Patent US4912068A successfully refreshed from Google Patents.
US4912068A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Magnesite-carbon refractories
Assignee: Resco Products Inc
•
Filing: 1988-11-21
•
Granted: 1990-03-27
•
Expires: 2008-11-21
Abstract
Abstract A mix for forming a carbon-bonded refractory shape comprising from about 70 to 92 wt. % of a high purity magnesite and about 8 to 30 wt. % of a high purity graphite, and for each 100 wt. % of said magnesite and graphite, from about 1.5 to 6 wt. % of a carbon-containing bonding agent; said graphite containing at least about 98% carbon and having at least about 75% by weight -65 mesh or finer particles and said magnesite containing at least about 98% MgO, and containing less than about 0.03% boron oxide, less than about 0.3% silica, and having a CaO/SiO2 weight ratio above about 2, and the resultant carbon-bonded refractory shape and liner for basic oxygen furnaces made from such shapes and the method of increasing the life of liners for basic oxygen furnaces.
Inventors
- 👤 David J. Michael
- 👤 David A. Kirk
- 👤 Leigh F. Brooks
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 07:00
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/632; C04B35/634; C04B35/01; C04B35/013; C04B35/03; C04B35/04; C04B35/043; C04B35/63448; C04B35/63472; C04B35/63496; C04B35/66; C04B2111/00; C04B2111/00474; C04B2111/0087; C04B2111/00887; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/32; C04B2235/3205; C04B2235/3206; C04B2235/42; C04B2235/422; C04B2235/70; C04B2235/96; C04B2235/9669; C04B2235/9676
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
114 words
A metal-free mix for forming a magnesite-carbon refractory shape comprising from about 70 to 92 wt. % of a high purity magnesite and, correspondingly, about 8 to 30 wt. % of a high purity graphite, and for each 100 wt. % of said magnesite and graphite from about 1.5 to 6 wt. % of a carbonaceous bonding agent; said magnesite containing at least about 98% MgO and containing less than about 0.03% boron oxide, less than about 0.3% silica, and having a CaO/SiO 2 weight ratio above about 2, and said graphite having a loss on ignition of at least about 98% and at least about 75% by weight -65 mesh or finer particles.
Claim 2
Dependent Claim
114 words
A metal-free mix for forming a magnesite-carbon refractory shape comprising from about 70 to 92 wt. % of a high purity magnesite and, correspondingly, about 8 to 30 wt. % of a high purity graphite, and for each 100 wt. % of said magnesite and graphite from about 1.5 to 6 wt. % of a carbonaceous bonding agent; said magnesite containing at least about 98% MgO and containing less than about 0.03% boron oxide, less than about 0.3% silica, and having a CaO/SiO 2 weight ratio above about 2, and said graphite having a loss on ignition of at least about 98% and at least about 75% by weight -65 mesh or finer particles.
Claim 3
Dependent Claim
30 words
The mix of claim 1 wherein said magnesite contains at least 99% MgO and said carbonaceous bonding agent is a novolak resin, a resol resin, tar, pitch, or mixtures thereof.
Claim 4
Dependent Claim
18 words
The mix of claim 1 or 2 wherein said graphite is a flake graphite or a vein graphite.
Claim 5
Dependent Claim
130 words
A metal-free mix for forming a magnesite-carbon refractory consisting essentially of from about 70 to 92 wt. % of a high purity magnesite and about 8 to 30 wt. % of a high purity flake graphite or a vein graphite, and for each 100 wt. % of said magnesite and graphite from abut 1.5 to 6 wt. % of a carbonaceous bonding agent selected from novolak resins, resol resins, tar, pitch or mixtures thereof; said magnesite containing at least about 98% MgO and containing less than about 0.03% boron oxide, less than about 0.3% silica, and having a CaO/SiO 2 weight ratio above about 2, and said graphite having a loss on ignition of at least about 98% and at least about 75% by weight -65 mesh or finer particles.
