Method of manufacturing optical fibers
Assignee: Nortel Networks Ltd
•
Filing: 1989-02-23
•
Granted: 1990-03-27
•
Expires: 2009-02-23
Abstract
Abstract In order to eliminate the effect of water attack on silica optical fibres, the fibres are provided with a surface layer of silicon nitride or silicon oxynitride. The method proposed comprises direct nitridation. This may be achieved by adding a nitriding atmosphere to the drawing furnace gases, or to the reactive gases (TiCl 4 and SiCl 4 ) incorporated in the flame of an oxyhydrogen torch for the formation of a compressive silica/titania layer on an optical fibre by a glass soot deposition and sintering process.
Inventors
- 👤 Richard T. Newbould
- 👤 Susan J. Piggs
- 👤 Stephen J. Wilson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 06:38
CPC Classifications
C; C03; C03C; C03C25/00; C03C25/10; C03C25/12; C03C25/22; C03B; C03B37/00; C03B37/01; C03B37/02; C03B37/025; C03B37/029; C03B2201/00; C03B2201/06; C03B2201/20; C03B2201/24; C03B2201/30; C03B2201/58; Y; Y10; Y10S; Y10S65/00; Y10S65/90
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
142 words
A method of manufacturing silica optical fibers comprising the steps of taking a consolidated silica preform from which the optical fiber is to be drawn, the consolidated silica preform having a radially outermost surface layer containing oxygen; subjecting the preform to an atmosphere of ammonia at a temperature on the order of 900° C. to chemically change the surface layer by substituting at least part of the oxygen therein with nitrogen provided by said ammonia so as to form a silicon oxynitride or a silicon nitride layer in dependence on the amount of oxygen substituted with nitrogen; and heating the preform with the changed surface layer to a fiber drawing temperature and drawing optical fiber therefrom, which optical fibre has a silicon oxynitride or silicon nitride layer at its radially outermost surface that protects the fiber at least partially from water attack.
Claim 2
Independent Claim
142 words
A method of manufacturing silica optical fibers comprising the steps of taking a consolidated silica preform from which the optical fiber is to be drawn, the consolidated silica preform having a radially outermost surface layer containing oxygen; subjecting the preform to an atmosphere of ammonia at a temperature on the order of 900° C. to chemically change the surface layer by substituting at least part of the oxygen therein with nitrogen provided by said ammonia so as to form a silicon oxynitride or a silicon nitride layer in dependence on the amount of oxygen substituted with nitrogen; and heating the preform with the changed surface layer to a fiber drawing temperature and drawing optical fiber therefrom, which optical fibre has a silicon oxynitride or silicon nitride layer at its radially outermost surface that protects the fiber at least partially from water attack.
Claim 3
Dependent Claim
81 words
A method as claimed in claim 1 including, prior to said step of subjecting the preform to the ammonia atmosphere, the step of applying a compressive surface layer to the radially outermost surface layer of the preform, and wherein a radially outermost part of the compressive surface layer comprises the radially outermost surface layer containing oxygen which is to be chemically changed, the manufactured fiber thus being provided with a corresponding compressive layer under the silicon oxynitride or silicon nitride layer.
Claim 4
Independent Claim
166 words
A method of manufacturing silica optical fibers comprising the steps of taking a consolidated silica preform from which the silicon optical fibre is to be drawn, the silica preform having a radially outermost surface layer containing oxygen, heating the preform to a fiber drawing temperature in a drawing furnace while an atmosphere of ammonia is injected into the drawing furnace and drawing and optical fiber from the heated preform, the ammonia atmosphere within the drawing furnace serving to chemically change a radially outermost part of the radially outermost oxygen containing surface layer of the preform and the corresponding radially outermost surface of the optical fiber being drawn from the preform by substituting at least part of the oxygen therein with nitrogen provided by said ammonia to form a silicon oxynitride or a silicon nitride layer in dependence on the amount of oxygen substituted with nitrogen at said radially outermost surface of the fiber so that the manufactured fiber is at least partially protected from water attack.
Claim 5
Independent Claim
166 words
A method of manufacturing silica optical fibers comprising the steps of taking a consolidated silica preform from which the silicon optical fibre is to be drawn, the silica preform having a radially outermost surface layer containing oxygen, heating the preform to a fiber drawing temperature in a drawing furnace while an atmosphere of ammonia is injected into the drawing furnace and drawing and optical fiber from the heated preform, the ammonia atmosphere within the drawing furnace serving to chemically change a radially outermost part of the radially outermost oxygen containing surface layer of the preform and the corresponding radially outermost surface of the optical fiber being drawn from the preform by substituting at least part of the oxygen therein with nitrogen provided by said ammonia to form a silicon oxynitride or a silicon nitride layer in dependence on the amount of oxygen substituted with nitrogen at said radially outermost surface of the fiber so that the manufactured fiber is at least partially protected from water attack.
Claim 6
Dependent Claim
81 words
A method as claimed in claim 3 including the step, prior to said heating step, of applying a compressive surface layer to the radially outermost surface layer of said consolidated preform, and wherein a radially outermost part of the compressive surface layer comprises said radially outermost part of the radially outermost surface layer of the preform which is to be chemically changed, the manufactured fiber thus being provided with a corresponding compressive layer under the silicon oxynitride or silicon nitride layer.
Claim 7
Dependent Claim
136 words
A method as claimed in claim 4 wherein the application of the compressive surface layer comprises incorporating TiCl 4 and SiCl 4 in the flame of an oxyhydrogen torch so as to form a titania/silica soot, depositing the soot on the radially outermost surface of the preform and sintering the soot, and wherein the fiber is drawn from the preform in the drawing furnace while the ammonia atmosphere is injected into the drawing furnace, the ammonia atmosphere within the furnace chemically changing the radially outermost part of the compressive surface layer of the preform and the corresponding surface layer of the optical fiber being drawn from the preform, which radially outermost part of the compressive surface layer comprises said radially outermost surface layer containing oxygen, by substituting at least part of the oxygen therein with nitrogen.
