Wear-resistant sintered alloy and method for its production
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1987-07-14
•
Granted: 1990-04-10
•
Expires: 2007-07-14
Abstract
Abstract A wear-resistant sintered alloy comprising an Cr-C-Fe base alloy in which 0.5 to 3% by weight of CaF 2 and 5 to 20% by weight of hard particles having particle size of 44 to 150 μm and a mean value of Vickers hardness of 800 to 2000 are dispersed. This wear-resistant sintered alloy is produced by a method comprising the steps of adding 1.2 to 2% by weight of carbon powder, 0.5 to 3% by weight of calcium fluoride powder, and 5 to 20% by weight of hard metal powder having the particle size of 44 to 150 μm and a mean value of Vickers hardness of 800 to 2000, to an Fe-Cr-C base alloy powder containing 10 to 20% by weight of Cr and 0.8 to 1.5% by weight of C, mixing them, molding the resultant mixed powder into a desired shaped, and then sintering the compact in the temperature range of from 1180° to 1260° C. in a non-oxidizing atmosphere. The sintered alloy is useful as a material for parts required to have the heat resistance and wear resistance.
Inventors
- 👤 Naoki Motooka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:22
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0207; C22C33/0228; C22C33/0257; C22C33/0278; C22C33/0285
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
135 words
A wear-resistant sintered alloy consisting essentially of an iron base alloy matrix, 0.5 to 3% by weight of particles of CaF 2 , and 5 to 20% by weight of particles of a hard alloy, said CaF2 and said hard alloy being dispersed in said iron base alloy matrix in the form of particles, said iron base alloy matrix consisting essentially, by weight, of 10 to 20% of Cr, 1.5 to 3.5% of C, and the balance being essentially iron, said hard alloy consisting essentially, by weight, of 50 to 70 of Cr, 5 to 10% of C, not more than 1% of Si, and the balance being essentially Fe, the particle of said hard alloy having particle size of 44 to 150 μm and the mean value of Vickers hardness of 800 to 2000.
Claim 2
Dependent Claim
135 words
A wear-resistant sintered alloy consisting essentially of an iron base alloy matrix, 0.5 to 3% by weight of particles of CaF 2 , and 5 to 20% by weight of particles of a hard alloy, said CaF2 and said hard alloy being dispersed in said iron base alloy matrix in the form of particles, said iron base alloy matrix consisting essentially, by weight, of 10 to 20% of Cr, 1.5 to 3.5% of C, and the balance being essentially iron, said hard alloy consisting essentially, by weight, of 50 to 70 of Cr, 5 to 10% of C, not more than 1% of Si, and the balance being essentially Fe, the particle of said hard alloy having particle size of 44 to 150 μm and the mean value of Vickers hardness of 800 to 2000.
Claim 3
Dependent Claim
27 words
A wear-resistnt sintered alloy claimed in claim 1 wherein particle size of CaF 2 containe in the iron base alloy matrix is not more than 149 μm.
Claim 4
Dependent Claim
25 words
A wear-resistant sintered alloy claimed in claim 1 wherein said sintered alloy has a density of which a density ratio is not less than 95%.
Claim 5
Dependent Claim
149 words
A wear-resistant sintered alloy consisting essentially of an iron base alloy matrix, 0.5 to 3% by weight of particles of CaF 2 , and 5 to 20% by weight of particles of a hard alloy, said CaF 2 and said hard alloy being dispersed in said iron base alloy matrix in the form of particles, said iron base alloy matrix consisting essentially, by weight, of 10 to 20% of Cr, 1.5 to 3.5% of C, 1 to 5% of at least one element selected from the group consisting of Co and Ni, and the balance being essentially of iron, said had alloy consisting essentially, by weight, of 50 to 70% of C, not more than 1% of Si, and the balance being essentially Fe, the particles of said hard alloy having particle size of 44 to 150 μm and a mean value of Vickers hardness of 800 to 2000.
Claim 6
Dependent Claim
149 words
A wear-resistant sintered alloy consisting essentially of an iron base alloy matrix, 0.5 to 3% by weight of particles of CaF 2 , and 5 to 20% by weight of particles of a hard alloy, said CaF 2 and said hard alloy being dispersed in said iron base alloy matrix in the form of particles, said iron base alloy matrix consisting essentially, by weight, of 10 to 20% of Cr, 1.5 to 3.5% of C, 1 to 5% of at least one element selected from the group consisting of Co and Ni, and the balance being essentially of iron, said had alloy consisting essentially, by weight, of 50 to 70% of C, not more than 1% of Si, and the balance being essentially Fe, the particles of said hard alloy having particle size of 44 to 150 μm and a mean value of Vickers hardness of 800 to 2000.
Claim 7
Dependent Claim
27 words
A wear-resistant sintered alloy claimed in claim 4 wherein particle size of CaF 2 contained in the iron base alloy matrix is not more than 149 μm.