Claim 6
Dependent Claim
130 words
A metal-free mix for forming a magnesite-carbon refractory consisting essentially of from about 70 to 92 wt. % of a high purity magnesite and about 8 to 30 wt. % of a high purity flake graphite or a vein graphite, and for each 100 wt. % of said magnesite and graphite from abut 1.5 to 6 wt. % of a carbonaceous bonding agent selected from novolak resins, resol resins, tar, pitch or mixtures thereof; said magnesite containing at least about 98% MgO and containing less than about 0.03% boron oxide, less than about 0.3% silica, and having a CaO/SiO 2 weight ratio above about 2, and said graphite having a loss on ignition of at least about 98% and at least about 75% by weight -65 mesh or finer particles.
Claim 7
Dependent Claim
116 words
A metal-free unburned magnesite-carbon refractory shape consisting of a baked mix comprising from about 70 to 92 wt. % of a high purity magnesite and, correspondingly, about 8 to 30 wt. % of a high purity graphite, and for each 100 wt. % of said magnesite and graphite, from about 1.5 to 6 wt. % of a carbonaceous bonding agent; said magnesite containing at least about 98% MgO and containing less than about 0.03% boron oxide, less than about 0.3% silica, and having a CaO/SiO 2 weight ratio above about 2, and said graphite having a loss on ignition of at least about 98% and at least about 75% by weight -65 mesh or finer particles.
Claim 8
Dependent Claim
116 words
A metal-free unburned magnesite-carbon refractory shape consisting of a baked mix comprising from about 70 to 92 wt. % of a high purity magnesite and, correspondingly, about 8 to 30 wt. % of a high purity graphite, and for each 100 wt. % of said magnesite and graphite, from about 1.5 to 6 wt. % of a carbonaceous bonding agent; said magnesite containing at least about 98% MgO and containing less than about 0.03% boron oxide, less than about 0.3% silica, and having a CaO/SiO 2 weight ratio above about 2, and said graphite having a loss on ignition of at least about 98% and at least about 75% by weight -65 mesh or finer particles.
Claim 9
Dependent Claim
20 words
The refractory shape of claim 5 wherein said shape is a brick and said magnesite contains at least 99% MgO.
Claim 10
Dependent Claim
17 words
The refractory shape of claim 5 wherein said graphite is a flake graphite or a vein graphite.
Claim 11
Dependent Claim
26 words
The refractory shape of claim 5, 6, or 7 wherein said carbonaceous bonding agent is a novolak resin, a resol resin, tar, pitch, or mixtures thereof.
Claim 12
Dependent Claim
123 words
A metal-free unburned refractory brick consisting essentially of a baked mix consisting essentially of from about 70 to 92 wt. % of a high purity magnesite and, correspondingly, about 8 to 30 wt. % of a high purity flake graphite or a vein graphite, and for each 100 wt. % of said magnesite and graphite, from about 1.5 to 6 wt. % of a carbonaceous bonding agent; said magnesite containing at least about 98% MgO and containing less than about 0.03% boron oxide, less than about 0.3% silica and having a CaO/SiO 2 weight ratio above about 2, and said graphite having a loss on ignition of at least about 98% and at least about 75% by weight -65 mesh or finer particles.
Claim 13
Dependent Claim
123 words
A metal-free unburned refractory brick consisting essentially of a baked mix consisting essentially of from about 70 to 92 wt. % of a high purity magnesite and, correspondingly, about 8 to 30 wt. % of a high purity flake graphite or a vein graphite, and for each 100 wt. % of said magnesite and graphite, from about 1.5 to 6 wt. % of a carbonaceous bonding agent; said magnesite containing at least about 98% MgO and containing less than about 0.03% boron oxide, less than about 0.3% silica and having a CaO/SiO 2 weight ratio above about 2, and said graphite having a loss on ignition of at least about 98% and at least about 75% by weight -65 mesh or finer particles.
Claim 14
Dependent Claim
23 words
The refractory brick of claim 8 wherein said carbonaceous bonding agent is a novolak resin, a resol resin, tar, pitch, or mixtures thereof.
Claim 15
Dependent Claim
141 words
A refractory brick lining for metal processing equipment wherein a principal mode of wear of the lining is by slag attack comprising a plurality of unburned magnesite-carbon brick, said brick consisting essentially of a baked mix comprising from about 70 to 92 wt. % of a high purity magnesite and, correspondingly, about 8 to 30 wt. % of a high purity graphite, and for each 100 wt. % of said magnesite and graphite from about 1.5 to 6 wt. % of a carbonaceous bonding agent; said magnesite containing at least about 98% MgO and containing less than about 0.03% boron oxide, less than about 0.3% silica, and having a CaO/SiO 2 weight ratio above about 2, and said graphite having a loss on ignition of at least about 98% and at least about 75% by weight -65 mesh or finer particles.