Claim 8
Independent Claim
200 words
A method of manufacturing silica optical fibers comprising the steps of taking a consolidated silica preform from which the silica optical fiber is to be drawn; applying a compressive surface layer containing oxygen to a radially outermost surface of the preform by incorporating TiCl 4 and SiCl 4 in the flame of an oxyhydrogen torch so as to form a titania/silica soot, depositing the soot on the radially outermost surface of the preform and sintering the soot; and heating the preform to a fiber-drawing temperature in a drawing furnace while an ammonia atmosphere is injected into the drawing furnace, and drawing an optical fiber from the heated preform, the ammonia temperature within the drawing furnace serving to chemically change a radially outermost part of the compressive surface layer of the preform, and the corresponding surface layer of the optical fiber being drawn from the preform, by substituting at least part of the oxygen therein with nitrogen provided by said ammonia to form a silicon oxynitride or silicon nitride layer in dependence on the amount of oxygen substituted with nitrogen at the radially outermost surface of the fibre so that the manufactured fiber is protected at least partially from water attack.
Claim 9
Independent Claim
200 words
A method of manufacturing silica optical fibers comprising the steps of taking a consolidated silica preform from which the silica optical fiber is to be drawn; applying a compressive surface layer containing oxygen to a radially outermost surface of the preform by incorporating TiCl 4 and SiCl 4 in the flame of an oxyhydrogen torch so as to form a titania/silica soot, depositing the soot on the radially outermost surface of the preform and sintering the soot; and heating the preform to a fiber-drawing temperature in a drawing furnace while an ammonia atmosphere is injected into the drawing furnace, and drawing an optical fiber from the heated preform, the ammonia temperature within the drawing furnace serving to chemically change a radially outermost part of the compressive surface layer of the preform, and the corresponding surface layer of the optical fiber being drawn from the preform, by substituting at least part of the oxygen therein with nitrogen provided by said ammonia to form a silicon oxynitride or silicon nitride layer in dependence on the amount of oxygen substituted with nitrogen at the radially outermost surface of the fibre so that the manufactured fiber is protected at least partially from water attack.
Claim 10
Independent Claim
138 words
A method of manufacturing silica optical fibers protected at least partially from water attack comprising the steps of taking in consolidated silica preform which is unprotected from water attack and has a radially outermost surface layer containing oxygen and drawing a silica optical fiber from the preform while an ammonia atmosphere is present in the drawing furnace so that a radially outermost part of the surface layer of the preform, and the corresponding surface layer of the optical fiber being drawn from the preform, is converted, due to the presence of the ammonia atmosphere in the furnace, to a silicon oxynitride surface by substituting at least part of the oxygen therein with nitrogen provided by ammonia, the drawn silicon fiber being protected at least partially from water attack by said corresponding converted surface layer of the optical fiber.
Claim 11
Independent Claim
138 words
A method of manufacturing silica optical fibers protected at least partially from water attack comprising the steps of taking in consolidated silica preform which is unprotected from water attack and has a radially outermost surface layer containing oxygen and drawing a silica optical fiber from the preform while an ammonia atmosphere is present in the drawing furnace so that a radially outermost part of the surface layer of the preform, and the corresponding surface layer of the optical fiber being drawn from the preform, is converted, due to the presence of the ammonia atmosphere in the furnace, to a silicon oxynitride surface by substituting at least part of the oxygen therein with nitrogen provided by ammonia, the drawn silicon fiber being protected at least partially from water attack by said corresponding converted surface layer of the optical fiber.
Claim 12
Independent Claim
138 words
A method of manufacturing silica optical fibers protected at least partially from water attack comprising the steps of taking a consolidated silica preform which is unprotected from water attack and has a radially outermost surface layer containing oxygen and drawing a silica fiber from the preform while an ammonia atmosphere is present in the drawing furnace so that a radially outermost part of the surface layer of the preform, and the corresponding surface layer of the optical fiber being drawing from the preform, is converted, due to the presence of the ammonia atmosphere in the furnace, to a silicon nitride surface by substituting at least part of the oxygen therein with nitrogen provided by said ammonia, the drawn silica fiber being protected at least partially from water attack by said corresponding converted surface layer of the optical fiber.
Claim 13
Independent Claim
138 words
A method of manufacturing silica optical fibers protected at least partially from water attack comprising the steps of taking a consolidated silica preform which is unprotected from water attack and has a radially outermost surface layer containing oxygen and drawing a silica fiber from the preform while an ammonia atmosphere is present in the drawing furnace so that a radially outermost part of the surface layer of the preform, and the corresponding surface layer of the optical fiber being drawing from the preform, is converted, due to the presence of the ammonia atmosphere in the furnace, to a silicon nitride surface by substituting at least part of the oxygen therein with nitrogen provided by said ammonia, the drawn silica fiber being protected at least partially from water attack by said corresponding converted surface layer of the optical fiber.
References Cited (Backward Citations)
US4030901A
Cited
GB1592234A
Cited
US4118211A
Cited
US4203744A
Cited
US4445754A
Cited
GB2062615A
Cited
US4227907A
Cited
US4402720A
Cited
US4367013A
Cited
US4286978A
Cited
US4417910A
Cited
US4388094A
Cited
US4501602A
Cited
US4574063A
Cited
US4608276A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-26 | 1993-09-25 | 1994-03-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-26 | 1997-09-25 | 1998-03-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-26 | 2001-09-25 | 2002-03-27 | $7700.00 | Window Closed / Lapsed |