Process for joining molded silicon nitride parts
Assignee: Forschungszentrum Jülich
•
Filing: 1987-10-30
•
Granted: 1990-04-17
•
Expires: 2007-10-30
Abstract
Abstract For joining shaped bodies of silicon nitride together, silicon nitride surfaces to be joined are first polished and then put into an apparatus for applying sputtered layers where they are first cleaned by ion bombardment in argon, followed immediately by sputtering with silicon in a nitrogen atmosphere such that a layer is deposited having a nitrogen content exceeding the Si3N4 stoichiometric ratio. This readily provides a layer of the composition Si3N5.5. A complementary nitrogen deficient layer is also provided in the joint before hot pressing, either in the form of a silicon layer that goes between the nitrogen-rich silicon nitride layers or in the form of a nitrogen-deficient silicon nitride layer sputtered onto a polished silicon nitride surface at relatively low nitrogen pressure. The parts are isostatically hot pressed together at 1500 DEG to 1750 DEG C. in a nitrogen atmosphere. The layers which are usually thinner than 1 mu m interact, with the disappearance of excess nitrogen and silicon, so that once the joint is produced all traces of jointure tend to disappear. The presence of a small amount of Y2O3 at the joint has a favorable effect.
Inventors
- 👤 Erno Gyarmati
- 👤 Xiliang Qiu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 12:01
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/64; C04B35/645; C04B37/00; C04B37/003; C04B37/005; C04B2237/00; C04B2237/02; C04B2237/16; C04B2237/30; C04B2237/32; C04B2237/36; C04B2237/368; C04B2237/50; C04B2237/52; C04B2237/56; C04B2237/568; C04B2237/70; C04B2237/704; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1052; Y10T156/1062; Y10T156/1075
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
147 words
Process for joining together, by hot pressing, first and second molded parts each having a silicon nitride surface at least in the portion of each said part which is intended to be joined to the other said part, comprising the steps of: polishing at least said portions of said molded silicon nitride surfaces which are to be joined together, for reducing surface roughness; applying sputtering a silicon nitride layer having a nitrogen content exceeding the Si 3 N 4 stoichiometric ratio on at least one of said surface portions which are to be joined together, and hot pressing together said surface portions which are to be joined with provision between said surface portions of a complementary nitrogen deficiency relative to silicon for establishment of an at least approximate stoichiometric ratio of nitrogen to silicon in a and cross a resulting joint by diffusive migration during hot pressing.
Claim 2
Dependent Claim
147 words
Process for joining together, by hot pressing, first and second molded parts each having a silicon nitride surface at least in the portion of each said part which is intended to be joined to the other said part, comprising the steps of: polishing at least said portions of said molded silicon nitride surfaces which are to be joined together, for reducing surface roughness; applying sputtering a silicon nitride layer having a nitrogen content exceeding the Si 3 N 4 stoichiometric ratio on at least one of said surface portions which are to be joined together, and hot pressing together said surface portions which are to be joined with provision between said surface portions of a complementary nitrogen deficiency relative to silicon for establishment of an at least approximate stoichiometric ratio of nitrogen to silicon in a and cross a resulting joint by diffusive migration during hot pressing.
Claim 3
Dependent Claim
111 words
Process as defined in claim 1, wherein a said silicon nitride layer having a nitrogen content exceeding the Si 3 N 4 stoichiometric ratio, having an approximate composition of Si 3 N 5 .5 and having a thickness not greater than 1 μm, is applied on both of said surface portions which are to be joined together and the said provision between said surface portions of a complementary nitrogen deficiency relative to silicon is performed by providing a silicon layer of about half the thickness of said Si 3 N 5 .5 layer immediately adjoining each said Si 3 N 5 .5 layer before said surface portions are hot pressed together.
Claim 4
Dependent Claim
184 words
Process as defined in claim 1, wherein a said silicon nitride layer having a nitrogen content exceeding the Si 3 N 4 stoichiometric ratio is applied by sputtering on said polished silicon nitride surface portion of said first molded part which is to be joined to said second molded part and there is applied by sputtering on the silicon nitride surface portion of said second molded part which is to be joined with said first molded part a nitrogen deficient silicon nitride layer of substantially the same thickness as said silicon nitride layer having excess nitrogen content, said silicon nitride layer having excess nitrogen content being applied under sputtering conditions producing an approximate layer composition of Si 3 N 5 .5 and said nitrogen deficient silicon nitride layer being applied under sputtering conditions producing an approximate layer composition of Si 3 N 2 .5 whereby said complementary nitrogen deficiency relative to silicon is established between said surface portions which are to be joined, both said layers being applied prior to hot pressing said polished silicon nitride surface portions of said respective molded parts together.
