Manufacture of polyurethane foam
Assignee: Huntsman International LLC
•
Filing: 1988-09-21
•
Granted: 1990-03-20
•
Expires: 2008-09-21
Abstract
Abstract Substantially water blown flexible polyurethane foams, based on methylene diphenyl isocyanates, having a density ranging from 15-25 kg/m<3>. Such foams may be obtained through a process substantially avoiding halocarbon blowing agents, which comprises reacting methylene diphenyl isocyanates with water and one or more isocyanate-reactive compounds selected from polyols and polyamines with a functionality of 2-4 and an average equivalent weight ranging from 750-5000, while the isocyanate index ranges from 10 to 60, and weight ratio of the isocyanate-reactive compound(s) to water is less than 20.
Inventors
- 👤 Tu Pham
- 👤 Louis Muller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:07
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/48; C08G18/08; C08G18/50; C08G18/5021; C08G18/5024; C08G18/70; C08G18/72; C08G18/721; C08G18/727; C08G18/74; C08G18/76; C08G18/7657; C08G18/7664; C08G18/77; C08G18/78; C08G2110/00; C08G2110/0008; C08G2110/0041; C08G2110/005; C08G2110/0075; C08G2110/0083
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
83 words
Process for manufacturing flexible polyurethane foams based on methylene diphenyl isocyanates and isocyanate-reactive compounds, substantially avoiding halocarbon blowing agents, which comprises reacting methylene diphenyl isocyanates with water and one or more isocyanate-reactive compounds selected from polyols and polyamines with a functionality of 2-4 and an average equivalent weight ranging from 750-5000 optionally together with additives conventional in the art, whereas the isocyanate index ranges from 10 to 60, and whereas the weight ratio of the isocyanate-reactive compound(s) to water is less than 20.
Claim 2
Dependent Claim
83 words
Process for manufacturing flexible polyurethane foams based on methylene diphenyl isocyanates and isocyanate-reactive compounds, substantially avoiding halocarbon blowing agents, which comprises reacting methylene diphenyl isocyanates with water and one or more isocyanate-reactive compounds selected from polyols and polyamines with a functionality of 2-4 and an average equivalent weight ranging from 750-5000 optionally together with additives conventional in the art, whereas the isocyanate index ranges from 10 to 60, and whereas the weight ratio of the isocyanate-reactive compound(s) to water is less than 20.
Claim 3
Dependent Claim
24 words
Process according to claim 1, characterized in that one or more isocyanate reactive compounds are selected from polyether polyols, polyester polyols and polyether polyamines.
Claim 4
Dependent Claim
24 words
Process according to claim 1, characterized in that the weight ratio of the isocyanate-reactive compound(s) to the water ranges from 3 to below 20.
Claim 5
Dependent Claim
29 words
Substantially water blown "flexible polyurethane foam" based on methylene diphenyl isocyanates and isocyanate reactive compounds selected from polyols and polyamines, having a density ranging from 15-45 kg/m 3 .
Claim 6
Dependent Claim
29 words
Substantially water blown "flexible polyurethane foam" based on methylene diphenyl isocyanates and isocyanate reactive compounds selected from polyols and polyamines, having a density ranging from 15-45 kg/m 3 .
Claim 7
Dependent Claim
13 words
Flexible polyurethane foam according to claim 4 obtained by a one shot process.
Claim 8
Dependent Claim
34 words
Flexible polyurethane foam according to any one of claims 7 to 9, characterized by an indentation hardness index ranging from 30 to 210 Newton, when measured according to the method described in ISO 2439.
Claim 9
Dependent Claim
16 words
Flexible polyurethane foam obtainable by the process according to any one of claims 1 to 3.
Claim 10
Dependent Claim
94 words
Reactive system for the manufacture of flexible polyurethane foams involving a substantially halocarbon free isocyanate composition based on methylene diphenyl isocyanates and a substantially halocarbon free isocyanate reactive composition comprising one or more polyols and/or polyamines with a functionality of 2-4 and an average equivalent weight ranging from 750-5000 and at least 5 parts by weight of water per 100 parts of polyol and polyamine, optionally together with additives conventional in the art, said isocyanate composition and isocyanate reactive composition being provided in proportions to give an isocyanate index ranging from 10 to 60.
Claim 11
Dependent Claim
94 words
Reactive system for the manufacture of flexible polyurethane foams involving a substantially halocarbon free isocyanate composition based on methylene diphenyl isocyanates and a substantially halocarbon free isocyanate reactive composition comprising one or more polyols and/or polyamines with a functionality of 2-4 and an average equivalent weight ranging from 750-5000 and at least 5 parts by weight of water per 100 parts of polyol and polyamine, optionally together with additives conventional in the art, said isocyanate composition and isocyanate reactive composition being provided in proportions to give an isocyanate index ranging from 10 to 60.
Claim 12
Dependent Claim
96 words
Polyurethane foam formulation constituting an incitation to manufacture flexible polyurethane foams using a substantially halocarbon free isocyanate composition based on methylene diphenyl isocyanates and a substantially halocarbon free isocyanate reactive composition comprising one or more polyols and/or polyamines with a functionality of 2-4 and an average equivalent weight ranging from 750-5000 and at least 5 parts by weight of water per 100 parts of polyol and polyamine, optionally together with additives conventional in the art, said isocyanate composition and isocyanate reactive composition being provided in proportions to give an isocyanate index ranging from 10 to 60.
Claim 13
Dependent Claim
96 words
Polyurethane foam formulation constituting an incitation to manufacture flexible polyurethane foams using a substantially halocarbon free isocyanate composition based on methylene diphenyl isocyanates and a substantially halocarbon free isocyanate reactive composition comprising one or more polyols and/or polyamines with a functionality of 2-4 and an average equivalent weight ranging from 750-5000 and at least 5 parts by weight of water per 100 parts of polyol and polyamine, optionally together with additives conventional in the art, said isocyanate composition and isocyanate reactive composition being provided in proportions to give an isocyanate index ranging from 10 to 60.
Claim 14
Dependent Claim
18 words
A process according to claim 1 wherein the isocyanate index is in the range of 10 to 43.
Claim 15
Dependent Claim
20 words
A flexible polyurethane foam according to claim 4 wherein the density range is from 20 to 45 kg/m 3 .
Claim 16
Dependent Claim
13 words
A flexible polyurethane foam according to claim 4 in the form of slabstock.
References Cited (Backward Citations)
US4384050A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-19 | 1993-09-18 | 1994-03-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-19 | 1997-09-18 | 1998-03-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-19 | 2001-09-18 | 2002-03-20 | $7700.00 | Window Closed / Lapsed |