Claim 8
Dependent Claim
25 words
A wear-resistant sintered alloy claimed in claim 4 wherein said sintered alloy has a density of which a density ratio is not less than 95%.
Claim 9
Dependent Claim
159 words
A wear-resistant sintered alloy consisting essentially of an iron base alloy matrix, 0.5 to 3% by weight of particles of CaF 2 , and 5 to 20% by weight of particles of a hard alloy, said CaF 2 and said hard alloy being dispersed in said iron base alloy matrix in the form of particles, said iron base alloy matrix consisting essentially of 10 to 20% by weight of Cr, 1.5 to 3.5% by weight of C, 1 to 5% by weight of at least one element selected from the group consisting of Mo, Nb, W and V, and the balance essentially iron, said hard alloy consisting essentially, by weight, of 50 to 70% of Cr, 5 to 10% of C, not more than 1% of Si, and the balance being essentially Fe, the particles of said hard alloy having the particle size of 44 to 150 μm and a mean value of Vickers hardness of 800 to 2000.
Claim 10
Dependent Claim
159 words
A wear-resistant sintered alloy consisting essentially of an iron base alloy matrix, 0.5 to 3% by weight of particles of CaF 2 , and 5 to 20% by weight of particles of a hard alloy, said CaF 2 and said hard alloy being dispersed in said iron base alloy matrix in the form of particles, said iron base alloy matrix consisting essentially of 10 to 20% by weight of Cr, 1.5 to 3.5% by weight of C, 1 to 5% by weight of at least one element selected from the group consisting of Mo, Nb, W and V, and the balance essentially iron, said hard alloy consisting essentially, by weight, of 50 to 70% of Cr, 5 to 10% of C, not more than 1% of Si, and the balance being essentially Fe, the particles of said hard alloy having the particle size of 44 to 150 μm and a mean value of Vickers hardness of 800 to 2000.
Claim 11
Dependent Claim
27 words
A wear-resistant sintered alloy claimed in claim 7 wherein particle size of CaF 2 contained in the iron base alloy matrix is not more than 149 μm.
Claim 12
Dependent Claim
25 words
A wear-resistant sintered alloy claimed in claim 7 wherein said sintered alloy has a density of which a density ratio is not less than 95%.
Claim 13
Independent Claim
187 words
A method for producing a wear-resistant sintered alloy containing 0.5 to 3% by weight of particles of CaF 2 , and 5 to 20% by weight of particles of a hard alloy, which are dispersed in a matrix of an iron base alloy in the form of particles, said hard alloy consisting essentially, by weight, of 50 to 70% of Cr, 5 to 10% of C, not more than 1% of Si, and the balance being essentially Fe, said method comprising the steps of mixing 1.2 to 2% by weight of carbon powder, 0.5 to 3% by weight of calcium fluoride powder, 5 to 20% of hard alloy powder having the particle size of 44 to 150 μm and a mean value of Vickers hardness in the range of 800 to 2000, and powder of an iron base alloy containing at least 10 to 20% by weight of Cr and 1.5 to 3.5% by weight of C, molding the resultant mixture into a desired shape to prepare compact, and then firing the resultant compact in the temperature range of 1180° to 1260° C. in a non-oxidizing atmosphere.
Claim 14
Independent Claim
187 words
A method for producing a wear-resistant sintered alloy containing 0.5 to 3% by weight of particles of CaF 2 , and 5 to 20% by weight of particles of a hard alloy, which are dispersed in a matrix of an iron base alloy in the form of particles, said hard alloy consisting essentially, by weight, of 50 to 70% of Cr, 5 to 10% of C, not more than 1% of Si, and the balance being essentially Fe, said method comprising the steps of mixing 1.2 to 2% by weight of carbon powder, 0.5 to 3% by weight of calcium fluoride powder, 5 to 20% of hard alloy powder having the particle size of 44 to 150 μm and a mean value of Vickers hardness in the range of 800 to 2000, and powder of an iron base alloy containing at least 10 to 20% by weight of Cr and 1.5 to 3.5% by weight of C, molding the resultant mixture into a desired shape to prepare compact, and then firing the resultant compact in the temperature range of 1180° to 1260° C. in a non-oxidizing atmosphere.
Claim 15
Dependent Claim
43 words
A method for producing a wear-resistant sintered alloy claimed in claim 10, characterized in that said hard alloy powder is stable at a temperature within the range of 1180° to 1260° C. and does not melt into the matrix of the sintered alloy.
Claim 16
Dependent Claim
57 words
A method for producing a wear-resistant sintered alloy claimed in claim 10 characterized in that said hard alloy contains Cr carbide with particle size of not more than 20 μm, and hard alloy with particle size of 44 to 150 μm, said Cr carbide and hard alloy being uniformly dispersed in the matrix of the hard alloy.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-04-09 | 1993-10-09 | 1994-04-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-04-09 | 1997-10-09 | 1998-04-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-04-09 | 2001-10-09 | 2002-04-10 | $7700.00 | Window Closed / Lapsed |