Method for producing laminated bodies comprising an RE-FE-B type magnetic layer and a metal backing layer
Assignee: Magnequench International LLC
•
Filing: 1988-08-05
•
Granted: 1990-04-24
•
Expires: 2008-08-05
Abstract
Abstract Magnetically isotropic, fine grain, RE 2 Fe 4 B phase containing particulate material is hot pressed to full density and bonded to a metal backing layer of desired shape and composition. Additionally, if desired, the fully dense isotropic material can be further deformed in a direction lateral to the press direction so as to strain the particles to align the preferred magnetic axes of the crystal grains therein and thus form a laminate of a magnetically anisotropic magnet layer bonded to a metal backing layer.
Inventors
- 👤 Robert W. Lee
- 👤 Earl G. Brewer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 10:58
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/047; H01F1/053; H01F1/055; H01F1/057; H01F1/0571; H01F1/0575; H01F1/0576; B; B22; B22F; B22F7/00; B22F7/02; B22F7/04; B22F7/06; B22F7/08; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12049; Y10T428/12056
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
182 words
A method of making a laminated magnetic article comprising a magnetic layer comprising iron, neodymium and/or praseodymium, and boron and a supportive metal layer bonded to the magnetic layer, said method comprising: providing particulate material that is magnetically isotropic and characterized by a microstructure that is either amorphous material or of generally spherical crystal grains of an average size no greater than about 500 nm; and of a composition comprising a transition metal (TM) taken from the group consisting of iron and mixtures of iron and cobalt, one or more rare earth metals (RE) including neodymium and praseodymium, and boron, the proportions of such constituents being sufficient to form a product that upon crystallization consists essentially of the tetragonal crystalline compound having the empirical formula RE 2 TM 14 B; hot pressing a layer of the particulate material against a layer of chemically compatable, different metal composition at a temperature and pressure to consolidate the particulate layer into a fully densified layer and to bond it to the metal backing to produce a resultant layer of magnetic material on a metallic backing.
Claim 2
Independent Claim
182 words
A method of making a laminated magnetic article comprising a magnetic layer comprising iron, neodymium and/or praseodymium, and boron and a supportive metal layer bonded to the magnetic layer, said method comprising: providing particulate material that is magnetically isotropic and characterized by a microstructure that is either amorphous material or of generally spherical crystal grains of an average size no greater than about 500 nm; and of a composition comprising a transition metal (TM) taken from the group consisting of iron and mixtures of iron and cobalt, one or more rare earth metals (RE) including neodymium and praseodymium, and boron, the proportions of such constituents being sufficient to form a product that upon crystallization consists essentially of the tetragonal crystalline compound having the empirical formula RE 2 TM 14 B; hot pressing a layer of the particulate material against a layer of chemically compatable, different metal composition at a temperature and pressure to consolidate the particulate layer into a fully densified layer and to bond it to the metal backing to produce a resultant layer of magnetic material on a metallic backing.
Claim 3
Dependent Claim
41 words
In the method of claim 1, subsequently hot working the magnetic layer to deform it such that crystallographically preferred magnetic axes of grains therein are aligned so as to form a resultant magnetically anisotropic magnet body with a supportive backing plate.
Claim 4
Dependent Claim
47 words
In the method of claim 1, layering metallic backing powder and the isotropic particles and simultaneously pressing them during hot working to convert the metallic backing powder to a fully dense, sintered supportive backing plate bonded to a layer of fully dense, compressed, substantially isotropic magnetic material.
Claim 5
Dependent Claim
42 words
In the method of claim 3, subsequently hot working the consolidated isotropic material to deform it such that crystallographically preferred magnetic axes of grains therein are aligned so as to form a resultant magnetically anisotropic magnet body with a supportive backing plate.
Claim 6
Dependent Claim
45 words
In the method of claim 2, providing an expansion space, heating the compressed isotropic material and deforming it laterally into the expansion space to orient crystallites in the isotropic material while bonding the isotropic material metallic backing without removing the coercivity of the treated particles.
Claim 7
Dependent Claim
40 words
In the method of claim 1, providing a solid metallic backing with a reaction surface thereon, and loading the solid metal plate and the isotropic material in a hot press die prior to pressing the material against the reaction surface.
