Method for the continuous fabrication of comminuted hydrogen storage alloy material negative electrodes
Assignee: Chevron Technology Ventures LLC
•
Filing: 1989-02-09
•
Granted: 1990-04-10
•
Expires: 2009-02-09
Abstract
Abstract An improved method for the continuous fabrication of metal-hydride, electrochemical, hydrogen storage alloy, negative electrodes for use in rechargeable nickel metal hydride cells. The improved method comprises the steps of reducing the size of a high hardness, metal hydride, hydrogen storage alloy by shattering it along natural fracture line thereof. The process next includes providing measured amounts of powered metal hydride electrochemical hydrogen storage alloy material and disposing said material upon a continuous wire mesh screen substrate. Thereafter, the powdered metal hydride electrochemical hydrogen storage alloy and wire mesh screen are subjected to a compaction process wherein they are rolled and pressed so as to form a single integral electrode web which is subsequently exposed to a high temperature sintering process in a chemically inert environment. The sintering process is designed to drive off excess moisture in the material while discouraging oxidation of the electrode web and set the electrode web state of charge.
Inventors
- 👤 Merle Wolff
- 👤 Mark A. Nuss
- 👤 Michael A. Fetchenko
- 👤 Andrea L. Lijoi
- 👤 Steven P. Sumner
- 👤 Joseph LaRocca
- 👤 Thomas Kaatz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 21:33
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/24; H01M4/242; B; B22; B22F; B22F7/00; B22F7/002; B22F9/00; B22F9/02; B22F9/023; B22F9/04; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
286 words
A method of substantially continuously fabricating a large area, metal hydride electrochemical hydrogen storage alloy negative electrode for use in a rechargeable nickel-metal hydride battery, said method comprising the steps of: (a) providing particulate metal hydride electrochemical hydrogen storage alloy material in a substantially non-reactive gas atmosphere; (b) providing a high speed impact mill adapted to tangentially and radially accelerate particles placed therein against an impact block; (c) introducing said particulate metal hydride, hydrogen storage alloy material into said impact mill for comminution along natural fracture lines of the material, while maintaining said non-reactive atmosphere; (d) transporting said comminuted metal hydride, electrochemical hydrogen storage material to a classifying means in a stream of said substantially non-reactive gas; (e) separating oversized particles from said comminuted material in said classifying means; (f) recirculating said non-reactive gas; (g) transporting said comminuted metal hydride electrochemical hydrogen storage alloy to a compaction means; (h) providing a continuous, wire mesh screen substrate to said compaction means; (i) providing a measured amount of the comminuted metal hydride electrochemical hydrogen storage alloy material to said compaction means; (j) continuously disposing a layer of the comminuted electrochemical hydrogen storage alloy material into contact with the wire mesh screen substrate, in a substantially inert atmosphere; (k) compacting the hydrogen storage alloy material into the wire mesh screen so as to form a green deposit thereof; (l) preheating the green deposit of hydrogen storage alloy-wire mesh screen; (m) sintering the green deposit of hydrogen storage alloy wire mesh screen in an anhydrous, substantially oxygen free inert atmosphere so as to liberate moisture therefrom; and (n) cooling said sintered hydrogen storage alloy wire mesh screen in a controlled hydrogen atmosphere so as to impart a partial charge thereto.
Claim 2
Independent Claim
286 words
A method of substantially continuously fabricating a large area, metal hydride electrochemical hydrogen storage alloy negative electrode for use in a rechargeable nickel-metal hydride battery, said method comprising the steps of: (a) providing particulate metal hydride electrochemical hydrogen storage alloy material in a substantially non-reactive gas atmosphere; (b) providing a high speed impact mill adapted to tangentially and radially accelerate particles placed therein against an impact block; (c) introducing said particulate metal hydride, hydrogen storage alloy material into said impact mill for comminution along natural fracture lines of the material, while maintaining said non-reactive atmosphere; (d) transporting said comminuted metal hydride, electrochemical hydrogen storage material to a classifying means in a stream of said substantially non-reactive gas; (e) separating oversized particles from said comminuted material in said classifying means; (f) recirculating said non-reactive gas; (g) transporting said comminuted metal hydride electrochemical hydrogen storage alloy to a compaction means; (h) providing a continuous, wire mesh screen substrate to said compaction means; (i) providing a measured amount of the comminuted metal hydride electrochemical hydrogen storage alloy material to said compaction means; (j) continuously disposing a layer of the comminuted electrochemical hydrogen storage alloy material into contact with the wire mesh screen substrate, in a substantially inert atmosphere; (k) compacting the hydrogen storage alloy material into the wire mesh screen so as to form a green deposit thereof; (l) preheating the green deposit of hydrogen storage alloy-wire mesh screen; (m) sintering the green deposit of hydrogen storage alloy wire mesh screen in an anhydrous, substantially oxygen free inert atmosphere so as to liberate moisture therefrom; and (n) cooling said sintered hydrogen storage alloy wire mesh screen in a controlled hydrogen atmosphere so as to impart a partial charge thereto.
