US4919865A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Composite membranes of poly (methyl methacrylate) blends, their manufacture and their use
Assignee: Praxair Technology Inc
•
Filing: 1987-11-05
•
Granted: 1990-04-24
•
Expires: 2007-11-05
Abstract
Abstract Composite membranes are disclosed having a separation layer comprised of a mixture of poly(methy methacrylate) or a copolymer thereof and at least one cellulosic derivative resulting in enhanced separation and permeating characteristics of the overall composite membrane. Processes for making these composite membranes and the methods of using them are also disclosed. The membranes are particularly useful in gas separation applications and are most suited for the separation of hydrogen from a hydrogen containing stream.
Inventors
- 👤 Joyce K. Nelson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 08:05
CPC Classifications
B; B01; B01D; B01D71/00; B01D71/06; B01D71/40; B01D71/401; B01D71/4011; B01D69/00; B01D69/12; B01D71/08; B01D71/10; B01D71/76; C; C01; C01B; C01B3/00; C01B3/50; C01B3/501; C01B3/503; Y; Y10; Y10S; Y10S264/00; Y10S264/48; Y10S264/62
Claims Analysis
Total Claims: 63
Claim 1
Independent Claim
194 words
A composite membrane capable of selectively permeating at least one more readily permeable gaseous component from a gaseous feed mixture containing said component, and utilizing the high selectivity characteristics of poly(methyl) methacrylate) without the corresponding low permeability characteristics thereof, comprising: (a) a porous support layer that serves to provide support for a thin separation layer positioned thereon, said porous substrate having substantially no gas separation characteristics with respect to said gaseous feed mixture; and (b) an essentially non-porous gas separation layer positioned on said porous support layer, said separation layer that substantially determines the separation characteristics of the composite gas membrane being comprised of a mixture of poly(methyl methacrylate) or a copolymer thereof containing at least 50% by weight of poly(methyl methacrylate) and at least one cellulosic derivative, the proportions of said materials being selected so as to match the high separation characteristics provided by said poly(methyl methacrylate) and the high permeation characteristics provided by said cellulosic derivative to provide a particular, uniquely complementing combination of high gas separation and permeability for the separation of a particular gaseous feed mixture, whereby said composite membrane exhibits an enhanced combination of gas separation and permeability characteristics.
Claim 2
Dependent Claim
194 words
A composite membrane capable of selectively permeating at least one more readily permeable gaseous component from a gaseous feed mixture containing said component, and utilizing the high selectivity characteristics of poly(methyl) methacrylate) without the corresponding low permeability characteristics thereof, comprising: (a) a porous support layer that serves to provide support for a thin separation layer positioned thereon, said porous substrate having substantially no gas separation characteristics with respect to said gaseous feed mixture; and (b) an essentially non-porous gas separation layer positioned on said porous support layer, said separation layer that substantially determines the separation characteristics of the composite gas membrane being comprised of a mixture of poly(methyl methacrylate) or a copolymer thereof containing at least 50% by weight of poly(methyl methacrylate) and at least one cellulosic derivative, the proportions of said materials being selected so as to match the high separation characteristics provided by said poly(methyl methacrylate) and the high permeation characteristics provided by said cellulosic derivative to provide a particular, uniquely complementing combination of high gas separation and permeability for the separation of a particular gaseous feed mixture, whereby said composite membrane exhibits an enhanced combination of gas separation and permeability characteristics.
Claim 3
Dependent Claim
29 words
The composite membrane of claim 1, wherein the ratio by weight of the poly(methyl methacrylate) or copolymer thereof to the cellulose derivative is from about 10:90 to about 90:10.
Claim 4
Dependent Claim
16 words
The composite membrane of claim 2, wherein the ratio is from about 30:70 to about 70:30.
Claim 5
Dependent Claim
12 words
The composite membrane of claim 2, wherein the ratio is about 50:50.
Claim 6
Dependent Claim
19 words
The composite membrane of claim 1, wherein the copolymer is comprised of methyl methacrylate and ethyl methacrylate monomer units.
Claim 7
Dependent Claim
19 words
The composite membrane of claim 1, wherein the copolymer is comprised of methyl methacrylate and n-butyl methacrylate monomer units.
Claim 8
Dependent Claim
19 words
The composite membrane of claim 1, wherein the copolymer is comprised of methyl methacrylate and iso-butyl methacrylate monomer units.
Claim 9
Dependent Claim
32 words
The composite membrane of claim 1, wherein the cellulosic derivative is selected from the group consisting of cellulose acetate, cellulose acetate butyrate, cellulose propionate, cellulose butyrate, cellulose acetate propionate, and mixtures thereof.
Claim 10
Dependent Claim
13 words
The composite membrane of claim 8, wherein the cellulosic derivative is cellulose acetate.