Claim 8
Dependent Claim
39 words
In the method of claim 6, subsequently hot working the compressed isotropic material to deform crystallites therein to be oriented along a crystallographically preferred magnetic axis to form a resultant magnetically anisotropic magnet body with a supportive backing plate.
Claim 9
Dependent Claim
55 words
In the method of claim 6, forming the metallic backing as a closed cylinder; loading the closed cylinder with the magnetically isotropic particles by filling the cylinder therewith; and isostatically compressing the outer surface of the cylinder and hot working the particles to simultaneously bond a treated, magnetically anisotropic material layer to the metallic backing.
Claim 10
Dependent Claim
53 words
In the method of claim 6, forming the metallic backing as spaced solid plates, surrounding the spaced solid plates with the isotropic particles and applying heat and pressure thereto so as to hot work the isotropic particles against the spaced solid plates while simultaneously bonding treated particles to each of said solid plates.
Claim 11
Dependent Claim
47 words
In the method of claim 6, providing a metal cylinder to form a metallic backing, loading the cylinder with the isotropic particles and pressing the particles along the axis of the metal cylinder while hot working them thereagainst to form a bonded connection to the metallic backing.
Claim 12
Independent Claim
101 words
A method for manufacturing magnetically anisotropic material from powder particles of magnetically isotropic material comprising RE 2 Fe 14 B crystal grains with a rare earth-rich grain boundary structure comprising the steps of: melt spinning a molten mixture of precursor material to form a ribbon of said magnetically isotropic material; fragmenting the ribbon to form particles of magnetically isotropic material; hot working the particles against a reaction surface of a metal backing to compress the isotropic particles together; and simultaneously bonding the coarse particles to the metal backing to form a composite magnet of isotropic material layer bonded to metal cladding.
Claim 13
Independent Claim
101 words
A method for manufacturing magnetically anisotropic material from powder particles of magnetically isotropic material comprising RE 2 Fe 14 B crystal grains with a rare earth-rich grain boundary structure comprising the steps of: melt spinning a molten mixture of precursor material to form a ribbon of said magnetically isotropic material; fragmenting the ribbon to form particles of magnetically isotropic material; hot working the particles against a reaction surface of a metal backing to compress the isotropic particles together; and simultaneously bonding the coarse particles to the metal backing to form a composite magnet of isotropic material layer bonded to metal cladding.
Claim 14
Dependent Claim
37 words
In the method of claim 11, hot working the particles by placing the particles and a metallic backing in a hot working die and compressing the particles against the metal backing to bond the isotropic particles thereto.
Claim 15
Dependent Claim
38 words
In the method of claim 12, subsequently hot working the compressed particles to deform crystallites therein to be oriented along a crystallographically preferred magnetic axis to form a resultant magnetically anisotropic magnet body with a supportive backing plate.
Claim 16
Dependent Claim
46 words
In the method of claim 12, forming the metallic backing as powder, layering the metallic backing powder and the isotropic particles and simultaneously pressing them during hot working to convert the metallic backing powder to a fully dense sintered metal layer bonded to the isotropic particles.
Claim 17
Dependent Claim
38 words
In the method of claim 14, subsequently hot working the compressed particles to deform crystallites therein to be oriented along a crystallographically preferred magnetic axis to form a resultant magnetically anisotropic magnet body with a supportive backing plate.
Claim 18
Dependent Claim
36 words
In the method of claim 14, applying the hot working pressure on the magnetically isotropic particles in a direction parallel to the press direction so as to form an interface therebetween of a mechanically interlocked pattern.
Claim 19
Dependent Claim
11 words
A laminated magnetic article produced by the process of claim 1.
Claim 20
Dependent Claim
11 words
A laminated magnetic article produced by the process of claim 2.
Claim 21
Dependent Claim
11 words
A laminated magnetic article produced by the process of claim 11.
Claim 22
Dependent Claim
11 words
A laminated magnetic article produced by the process of claim 13.
References Cited (Backward Citations)
US4322257A
Cited
US4076561A
Cited
US4104787A
Cited
US4325757A
Cited
EP0133758A2
Cited
US4792367A
Cited
US4710239A
Cited
US4793874A
Cited
US4808224A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-23 | 1993-10-23 | 1994-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-23 | 1997-10-23 | 1998-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-23 | 2001-10-23 | 2002-04-24 | $7700.00 | Window Closed / Lapsed |