Claim 3
Dependent Claim
34 words
The method as recited in claim 1, wherein said metal hydride, hydrogen storage alloy material comprises an alloy of vanadium, zirconium, titanium, nickel and chromium, having a Rockwell hardness of between 45 and 60
Claim 4
Dependent Claim
44 words
The method as in claim 2, wherein said metal hydride, hydrogen storage alloy material has the composition: (Ti.sub.z-x Zr.sub.x V.sub.4-y Ni.sub.y).sub.1-z Cr.sub.z where x is between 0 and 1.5, y is between 0.6 and 3.5, and z is an effective amount less than 0.20.
Claim 5
Dependent Claim
28 words
The method as recited in claim 1, wherein the step of providing particulate metal hydride hydrogen storage alloy material comprises providing particulate material of about 75-100 mesh size.
Claim 6
Dependent Claim
26 words
The method as recited in claim 1, wherein said substantially non-reactive gas is selected from the group consisting of argon, neon, helium, nitrogen and combinations thereof.
Claim 7
Dependent Claim
15 words
The method as recited in claim 5, wherein the preferred substantially non-reactive gas is nitrogen.
Claim 8
Dependent Claim
36 words
The method as recited in claim 1, wherein said high speed impact mill is center-fed, high speed rotor mill adapted to turn at a speed of about 5,000 to 20,000 rpm, and preferably about 10,000 rpm.
Claim 9
Dependent Claim
36 words
The method as recited in claim 7, wherein said particulate metal hydride, hydrogen storage material and substantially non-reactive gas are fed into the center of said mill, for acceleration thereof into a concentrically disposed impact block.
Claim 10
Dependent Claim
22 words
The method as recited in claim 1, wherein said stream of substantially non-reactive gas is provided at a rate of 100-300 SCFH.
Claim 11
Dependent Claim
20 words
The method as recited in claim 1, including the further step of supplementing the non-reactive gas with make-up non-reactive gas.
Claim 12
Dependent Claim
16 words
The method as recited in claim 10, wherein said non-reactive gas is recycled for subsequent reuse.
Claim 13
Dependent Claim
22 words
The method as recited in claim 11, wherein the pressure of said non-reactive gas is uniformly maintained at a slight positive pressure.
Claim 14
Dependent Claim
71 words
The method as recited in claim 1, wherein the step of separating particles of said material in said classifying means includes the further steps of: (a) providing means for separating said substantially non-reactive gas from said comminuted hydrogen storage alloy material; (b) separating said non-reactive gas from said comminuted material; (c) providing a vibratory screen classifier as said classifying means; and (d) separately collecting classified of said hydrogen storage alloy material.
Claim 15
Dependent Claim
24 words
The method as recited in claim 13, wherein said hydrogen storage material is comminuted to a powder of less than about 200 mesh size.
Claim 16
Dependent Claim
24 words
The method as recited in claim 13, wherein said hydrogen storage material is comminuted to a powder averaging about 400 mesh, 38 micron size.
Claim 17
Dependent Claim
23 words
The method as recited in claim 13, wherein said means for separating said non-reactive gas from said comminuted material comprises a cyclone separator.
Claim 18
Dependent Claim
75 words
The method as recited in claim 1, wherein the step of providing particulate, metal hydride, hydrogen storage alloy material comprises the further steps of: (a) providing a powder dispenser capable of maintaining an inert atmosphere, and operatively disposed to feed said hydrogen storage alloy material into said impact mill by gravity; and (b) providing a regulating means operatively disposed between said impact mill and said powder dispenser to regulate the flow of said particulate material.
References Cited (Backward Citations)
US4820481A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-09 | 1993-10-09 | 1994-04-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-09 | 1997-10-09 | 1998-04-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-09 | 2001-10-09 | 2002-04-10 | $7700.00 | Window Closed / Lapsed |