Claim 16
Dependent Claim
141 words
A refractory brick lining for metal processing equipment wherein a principal mode of wear of the lining is by slag attack comprising a plurality of unburned magnesite-carbon brick, said brick consisting essentially of a baked mix comprising from about 70 to 92 wt. % of a high purity magnesite and, correspondingly, about 8 to 30 wt. % of a high purity graphite, and for each 100 wt. % of said magnesite and graphite from about 1.5 to 6 wt. % of a carbonaceous bonding agent; said magnesite containing at least about 98% MgO and containing less than about 0.03% boron oxide, less than about 0.3% silica, and having a CaO/SiO 2 weight ratio above about 2, and said graphite having a loss on ignition of at least about 98% and at least about 75% by weight -65 mesh or finer particles.
Claim 17
Dependent Claim
46 words
The refractory brick liner of claim 11 for use in a basic oxygen furnace wherein the magnesite contains at least about 99% MgO and the graphite is a flake graphite or a vein graphite having at least about 95% by weight -65 mesh or finer particles.
Claim 18
Dependent Claim
26 words
The refractory brick liner of claim 11 or 12 wherein said carbonaceous bonding agent is a novolak resin, a resol resin, tar, pitch, or mixtures thereof.
Claim 19
Independent Claim
157 words
The method of increasing the life of liners for metal processing equipment wherein a principal mode of wear of the lining is by slag attack comprising forming a lining in said equipment comprising a plurality of unburned magnesite-carbon brick and subsequently burning said brick; said unburned brick consisting essentially of baked mix comprising from about 70 to 92 wt. % of a high purity magnesite and, correspondingly, about 8 to 30 wt. % of a high purity graphite, and for each 100 wt. % of said magnesite and graphite from about 1.5 to 6 wt. % of a carbonaceous bonding agent; said magensite containing at least about 98% MgO and containing less than about 0.03% boron oxide, less than about 0.3% silica, and having a CaO/SiO 2 weight ratio above about 2, and said graphite having a loss of ignition of at least about 98% and at least about 75% by weight -65 mesh or finer particles.
Claim 20
Independent Claim
157 words
The method of increasing the life of liners for metal processing equipment wherein a principal mode of wear of the lining is by slag attack comprising forming a lining in said equipment comprising a plurality of unburned magnesite-carbon brick and subsequently burning said brick; said unburned brick consisting essentially of baked mix comprising from about 70 to 92 wt. % of a high purity magnesite and, correspondingly, about 8 to 30 wt. % of a high purity graphite, and for each 100 wt. % of said magnesite and graphite from about 1.5 to 6 wt. % of a carbonaceous bonding agent; said magensite containing at least about 98% MgO and containing less than about 0.03% boron oxide, less than about 0.3% silica, and having a CaO/SiO 2 weight ratio above about 2, and said graphite having a loss of ignition of at least about 98% and at least about 75% by weight -65 mesh or finer particles.
Claim 21
Dependent Claim
48 words
The method of claim 14 for increasing the life of a liner for a basic oxygen furnace wherein the magnesite contains at least about 99% MgO and the graphite is a flake graphite or vein graphite having at least about 95% by weight -65 mesh or finer particles.
Claim 22
Independent Claim
24 words
The method of claims 14 or 15 wherein said carbonaceous bonding agent is a novolak resin, a resol resin, tar, pitch, or mixtures thereof.
References Cited (Backward Citations)
US3322551A
Cited
US2354757A
Cited
US641551A
Cited
US976996A
Cited
US1365336A
Cited
US2062962A
Cited
US2314107A
Cited
US2516249A
Cited
US3082104A
Cited
US3086876A
Cited
US3220860A
Cited
US4306030A
Cited
US4557884A
Cited
US4454239A
Cited
US4431745A
Cited
US4574119A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-26 | 1993-09-25 | 1994-03-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-26 | 1997-09-25 | 1998-03-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-26 | 2001-09-25 | 2002-03-27 | $7700.00 | Window Closed / Lapsed |