Air-tight ceramic container
Assignee: Toshiba Corp
•
Filing: 1988-04-01
•
Granted: 1990-04-17
•
Expires: 2008-04-01
Abstract
Abstract A method of manufacturing an air-tight ceramic container is disclosed. This method includes the steps of coating an active metal consisting of Ti and/or Zr on an opening end face of a ceramic tubular member in an amount of 0.1 to 10 mg/cm 2 , thereby forming an active metal layer, placing a brazing filler metal on the active metal layer, placing a metal cover member for shielding an opening portion of the ceramic tubular member so that a peripheral portion end face of the metal cover member is in contact with the brazing filler metal, and melting the brazing filler metal by heating, thereby brazing the metal cover member to the opening end face of the ceramic tubular member.
Inventors
- 👤 Masako Nakahashi
- 👤 Makoto Shirokane
- 👤 Hiromitsu Takeda
- 👤 Tatsuo Yamazaki
- 👤 Tsutomu Okutomi
- 👤 Shozi Niwa
- 👤 Mikio Okawa
- 👤 Mitsutaka Homma
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 21:14
CPC Classifications
H; H01; H01H; H01H33/00; H01H33/60; H01H33/66; H01H33/662; H01H33/66207; C; C04; C04B; C04B37/00; C04B37/02; C04B37/023; C04B37/026; C04B2235/00; C04B2235/65; C04B2235/658; C04B2235/6581; C04B2237/00; C04B2237/02; C04B2237/12; C04B2237/125; C04B2237/126; C04B2237/127; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/343; C04B2237/40; C04B2237/405; C04B2237/406; C04B2237/407; C04B2237/50; C04B2237/70; C04B2237/708; C04B2237/76; C04B2237/765; C04B2237/80; C04B2237/84; H01H2033/66215; H01H33/66261; H01H2033/66276; H10; H10W; H10W72/00; H10W72/50; H10W72/531; H10W72/536; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/4913; Y10T29/49146
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
138 words
A method of manufacturing an air-tight ceramic container, comprising the steps of: coating an active metal consisting of Li and/or Zr on an opening end face of a ceramic tubular member in tight contact therewith by means of an organic adhesive in an amount of 0.1 to 10 mg/cm 2 , thereby forming an active metal layer which is not reacted with the ceramic member; placing a brazing filler metal on said active metal layer; placing a metal cover member for shielding an opening portion of said ceramic tubular member so that a peripheral portion end face of said metal cover is in contact with said brazing filler metal; melting said brazing filler metal by heating, thereby simultaneously reacting the active metal layer with the ceramic base to form a metal-ceramic bond and brazing said metal cover thereto.
Claim 2
Independent Claim
138 words
A method of manufacturing an air-tight ceramic container, comprising the steps of: coating an active metal consisting of Li and/or Zr on an opening end face of a ceramic tubular member in tight contact therewith by means of an organic adhesive in an amount of 0.1 to 10 mg/cm 2 , thereby forming an active metal layer which is not reacted with the ceramic member; placing a brazing filler metal on said active metal layer; placing a metal cover member for shielding an opening portion of said ceramic tubular member so that a peripheral portion end face of said metal cover is in contact with said brazing filler metal; melting said brazing filler metal by heating, thereby simultaneously reacting the active metal layer with the ceramic base to form a metal-ceramic bond and brazing said metal cover thereto.
Claim 3
Dependent Claim
23 words
A method according to claim 1, wherein a paste containing a powder of said active metal is applied to coat said active metal.
Claim 4
Dependent Claim
45 words
A method according to claim 1, wherein a powder of said active metal is sprayed to be adhered on the opening end face of said ceramic tubular member on which an adhesive material is applied in order to coat said active metal on said member.
Claim 5
Dependent Claim
25 words
A method according to claim 2, wherein the powder of said active metal has an average grain size which is not more than 10 μm.
Claim 6
Dependent Claim
50 words
A method according to claim 1, wherein an integral foil of brazing filler metal having an upper surface on which a projection is formed in a widthwise direction of the opening end face of said ceramic tubular member and a smooth lower surface is used as said brazing filler metal.
Claim 7
Dependent Claim
25 words
A method according to claim 5, wherein said foil of brazing filler metal in which a through hole is formed in the projections is used.
Claim 8
Dependent Claim
49 words
A method according to claim 1, wherein a foil of brazing filler metal has a multi-layer structure in which two brazing filler metal layers sandwich a barrier layer consisting of a metal having a higher melting point than that of the brazing filler metal which remains unmelted after brazing.
Claim 9
Dependent Claim
12 words
An air-tight ceramic container manufactured by a method defined in claim 1.
Claim 10
Dependent Claim
236 words
A method of manufacturing a vacuum interrupter which comprises an air-tight ceramic container defined in claim 1; a pair of contact rods extending from the outside of said ceramic container through to the inside and opposed to each other, at least one of said contact rods being moved in an axial direction so that said contact rods can be opened/closed; metal contact members arranged at the distal ends of said contact rods; a bellows for moving said contact rods in the axial direction while maintaining a vacuum state in said container; and a metal arc-shield, positioned to surround said contact members, for preventing the metal evaporated from said contact members from adhering to an inner surface of said tubular member, comprising he steps of: coating a powder of an active metal consisting of Li and/or Zr to an inner surface of the ceramic tubular member in tight contact therewith by means of an organic adhesive in an amount of 0.1 to 10 mg/cm 2 , thereby forming an active metal layer which is not reacted with the ceramic member; placing a brazing filler metal on said active metal layer; placing said arc-shield to be in contact with the brazing filler metal; melting said brazing filler metal by heating thereby simultaneously reacting the active metal layer with the ceramic base to form a metal-ceramic bond and brazing said arc-shield to the inner surface of said tubular member.
Claim 11
Dependent Claim
25 words
A method according to claim 9, wherein a paste containing a powder of said active metal is applied in order to coat said active metal.
Claim 12
Dependent Claim
40 words
A method according to claim 9, wherein a powder of said active metal is sprayed to be adhered to the inner surface of said ceramic tubular member on which an adhesive is applied in order to coat said active metal.
Claim 13
Dependent Claim
37 words
A method according to claim 9, wherein a stress relaxation member is provided to said arc-shield, and said stress relaxation member is bonded by way of brazing directly to the inner surface of said ceramic tubular member.
Claim 14
Dependent Claim
11 words
A vacuum interrupter manufactured by a method defined in claim 9.
References Cited (Backward Citations)
US2362893A
Cited
US2570248A
Cited
US2731578A
Cited
US2798577A
Cited
US2996401A
Cited
US3063144A
Cited
DE1045305B
Cited
US3088201A
Cited
US3141058A
Cited
US3171734A
Cited
US3368023A
Cited
US3475442A
Cited
US3656225A
Cited
US4077114A
Cited
FR2450794A1
Cited
US4436241A
Cited
US4729504A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-16 | 1993-10-16 | 1994-04-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-16 | 1997-10-16 | 1998-04-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-16 | 2001-10-16 | 2002-04-17 | $7700.00 | Window Closed / Lapsed |