Polymer coated alumina

Claim 2

A process for producing polybutadiene coated alumina particles wherein the alumina contains an alumina having a habit or form of crystals formed during a precipitation of aluminum hydroxide from an alkali metal aluminate by preselecting and controlling the pH of the alkali metal aluminate and the addition of certain monohydric and polyhydric alcohols to the alkali metal aluminate solution comprising: (a) coating an alumina having a habit or form of crystals formed during a precipitation of aluminum hydroxide from an alkali metal aluminate by preselecting and controlling the pH of the alkali metal aluminate and the addition of certain monohydric and polyhydric alcohols to the alkali metal aluminate solution with a solution of polybutadiene, radical generator, and solvent to form a polymer film layer on an acicular or lamellar alumina-based support, and (b) crosslinking said film layer to form a stable polybutadiene coating on said alumina-based support.

Claim 3

A process as set forth in claim 1 wherein said coating forms a polymer film layer comprising a substantially homogeneous film layer.

Claim 4

A process as set forth in claim 2 wherein said coating step includes sonicating said polybutadiene solution for at least about 30 minutes and then evaporating said solvent.

Claim 5

A process as set forth in claim 3 wherein said solvent is pentane and said evaporating is controlled to have a low rate, less than about 2 volume % of pentane used per minute.

Claim 6

A process as set forth in claim 4 wherein said evaporating temperature is controlled to remain below 30° C.

Claim 7

A process as set forth in claim 5 further including a drying step to remove solvent from the coated particles at a temperature below about 30° C.

Claim 8

A process as set forth in claim 6 wherein said crosslinking is uniform.

Claim 9

A process as set forth in claim 7 wherein said radical generator is at or about full strength.

Claim 10

A process as set forth in claim 8 wherein said radical generator is dicumylperoxide.

Claim 11

A process as set forth in claim 9 comprising controlling water content in pentane to minimal levels below about 5 ppm.

Claim 12

A process as set forth in claim 10 further comprising controlling water content in said pentane to a level below about 1 ppm.

Claim 13

A process as set forth in claim 11 further comprising removing unreacted polymer.

Claim 14

A process as set forth in claim 12 comprising washing with an organic solvent.

Claim 15

A process as set forth in claim 13 wherein said washing comprises washing with heptane, methylene chloride, acetone, or isopropyl alcohol.

Claim 16

A process as set forth in claim 14 wherein said washing comprises at least two discrete washings carried out for at least about 30 minutes each.

Claim 17

A process for producing polybutadiene coated alumina useful over a wide pH range at lower pressure drop requirements in a packed separations column comprising: (a) coating an alumina having a habit or form of crystals formed during a precipitation of aluminum hydroxide from an alkali metal aluminate by preselecting and controlling the pH of the alkali metal aluminate and the addition of certain monohydric and polyhydric alcohols to the alkali metal aluminate solution with a polybutadiene in pentane solution to form a polymer film layer on said alumina as support base, and (b) immobilizing said polymer film layer by crosslinking with a chemical radical generator to form a stable polybutadiene coating on said alumina.

Claim 18

A process for producing polybutadiene coated alumina useful over a wide pH range at lower pressure drop requirements in a packed separations column comprising: (a) coating an alumina having a habit or form of crystals formed during a precipitation of aluminum hydroxide from an alkali metal aluminate by preselecting and controlling the pH of the alkali metal aluminate and the addition of certain monohydric and polyhydric alcohols to the alkali metal aluminate solution with a polybutadiene in pentane solution to form a polymer film layer on said alumina as support base, and (b) immobilizing said polymer film layer by crosslinking with a chemical radical generator to form a stable polybutadiene coating on said alumina.

Claim 19

A process as set forth in claim 16 wherein said polymer film layer is substantially homogeneous, said crosslinking is substantially uniform.

Claim 20

A process as set forth in claim 17 wherein said coating is performed including sonication for at least about 30 minutes before evaporating the pentane at a rate of less than about 2 volume per cent per minute.

Claim 21

A process as set forth in claim 18 wherein said coating step is conducted at a temperature below about 25° C.

Claim 22

A process for producing a stable polybutadiene coated on a support base of an alumina having a habit or form of crystals formed during a precipitation of aluminum hydroxide from an alkali metal aluminate by preselecting and controlling the pH of the alkali metal aluminate and the addition of certain monohydric and polyhydric alcohols to the alkali metal aluminate solution comprising: (a) coating said alumina with a polybutadiene by suspending said alumina in a reactor of solution containing polybutadiene, dicumylperoxide, and solvent, sonicating the solution for about 30 minutes, and evaporating solvent slowly in a rotary evaporator connected to an aspirator to accelerate the evaporation process, said evaporation taking place at a temperature below about 25° C., (b) drying the polybutadiene coated particles with dry nitrogen at a temperature below about 25° C., (c) crosslinking and immobilizing the polybutadiene coated alumina in a temperature programmable oven starting at about 25° C. and heating to about 170° C. at a rate of about 5° C. per minute to form a stable polybutadiene coated and crosslinked alumina product, and (d) washing the polybutadiene coated and crosslinked alumina product with a heptane and methylene chloride to remove unreacted polybutadiene.

Claim 23

A process for producing a stable polybutadiene coated on a support base of an alumina having a habit or form of crystals formed during a precipitation of aluminum hydroxide from an alkali metal aluminate by preselecting and controlling the pH of the alkali metal aluminate and the addition of certain monohydric and polyhydric alcohols to the alkali metal aluminate solution comprising: (a) coating said alumina with a polybutadiene by suspending said alumina in a reactor of solution containing polybutadiene, dicumylperoxide, and solvent, sonicating the solution for about 30 minutes, and evaporating solvent slowly in a rotary evaporator connected to an aspirator to accelerate the evaporation process, said evaporation taking place at a temperature below about 25° C., (b) drying the polybutadiene coated particles with dry nitrogen at a temperature below about 25° C., (c) crosslinking and immobilizing the polybutadiene coated alumina in a temperature programmable oven starting at about 25° C. and heating to about 170° C. at a rate of about 5° C. per minute to form a stable polybutadiene coated and crosslinked alumina product, and (d) washing the polybutadiene coated and crosslinked alumina product with a heptane and methylene chloride to remove unreacted polybutadiene.