Residue-free plasma etch of high temperature AlCu
Assignee: NXP USA Inc
•
Filing: 1988-08-23
•
Granted: 1990-04-10
•
Expires: 2008-08-23
Abstract
Abstract A residue-free plasma etch of high temperature aluminum copper metallization is provided by the use of a single plasma etcher. The metallization layer is covered by a protective oxide layer. This structure is then placed in the single etcher and a vacuum is established. The protective oxide layer is then etched and without breaking the vacuum or removing the structure from the etcher the metal layer is also etched. This results in the etched surface being residue-free.
Inventors
- 👤 G. Scot Srodes
- 👤 Willis R. Goodner
- 👤 John L. Freeman, Jr.
- 👤 Andrew G. Nagy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:01
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/26; H10P50/264; H10P50/266; H10P50/267; C; C23; C23F; C23F4/00; Y; Y10; Y10S; Y10S438/00; Y10S438/942; Y10S438/948; Y10S438/95
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
106 words
A residue-free, plasma etch of high temperature AlCu layer, comprising: providing the high temperature AlCu layer on a semiconductor support; providing a protective layer over the AlCu layer; providing a layer of photoresist over the protective layer; patterning the photoresist to leave exposed portions of the protective layer; placing all the layers in a vacuum in a reactive ion etcher; etching through the exposed protective layer to expose portions of the AlCu layer; and etching through the exposed portions of the AlCu layer, wherein the vacuum is held continuously between the protective layer etching and AlCu layer etching steps to provide the residue-free high temperature AlCu.
Claim 2
Dependent Claim
106 words
A residue-free, plasma etch of high temperature AlCu layer, comprising: providing the high temperature AlCu layer on a semiconductor support; providing a protective layer over the AlCu layer; providing a layer of photoresist over the protective layer; patterning the photoresist to leave exposed portions of the protective layer; placing all the layers in a vacuum in a reactive ion etcher; etching through the exposed protective layer to expose portions of the AlCu layer; and etching through the exposed portions of the AlCu layer, wherein the vacuum is held continuously between the protective layer etching and AlCu layer etching steps to provide the residue-free high temperature AlCu.
Claim 3
Dependent Claim
29 words
The residue-free, plasma etch of claim 1 wherein the high temperature AlCu layer is a layer deposited at a temperature in the range of 350° C. to 500° C.
Claim 4
Dependent Claim
33 words
The residue-free, plasma etch of claim 1 wherein the vacuum is maintained by not opening the etcher between the etching of the exposed protective layer and the etching through the exposed AlCu layer.
Claim 5
Dependent Claim
16 words
The residue-free, plasma etch of claim 1 wherein the protective layer is a plasma enhanced oxide.
Claim 6
Independent Claim
140 words
A method for providing a residue-free high temperature AlCu metallization layer etching after the AlCu metallization layer has been deposited on a semiconductor structure, comprising: providing the high temperature AlCu layer on a semiconductor support; providing a protective layer over the AlCu metallization layer; providing a photoresist layer over the protective layer and patterning the photoresist layer to leave exposed portions of the protective layer; placing the semiconductor structure in a vacuum in a reactive ion etcher; etching away the exposed portions of the protective layer to leave exposed portions of the AlCu metallization layer; and etching away the exposed portions of the AlCu metallization layer to leave a residue-free area, wherein the protective layer and AlCu metallization layer are etched without breaking the vacuum in which the semiconductor structure was placed before the step of etching the protective layer.
Claim 7
Independent Claim
140 words
A method for providing a residue-free high temperature AlCu metallization layer etching after the AlCu metallization layer has been deposited on a semiconductor structure, comprising: providing the high temperature AlCu layer on a semiconductor support; providing a protective layer over the AlCu metallization layer; providing a photoresist layer over the protective layer and patterning the photoresist layer to leave exposed portions of the protective layer; placing the semiconductor structure in a vacuum in a reactive ion etcher; etching away the exposed portions of the protective layer to leave exposed portions of the AlCu metallization layer; and etching away the exposed portions of the AlCu metallization layer to leave a residue-free area, wherein the protective layer and AlCu metallization layer are etched without breaking the vacuum in which the semiconductor structure was placed before the step of etching the protective layer.
Claim 8
Dependent Claim
22 words
The method of claim 5 wherein the protective layer is a plasma enhanced oxide layer formed at a temperature below 500° C.
Claim 9
Dependent Claim
19 words
The method of claim 6 wherein the oxide layer is a plasma enhanced oxide and serves as a hardmask.
Claim 10
Dependent Claim
27 words
The method of claim 6 wherein the oxide layer is approximately 200 to 300 nanometers thick and the photoresist layer is approximately 1.2 to 2.5 microns thick.
Claim 11
Independent Claim
134 words
A method for etching a high temperature metallization layer on a semiconductor structure in a manner to provide a residue-free surface, comprising: providing the semiconductor structure; providing the high temperature metallization layer on the semiconductor structure; providing a protective layer over the metallization layer; providing a layer of photoresist over the protective layer and patterning the photoresist to expose portions of the protective layer; placing the semiconductor structure in a plasma etcher and creating a vacuum around the semiconductor structure; etching away the exposed portions of the protective layer to expose portions of the metallization layer while maintaining the vacuum; and etching away the exposed portions of the metallization layer without breaking the vacuum around the semiconductor structure to provide a residue-free surface where the exposed portions of the metallization layer had previously existed.
Claim 12
Independent Claim
134 words
A method for etching a high temperature metallization layer on a semiconductor structure in a manner to provide a residue-free surface, comprising: providing the semiconductor structure; providing the high temperature metallization layer on the semiconductor structure; providing a protective layer over the metallization layer; providing a layer of photoresist over the protective layer and patterning the photoresist to expose portions of the protective layer; placing the semiconductor structure in a plasma etcher and creating a vacuum around the semiconductor structure; etching away the exposed portions of the protective layer to expose portions of the metallization layer while maintaining the vacuum; and etching away the exposed portions of the metallization layer without breaking the vacuum around the semiconductor structure to provide a residue-free surface where the exposed portions of the metallization layer had previously existed.
Claim 13
Dependent Claim
35 words
The method of claim 9 wherein the high temperature metallization layer is deposited at a temperature over 350° C., the protective layer is a layer of oxide, and the etcher is a reactive ion etcher.
References Cited (Backward Citations)
US4030967A
Cited
US4062720A
Cited
US4182646A
Cited
US4333814A
Cited
US4637129A
Cited
US4717445A
Cited
US4790903A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-09 | 1993-10-09 | 1994-04-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-09 | 1997-10-09 | 1998-04-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-09 | 2001-10-09 | 2002-04-10 | $7700.00 | Window Closed / Lapsed |