Claim 5
Dependent Claim
30 words
Process as defined in claim 3, wherein both said silicon nitride layer having excess nitrogen content and said nitrogen deficient silicon nitride layer have a thickness of about 0.3 μm.
Claim 6
Dependent Claim
48 words
Process as defined in claim 2, wherein both of said silicon nitride layers having an approximate composition of Si 3 N 5 .5. have a thickness of about 0.2 μm and wherein the total thickness of silicon interposed between them likewise has a thickness of about 0.2 μm.
Claim 7
Dependent Claim
24 words
Process as defined in claim 2, wherein said molded parts to be joined together are of silicon nitride containing Y 2 O 3 .
Claim 8
Dependent Claim
24 words
Process as defined in claim 3, wherein said molded parts to be joined together are of silicon nitride containing Y 2 O 3 .
Claim 9
Dependent Claim
25 words
Process as defined in in claim 4, wherein said molded parts to be joined together are of silicon nitride containing Y 2 O 3 .
Claim 10
Dependent Claim
47 words
Process as claimed in claim 1, wherein the step of applying a silicon nitride layer by sputtering is preceded by argon etching said polished silicon nitride surface portion on which a silicon nitride layer is to be applied, said argon etching being preferred by argon ion bombardment.
Claim 11
Dependent Claim
55 words
Process as defined in claim 1, wherein the step of hot pressing together said surface portions which are to be joined is performed at a temperature in the range from 1500 to 1750° C. and at pressures in the range from 10 to 30 MPa for from 20 to 120 minutes in a nitrogen atmosphere.
Claim 12
Dependent Claim
190 words
Process of joining together, by hot pressing, first and second molded parts each having a molded silicon nitride surface at least in the portion of each said part which is intended to be joined to the other said part, comprising the steps of: polishing at least said portions of said molded silicon nitride surfaces which are to be joined together, for reducing surface roughness; producing a relative nitrogen deficiency in the polished portions of said silicon nitride surfaces by sputtering thereon a coating less than 2um thick of composition Si 3 N x in which x has a value from 0 to 3.9, inclusive; applying by sputtering a silicon nitride layer having a nitrogen content exceeding the Si 3 N 4 stoichiometric ratio on at least one of said nitrogen-deficient polished surface portions coated with said nitrogen-deficient silicon nitride coating, for providing a complementary nitrogen excess between said nitrogen-deficient polished surface portions, and then hot pressing together said surface portions which are to be joined for establishment of an at least approximate stoichiometric ratio of nitrogen to silicon in and across a resulting joint by diffusive migration during hot pressing.
Claim 13
Dependent Claim
190 words
Process of joining together, by hot pressing, first and second molded parts each having a molded silicon nitride surface at least in the portion of each said part which is intended to be joined to the other said part, comprising the steps of: polishing at least said portions of said molded silicon nitride surfaces which are to be joined together, for reducing surface roughness; producing a relative nitrogen deficiency in the polished portions of said silicon nitride surfaces by sputtering thereon a coating less than 2um thick of composition Si 3 N x in which x has a value from 0 to 3.9, inclusive; applying by sputtering a silicon nitride layer having a nitrogen content exceeding the Si 3 N 4 stoichiometric ratio on at least one of said nitrogen-deficient polished surface portions coated with said nitrogen-deficient silicon nitride coating, for providing a complementary nitrogen excess between said nitrogen-deficient polished surface portions, and then hot pressing together said surface portions which are to be joined for establishment of an at least approximate stoichiometric ratio of nitrogen to silicon in and across a resulting joint by diffusive migration during hot pressing.
Claim 14
Dependent Claim
65 words
Process as defined in claim 11, wherein said composition Si 3 N x of said coating of relative nitrogen deficiency is an approximate composition of Si 3 N 2 .5 and said coating is not more than 1 μm thick and wherein said silicon nitride layer having a nitrogen content exceeding Si 3 N 4 has an approximate composition of Si 3 N 5 .5.
Claim 15
Dependent Claim
38 words
Process as defined in claim 12, wherein said silicon nitride layer of approximate composition Si 3 N 5 .5 is applied to both said nitrogen-deficient polished surface portions in a thickness not exceeding 1 μm in each case.
