US4367013A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Preparation of semifinished product for manufacture of optical fibers
Assignee: Saint Gobain Quartz SAS
•
Filing: 1981-02-11
•
Granted: 1983-01-04
•
Expires: 2001-02-11
Abstract
Abstract A process is described for making a doped-silica ingot useful in the manufacture of optical fibers. At least a silicon compound and a titanium compound are decomposed in the flame of the induction plasma burner in the presence of a determined supply of hydrogen and are reacted with the oxygen contained in the burner feed gas and/or in the vector gas to form SiO 2 and H 2 O against a heat-stable support. As a result silica and titanium oxide are deposited on the support in the form of a homogeneous vitreous mass exhibiting a selected concentration of hydroxyl groups between 10 and 50 parts per million. Fluorine-doped silica is deposited radially in the same way on the resulting ingot. The resulting semifinished product is a cylinder consisting of a titanium-doped silica core, whose TiO 2 concentration by weight is about 0.1 to 8%, covered by a sheath of fluorine-doped silica, whose fluorine concentration is about 0.1 to 3%.
Inventors
- 👤 Pierre Guerder
- 👤 Andre Ranson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 20:29
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/01413; C03B37/0142; C03B37/01426; C03B37/018; C03B37/01807; C03B37/01815; C03B37/01823; C03B2201/00; C03B2201/06; C03B2201/08; C03B2201/12; C03B2201/30; C03B2201/40; C03B2201/42; C03B2207/00; C03B2207/80; C03B2207/85; C03B2207/86; C03B2207/87; Y; Y10; Y10S; Y10S65/00; Y10S65/15; Y10S65/16
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
162 words
A process of making optical fibers from doped silicas comprising the steps of: forming a cylindrical ingot by axial deposition, on a heat-stable support, of titanium-doped silica obtained by decomposition and oxidation of at least a silicon compound and a titanium compound in the flame of an induction plasma burner, at least one of said compounds containing a predetermined supply of hydrogen, coating said ingot surface by a radial deposition of at least a doped silica so that the index refraction of this silica is less than that of the ingot, and drawing the ingot thus coated into the shape of fibers of narrow diameter, wherein, during the first step, the silicon and titanium compounds are decomposed and oxidized to form SiO 2 , TiO 2 and H 2 O and the supply of hydrogen is determined so as to deposit directly on said heat-stable support a vitreous mass having a concentration of hydroxyl groups between 10 and 50 parts per million.
Claim 2
Dependent Claim
162 words
A process of making optical fibers from doped silicas comprising the steps of: forming a cylindrical ingot by axial deposition, on a heat-stable support, of titanium-doped silica obtained by decomposition and oxidation of at least a silicon compound and a titanium compound in the flame of an induction plasma burner, at least one of said compounds containing a predetermined supply of hydrogen, coating said ingot surface by a radial deposition of at least a doped silica so that the index refraction of this silica is less than that of the ingot, and drawing the ingot thus coated into the shape of fibers of narrow diameter, wherein, during the first step, the silicon and titanium compounds are decomposed and oxidized to form SiO 2 , TiO 2 and H 2 O and the supply of hydrogen is determined so as to deposit directly on said heat-stable support a vitreous mass having a concentration of hydroxyl groups between 10 and 50 parts per million.
Claim 3
Dependent Claim
25 words
The process of claim 1 wherein gaseous silicon and titanium compounds are injected on the outside of the burner and penetrate the plasma flame crosswise.
Claim 4
Dependent Claim
42 words
The process of claim 1 wherein the total hydrogen content of the compound or compounds sent in to the flame of said burner is such that concentrations of hydroxyl groups in the doped silica are between 20 and 30 parts per million.
Claim 5
Dependent Claim
29 words
The process of claim 1 wherein the silica is formed from the decomposition and oxidation of a mixture of silicon tetrachloride (SiCl 4 ) and trichlorosilane (SiHCl 3 ).
Claim 6
Dependent Claim
30 words
The process of claim 1 wherein the titanium is supplied by at least one of the compounds selected from the group consisting of titanium tetrachloride, isobutyl titanate, and isopropyl titanate.
Claim 7
Dependent Claim
32 words
The process of claim 5 wherein the amount of titanium injected in the plasma is such that the resulting vitreous silica contains a weight percentage of TiO 2 between 0.1 and 8%.
Claim 8
Dependent Claim
38 words
The process of claim 1 wherein during the step of coating the ingot surface by radial deposition there is deposited on the titanium-doped silica ingot a fluorine-doped silica whose weight content in fluorine is between 0.1 and 3%.
Claim 9
Dependent Claim
33 words
The process of claim 7 wherein between the titanium-doped silica core and the florine-doped silica periphery there is radially deposited an intermediate layer made up of silica simultaneously doped with titanium and fluorine.