Claim 11
Dependent Claim
19 words
The composite membrane of claim 9, wherein the cellulose acetate has a degree of acetylation of qreater than 2.0.
Claim 12
Dependent Claim
19 words
The composite membrane of claim 1, wherein the thickness of the separation layer is less than about 0.4 microns
Claim 13
Dependent Claim
17 words
The composite membrane of claim 1, wherein the thickness is from about 0.05 to about 2 microns.
Claim 14
Dependent Claim
14 words
The composite membrane of claim 1, wherein the support layer comprises a polymeric material.
Claim 15
Dependent Claim
23 words
The composite membrane of claim 13, wherein the support layer comprises at least one of polysulfone, polyolefins, polyphenylenesulfide, polyether ketone, polyam-ides and polyimides
Claim 16
Dependent Claim
12 words
The composite membrane of claim 13, wherein the support layer is polysulfone.
Claim 17
Dependent Claim
16 words
The composite membrane of claim 23 in which said porous substrate is an annealed polymeric material.
Claim 18
Dependent Claim
34 words
The composite membrane of claim 68 in which the annealed polymeric material substrate is in asymmetric form having a porous, non-selective support region comprising said porous support layer and a dense, semipermeable skin region.
Claim 19
Dependent Claim
23 words
The composite membrane of claim 1, wherein the cellulosic derivative of the separation layer comprises cellulose acetate and the support layer comprises polysulfone.
Claim 20
Dependent Claim
15 words
The composite membrane of claim 1, wherein the composite membrane is in hollow fiber form.
Claim 21
Dependent Claim
253 words
A process for the preparation of a composite membrane capable of selectively permeating at least one more readily permeable component from a gaseous feed mixture containing said component, and utilizing the high selectivity characteristics of poly(methyl methacrylate) without the corresponding low permeability characteristics thereof, comprising: (a) providing a porous support layer to provide support for a thin separation layer to be positioned thereon, said porous support layer having substantially no gas separation characteristics with respect to said gaseous feed mixture; (b) providing a solution containing a mixture of poly(methyl methacrylate) or a copolymer thereof containing at least 50% by weight of poly(methyl methacrylate), at least one cellulosic derivative and a solvent therefor, which solvent is a non-solvent for the porous support layer; (c) coating the porous support layer with said solution to provide an essentially non-porous gas separation layer on said porous support layer; and (d) drying said separation layer on the porous support layer to form the desired composite membrane, said non-porous gas separation layer substantially determining the gas separation characteristics of the composite membrane, the proportions of said materials being selected so as to match the high separation characteristics provided by said poly(methyl methacrylate) and the high permeation characteristics provided by said cellulosic derivative to provide a particular, uniquely complementing combination of high gas separation and permeability for the separation of a particular gaseous feed mixture, whereby composite membranes that exhibit an enhanced combination of gas separation and permeability characteristics can be readily prepared for use in desirable gas separation operations.
Claim 22
Dependent Claim
253 words
A process for the preparation of a composite membrane capable of selectively permeating at least one more readily permeable component from a gaseous feed mixture containing said component, and utilizing the high selectivity characteristics of poly(methyl methacrylate) without the corresponding low permeability characteristics thereof, comprising: (a) providing a porous support layer to provide support for a thin separation layer to be positioned thereon, said porous support layer having substantially no gas separation characteristics with respect to said gaseous feed mixture; (b) providing a solution containing a mixture of poly(methyl methacrylate) or a copolymer thereof containing at least 50% by weight of poly(methyl methacrylate), at least one cellulosic derivative and a solvent therefor, which solvent is a non-solvent for the porous support layer; (c) coating the porous support layer with said solution to provide an essentially non-porous gas separation layer on said porous support layer; and (d) drying said separation layer on the porous support layer to form the desired composite membrane, said non-porous gas separation layer substantially determining the gas separation characteristics of the composite membrane, the proportions of said materials being selected so as to match the high separation characteristics provided by said poly(methyl methacrylate) and the high permeation characteristics provided by said cellulosic derivative to provide a particular, uniquely complementing combination of high gas separation and permeability for the separation of a particular gaseous feed mixture, whereby composite membranes that exhibit an enhanced combination of gas separation and permeability characteristics can be readily prepared for use in desirable gas separation operations.
Claim 23
Dependent Claim
28 words
The process of claim 20, wherein the ratio by volume of poly(methyl methacrylate) or copolymer thereof to cellulose derivative in solution is from about 70:30 to about 30:70.
Claim 24
Dependent Claim
80 words
The process of claim 20, wherein the solvent for the solution includes a mixture of acetic acid and isopropanol; a mixture of acetic acid, a C 1 -C 4 aliphatic alcohol and water; nitromethane; a mixture of nitromethane and a C 1 -C 4 aliphatic alcohol; acetone; or a mixture of acetone and a C 1 -C 4 aliphatic alcohol; or a mixture of acetone, a C 1 -C 4 aliphatic alcohol and water; wherein the support layer is polysulfone.