Claim 16
Dependent Claim
36 words
Process as defined in claim 13, wherein said layer having an approximate composition of Si 3 N 5 .5. is applied on each of said nitrogen-deficient polished surface portions has a thickness of about 0.2 μm.
Claim 17
Dependent Claim
23 words
Process as defined in claim 11, wherein said first and second molded parts are of silicon nitride containing Y 2 O 3 .
Claim 18
Dependent Claim
43 words
Process as defined in claim 11, wherein the step of producing a relative nitrogen deficiency in said polished silicon nitride surface portions by sputtering is preceded by argon etching the said polished molded silicon nitride surface portions which are to be joined together.
Claim 19
Dependent Claim
55 words
Process as defined in claim 11, wherein the step of hot pressing together said surface portions which are to be joined is performed at a temperature in the range from 1500 to 1750° C. and at pressures in the range from 10 to 30 MPa for from 20 to 120 minutes in a nitrogen atmosphere.
Claim 20
Dependent Claim
217 words
Process for joining together, by hot pressing, first and second molded parts each having a molded silicon nitride surface at least in the portion of each said part which is intended to be joined to the other said part, comprising the steps of: polishing at least said portions of said molded silicon nitride surfaces which are to be joined together, for reducing surface roughness; producing a relative nitrogen deficiency in the polished silicon nitride surface portion of said first molded part by sputtering thereon a coating less than 2 μm thick of composition Si 3 N x in which x has a value from 0 to 3.9 inclusive; applying by sputtering a silicon nitride layer having a nitrogen content exceeding the Si 3 N 4 stoichiometric ratio on the nitrogen-deficient surface of said first molded part; thereafter applying a coating less than 2 μm thick by sputtering a coating of composition Si 3 N x in which x has a value from 0 to 3.9 inclusive on at least one of said surface portions which are to be joined, and then hot pressing together said surface portions which are to be joined for establishment of an at least approximate stoichiometric ratio of nitrogen to silicon in and across a resulting joint by diffusive migration during hot pressing.
Claim 21
Dependent Claim
217 words
Process for joining together, by hot pressing, first and second molded parts each having a molded silicon nitride surface at least in the portion of each said part which is intended to be joined to the other said part, comprising the steps of: polishing at least said portions of said molded silicon nitride surfaces which are to be joined together, for reducing surface roughness; producing a relative nitrogen deficiency in the polished silicon nitride surface portion of said first molded part by sputtering thereon a coating less than 2 μm thick of composition Si 3 N x in which x has a value from 0 to 3.9 inclusive; applying by sputtering a silicon nitride layer having a nitrogen content exceeding the Si 3 N 4 stoichiometric ratio on the nitrogen-deficient surface of said first molded part; thereafter applying a coating less than 2 μm thick by sputtering a coating of composition Si 3 N x in which x has a value from 0 to 3.9 inclusive on at least one of said surface portions which are to be joined, and then hot pressing together said surface portions which are to be joined for establishment of an at least approximate stoichiometric ratio of nitrogen to silicon in and across a resulting joint by diffusive migration during hot pressing.
Claim 22
Dependent Claim
81 words
Process as defined in claim 18, wherein said composition Si 3 N x of said coating sputtered onto the polished silicon nitride surface portion of said first molded part and the composition Si 3 N x of said coating sputtered as the third sputtering step of said process are each not more than 1 μm thick, and wherein said silicon nitride layer having a nitrogen content exceeding Si 3 N 4 has an approximate composition of Si 3 N 5 .5.
Claim 23
Dependent Claim
23 words
Process as defined in claim 18, wherein said first and second molded parts are of silicon nitride containing Y 2 O 3 .
Claim 24
Dependent Claim
42 words
Process as defined in claim 18, wherein the step of producing a relative nitrogen deficiency in said polished silicon nitride surface portion of said first molded part is preceded by argon etching of said polished surface portion of said first molded part.
Claim 25
Dependent Claim
56 words
Process as defined in claim 18, wherein the step of hot pressing together said surface portions which are to be joined is performed at a temperature in the range from 1500° C. to 1750° C. and at pressures in the range from 10 to 30 MPa for from 10 to 120 minutes in a nitrogen atmosphere.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-16 | 1993-10-16 | 1994-04-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-16 | 1997-10-16 | 1998-04-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-16 | 2001-10-16 | 2002-04-17 | $7700.00 | Window Closed / Lapsed |