Claim 10
Dependent Claim
39 words
The process of claim 8 wherein during formation of the intermediate layer the composition of the gaseous mixture is modified by progressively reducing the delivery of the titanium compound or compounds relative to the delivery of the fluorine compound.
Claim 11
Dependent Claim
28 words
The process of claim 7 wherein the fluorine is supplied by at least one of the compounds selected from the group consisting of sulfur hexafluoride and nitrogen trifluoride.
Claim 12
Dependent Claim
158 words
In the manufacture of optical fibers using doped silicas, a process for making a doped ingot comprising the steps of: forming a cylindrical ingot by axial deposition, on a heat-stable support, of titanium-doped silica obtained by decomposition and oxidation of at least a silicon compound and a titanium compound in the flame of an induction plasma burner, at least one of said compounds containing a predetermined supply of hydrogen, and coating said ingot surface by a radial deposition of at least a doped silica so that the index of refraction of this silica is less than that of the ingot, wherein, during the first step, the silicon and titanium compounds are decomposed and and oxidized to form SiO 2 , TiO 2 and H 2 O and the supply of hydrogen is determined so as to deposit directly on said heat-stable support a vitreous mass having a concentration of hydroxyl groups between 10 and 50 parts per million.
Claim 13
Dependent Claim
158 words
In the manufacture of optical fibers using doped silicas, a process for making a doped ingot comprising the steps of: forming a cylindrical ingot by axial deposition, on a heat-stable support, of titanium-doped silica obtained by decomposition and oxidation of at least a silicon compound and a titanium compound in the flame of an induction plasma burner, at least one of said compounds containing a predetermined supply of hydrogen, and coating said ingot surface by a radial deposition of at least a doped silica so that the index of refraction of this silica is less than that of the ingot, wherein, during the first step, the silicon and titanium compounds are decomposed and and oxidized to form SiO 2 , TiO 2 and H 2 O and the supply of hydrogen is determined so as to deposit directly on said heat-stable support a vitreous mass having a concentration of hydroxyl groups between 10 and 50 parts per million.
Claim 14
Dependent Claim
25 words
The process of claim 11 wherein gaseous silicon and titanium compounds are injected on the outside of the burner and penetrate the plasma flame crosswise.
Claim 15
Dependent Claim
81 words
A doped ingot for use in manufacturing optical fiber formed in accordance with claim 11 and comprising: a core of titanium-doped silica that is approximately 30 to 50 millimeters in diameter, said titanium constituting about 0.1 to 8% by weight of the silica; and a sheath of fluorine-doped silica surrounding said core, the total diameter of said core and sheath being approximately 50 to 120 millimeters, said fluorine constituting about 0.1 to 3% by weight of the silica of said sheath.
Claim 16
Dependent Claim
54 words
The process of claim 11 wherein the silica is formed from the decomposition and oxidation of a mixture of silicon tetrachloride (SiCl 4 ) and trichlorosilane (SiHCl 3 ) and the titanium is supplied by at least one of the compounds selected from the group consisting of titanium tetrachloride, isobutyl titanate, and isopropyl titanate.
Claim 17
Dependent Claim
32 words
The process of claim 14 wherein the amount of titanium injected in the plasma is such that the resulting vitreous silica contains a weight percentage of TiO 2 between 0.1 and 8%.
Claim 18
Dependent Claim
38 words
The process of claim 14 wherein during the step of coating the ingot surface by radial deposition there is deposited on the titanium-doped silica ingot a fluorine-doped silica whose weight content in fluorine is between 0.1 and 3%.
Claim 19
Dependent Claim
33 words
The process of claim 16 wherein between the titanium-doped silica core and the fluorine-doped silica periphery there is radially deposited an intermediate layer made up of silica simultaneously doped with titanium and fluorine.
Claim 20
Dependent Claim
39 words
The process of claim 17 wherein during formation of the intermediate layer the composition of the gaseous mixture is modified by progressively reducing the delivery of the titanium compound or compounds relative to the delivery of the fluorine compound.
Claim 21
Dependent Claim
28 words
The process of claim 16 wherein the fluorine is supplied by at least one of the compounds selected from the group consisting of sulfur hexafluoride and nitrogen trifluoride.
References Cited (Backward Citations)
GB1061042A
Cited
GB1213603A
Cited
GB1391177A
Cited
GB1431352A
Cited
DE2247307C3
Cited
GB1492920A
Cited
CA1029993A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-01-03 | 1986-07-05 | 1987-01-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-01-03 | 1990-07-05 | 1991-01-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-01-03 | 1994-07-05 | 1995-01-04 | $7700.00 | Window Closed / Lapsed |