Claim 25
Dependent Claim
26 words
The process of claim 20, wherein the solvent for the solution includes a mixture of acetic acid, isopropanol and water when the support layer is polysulfone.
Claim 26
Dependent Claim
31 words
The process of claim 20, wherein the cellulosic derivative is selected from the group consisting of cellulose acetate, cellulose acetate butyrate, cellulose propionate, cellulose butyrate, cellulose acetate propionate, and mixtures thereof.
Claim 27
Dependent Claim
12 words
The process of claim 24, wherein the cellulosic derivative is cellulose acetate.
Claim 28
Dependent Claim
19 words
The process of claim 25, wherein the cellulose acetate has a degree of acetylation that is greater than 2.0.
Claim 29
Dependent Claim
18 words
The process of claim 20, wherein the copolymer is comprised of methyl methacrylate and ethyl methacrylate monomer units.
Claim 30
Dependent Claim
18 words
The process of claim 20, wherein the copolymer is comprised of methyl methacrylate and n-butyl methacrylate monomer units.
Claim 31
Dependent Claim
18 words
The process of claim 20, wherein the copolymer is comprised of methyl methacrylate and iso-butyl methacrylate monomer units.
Claim 32
Dependent Claim
18 words
The process of claim 20, wherein the thickness of the separating layer is less than about 0.4 microns.
Claim 33
Dependent Claim
20 words
The process of claim 20, wherein the thickness of the separatinq layer is from about 0.05 to about 0.2 microns.
Claim 34
Dependent Claim
13 words
The process of claim 20, wherein the support layer comprises a polymeric material.
Claim 35
Dependent Claim
15 words
The process of claim 41 in which said porous substrate is an annealed polymeric material.
Claim 36
Dependent Claim
69 words
The process of claim 71 in which said porous substrate comprises a polymeric material having a glass transition temperature about 100° C., said polymeric material being annealed at a temperature close to its glass transition temperature for a short time under non-solvent and non-swelling conditions, the annealed substrate being in asymmetric form having a porous, non-selective support region comprising said porous support layer and a dense, semipermeable skin region.
Claim 37
Dependent Claim
22 words
The process of claim 32, wherein the support layer comprises at least one of polysulfone, polyolefins, polyphenylenesulfide, polyether ketone, polyamides and polyimides.
Claim 38
Dependent Claim
11 words
The process of claim 42, wherein the support layer is polysulfone.
Claim 39
Dependent Claim
22 words
The process of claim 20, wherein the cellulose derivative of the separation layer comprises cellulose acetate and the support layer comprises polysulfone.
Claim 40
Dependent Claim
14 words
The process of claim 20, wherein the composite membrane is in hollow fiber form.
Claim 41
Independent Claim
276 words
A method for separating at least one more readily permeable gaseous component from a gaseous feed mixture containing said component, and utilizing the high selectivity characteristics of poly(methyl methacrylate) without the corresponding low permeability characteristics thereof, comprising: (a) contacting said gaseous feed mixture with one surface of a composite membrane capable of selectively permeating said more readily permeable gaseous component, said composite membrane comprising (1) a porous support layer that serves to provide support for a thin separation layer positioned thereon, said porous substrate having substantially no gas separation characteristics with respect to said gaseous feed mixture, and (2) an essentially non-porous gas separation layer positioned on said porous support layer, said separation layer that substantially determines the separation characteristics of the composite membrane being comprised of a mixture of poly(methyl methacrylate) or a copolymer thereof containing at least 50% by weight of poly(methyl methacrylate) and at least one cellulosic derivative, the proportions of said materials being selected so as to match the high separation characteristics provided by said poly(methyl methacrylate) and the high permeation characteristics provided by said cellulosic derivative to provide a particular, uniquely complementing combination of high gas separation and permeability for the separation of a particular gaseous feed mixture, the more permeable gas component selectively permeating in and through said composite membrane; and (b) removing from the vicinity of the opposite surface of the composite membrane said more readily permeable component as permeate gas having a greater proportion of said more permeable component than is present in said gaseous feed mixture, whereby the gas separation method is enhanced by the desirable combination of gas separation and permeability characteristics of said composite membrane.
