but at which said initiator decomposes to generate free-radicals that effect grafting of said silane to said polymer; third extruding the mixture containing the grafted polymer from an extrusion die to form a shaped product; and fourth exposing said shaped product to water until it is crosslinked by hydrolytic condensation reactions of the grafted silane.