Claim 42
Independent Claim
276 words
A method for separating at least one more readily permeable gaseous component from a gaseous feed mixture containing said component, and utilizing the high selectivity characteristics of poly(methyl methacrylate) without the corresponding low permeability characteristics thereof, comprising: (a) contacting said gaseous feed mixture with one surface of a composite membrane capable of selectively permeating said more readily permeable gaseous component, said composite membrane comprising (1) a porous support layer that serves to provide support for a thin separation layer positioned thereon, said porous substrate having substantially no gas separation characteristics with respect to said gaseous feed mixture, and (2) an essentially non-porous gas separation layer positioned on said porous support layer, said separation layer that substantially determines the separation characteristics of the composite membrane being comprised of a mixture of poly(methyl methacrylate) or a copolymer thereof containing at least 50% by weight of poly(methyl methacrylate) and at least one cellulosic derivative, the proportions of said materials being selected so as to match the high separation characteristics provided by said poly(methyl methacrylate) and the high permeation characteristics provided by said cellulosic derivative to provide a particular, uniquely complementing combination of high gas separation and permeability for the separation of a particular gaseous feed mixture, the more permeable gas component selectively permeating in and through said composite membrane; and (b) removing from the vicinity of the opposite surface of the composite membrane said more readily permeable component as permeate gas having a greater proportion of said more permeable component than is present in said gaseous feed mixture, whereby the gas separation method is enhanced by the desirable combination of gas separation and permeability characteristics of said composite membrane.
Claim 43
Dependent Claim
22 words
The method of claim 39, wherein the said at least one gas comprises hydrogen and the gas mixture comprises hydrogen and nitrogen.
Claim 44
Dependent Claim
22 words
The method of claim 39 wherein the said at least one gas comprises hydrogen and the gas mixture comprises hydrogen and methane..
Claim 45
Dependent Claim
24 words
The method of claim 39, wherein the said at least one gas comprises carbon dioxide and the gas mixture comprises carbon dioxide and methane.
Claim 46
Dependent Claim
22 words
The method of claim 39, wherein the said at least one gas comprises nitrogen and the gas mixture comprises nitrogen and methane.
Claim 47
Dependent Claim
20 words
The method of claim 39, wherein the said at least one gas comprises oxygen and the gas mixture comprises air.
Claim 48
Dependent Claim
26 words
The method of claim 39, wherein the ratio by weight of poly(methyl methacrylate) or copolymer thereof to cellulosic derivative is from about 10:90 to about 90:10.
Claim 49
Dependent Claim
18 words
The method of claim 39, wherein the copolymer is comprised of methyl methacrylate and ethyl methacrylate monomer units.
Claim 50
Dependent Claim
18 words
The method of claim 39, wherein the copolymer is comprised of methyl methacrylate and n-butyl methacrylate monomer units.
Claim 51
Dependent Claim
18 words
The method of claim 39, wherein the copolymer is comprised of methyl methacrylate and iso-butyl methacrylate monomer units.
Claim 52
Dependent Claim
31 words
The method of claim 39, wherein the cellulosic derivative is selected from the group consisting of cellulose acetate, cellulose acetate butyrate, cellulose propionate, cellulose butyrate, cellulose acetate propionate, and mixtures thereof.
Claim 53
Dependent Claim
12 words
The method of claim 39, wherein the cellulosic derivative is cellulose acetate.
Claim 54
Dependent Claim
17 words
The method of claim 50, wherein the cellulose acetate has a degree of acetylation greater than 2.0.
Claim 55
Dependent Claim
18 words
The method of claim 39, wherein the thickness of the separating layer is less than about 0.4 microns.
Claim 56
Dependent Claim
13 words
The method of claim 39, wherein the support layer comprises a polymeric material.
Claim 57
Dependent Claim
22 words
The method of claim 53, wherein the support layer comprises at least one of polysulfone, polyolefins, polyphenylenesulfide, polyether ketone, polyamides and polyimides.
Claim 58
Dependent Claim
11 words
The method of claim 53, wherein the support layer is polysulfone.
Claim 59
Dependent Claim
22 words
The method of claim 39, wherein the cellulosic derivative of the separation layer comprises cellulose acetate and the support layer comprises polysulfone.
Claim 60
Dependent Claim
14 words
The method of claim 39, wherein the composite membrane is a hollow fiber form.
Claim 61
Dependent Claim
13 words
The method of claim 53, wherein the substrate is an annealed polymeric material.
Claim 62
Dependent Claim
15 words
The method of claim 73 in which said porous substrate is an annealed polymeric material.
Claim 63
Dependent Claim
33 words
The method of claim 74 in which the annealed polymeric material substrate is an asymmetric form having a porous, non-selective support region comprising said porous support layer and a dense, semipermeable skin region.
References Cited (Backward Citations)
US3892665A
Cited
US4230463A
Cited
US4214020A
Cited
US4459210A
Cited
US4662905A
Cited
US4664481A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-23 | 1993-10-23 | 1994-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-23 | 1997-10-23 | 1998-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-23 | 2001-10-23 | 2002-04-24 | $7700.00 | Window Closed / Lapsed |