US4910105A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Electrochemical cell
Assignee: Lilliwyte SA
•
Filing: 1988-11-30
•
Granted: 1990-03-20
•
Expires: 2008-11-30
Abstract
Abstract The invention provides a high temperature rechargeable electrochemical power storage cell which comprises an alkali metal anode which is molten at the operating temperature of the cell. The cell has a cathode and a separator which separates the anode from the cathode and which is a conductor of ions of the metal of the anode. The surface of the separator which is exposed to the anode is at least partly enclosed by and in contact with a layer of particulate material which acts as a wick for the molten alkali metal of the anode. The material of the particles of the layer is electronically conductive and chemically inert at the operating temperatures of the cell to the alkali metal of the anode and to the separator, and the particles thereof are coated by a surface coating. The alkali metal of the anode, when molten, exhibits a contact angle with respect to said coating which is less than the contact angle exhibited by the molten alkali metal with respect to the material of the particles which underlies their coatings.
Inventors
- 👤 Alec R. Tilley
- 👤 Diane Rowe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 14:31
CPC Classifications
H; H01; H01M; H01M10/00; H01M10/36; H01M10/39; H01M10/3909; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
196 words
A high temperature rechargeable electrochemical power storage cell which comprises an alkali metal anode which is molten at the operating temperature of the cell, a cathode and a separator which separates the anode from the cathode and which is a conductor of ions of the metal of the anode, the surface of the separator which is exposed to the anode being at least partly enclosed by and in contact with a layer of particulate material which acts as a wick for the molten alkali metal of the anode, the material of the particles of the layer being electronically conductive and chemically inert at the cell operating temperatures to the alkali metal of the anode and to the separator, and the particles thereof being coated by a surface coating, the alkali metal of the anode when molten exhibiting a contact angle respect to said coating which is less than the contact angle exhibited by the molten alkali metal with respect to the material of the particles which underlies their coatings, and the coatings being of a metal oxide selected from the group consisting of the oxides of lead, tin, zinc, copper, iron, nickel, manganese and mixtures thereof.
Claim 2
Dependent Claim
196 words
A high temperature rechargeable electrochemical power storage cell which comprises an alkali metal anode which is molten at the operating temperature of the cell, a cathode and a separator which separates the anode from the cathode and which is a conductor of ions of the metal of the anode, the surface of the separator which is exposed to the anode being at least partly enclosed by and in contact with a layer of particulate material which acts as a wick for the molten alkali metal of the anode, the material of the particles of the layer being electronically conductive and chemically inert at the cell operating temperatures to the alkali metal of the anode and to the separator, and the particles thereof being coated by a surface coating, the alkali metal of the anode when molten exhibiting a contact angle respect to said coating which is less than the contact angle exhibited by the molten alkali metal with respect to the material of the particles which underlies their coatings, and the coatings being of a metal oxide selected from the group consisting of the oxides of lead, tin, zinc, copper, iron, nickel, manganese and mixtures thereof.
Claim 3
Dependent Claim
179 words
A high temperature rechargeable electrochemical power storage cell which comprises an alkali metal anode which is molten at the operating temperature of the cell, a cathode and a separator which separates the anode from the cathode and which is a conductor of ions of the metal of the anode, the surface of the separator which is exposed to the anode being at least partly enclosed by and in contact with a layerof particulate material which acts as a wick for the molten alkali metal of the anode, the material of the particles of the layer being electronically conductive and chemically inert at the cell operating temperatures to the alkali metal of the anode and to the separator, and the particles of the layer being coated by a surface coating, the alkali metal of the anode when molten exhibiting a contact angle with respect to said coating which is less than the contact angle exhibited by the molten alkali metal with respect to the material of the particles which underlies their coatings, and the coatings being reduced metal oxide coatings.
Claim 4
Dependent Claim
179 words
A high temperature rechargeable electrochemical power storage cell which comprises an alkali metal anode which is molten at the operating temperature of the cell, a cathode and a separator which separates the anode from the cathode and which is a conductor of ions of the metal of the anode, the surface of the separator which is exposed to the anode being at least partly enclosed by and in contact with a layerof particulate material which acts as a wick for the molten alkali metal of the anode, the material of the particles of the layer being electronically conductive and chemically inert at the cell operating temperatures to the alkali metal of the anode and to the separator, and the particles of the layer being coated by a surface coating, the alkali metal of the anode when molten exhibiting a contact angle with respect to said coating which is less than the contact angle exhibited by the molten alkali metal with respect to the material of the particles which underlies their coatings, and the coatings being reduced metal oxide coatings.
Claim 5
Dependent Claim
39 words
A cell as claimed in claim 1 or in claim 1 or in claim 2, in which the layer has a thickness of 0.5-2 mm, and the particulate material has an average particle size in the range 2-400 microns.
Claim 6
Dependent Claim
46 words
A cell as claimed in claim 1 or claim 2, in which the material of the particles underlying their coatings is a member of the group consisting of metals which are more noble than the alkali metal of the anode, graphite, silicon carbide, and mixtures thereof.
Claim 7
Dependent Claim
42 words
A cell as claimed in claim 1 or claim 2, in which the cell contains, in contact with or dissolved in the alkali metal of the anode, a getter selected from the group consisting of aluminium, titanium, vanadium, magnesium and mixtures thereof.
Claim 8
Dependent Claim
26 words
A cell as claimed in claim 1 or claim 2, in which the alkali metal of the anode is sodium and the separator is of beta-alumina.
Claim 9
Dependent Claim
71 words
A cell as claimed in claim 7 or claim 2, in which the cathode has as its active cathode substance, a substance selected from sulphur/sodium sulphide/polysulphide and members of the group consisting of Fe/FeC1 2 , Ni/NiC1 2 , Cr/CrC1 2 and Mn/MnC1 2 , immersed in a NaA1C1 4 molten salt electrolyte in contact with the separator and in which the mole ratio of A1:Na ions is at most 1:1.
Claim 10
Dependent Claim
155 words
A cell sub-assembly for a high temperature rechargeable electrochemical power storage cell, which sub-assembly comprises a cell housing and a separator which divides the housing into an anode compartment and a cathode compartment, the separator being a conductor of alkali metal ions and having, on its surface exposed to the anode compartment, a layer of particulate material which is electronically conductive and chemically insert at the operating temperatures of such cells to alkali metals and to the separator, and the particles of the layer being coated by a surface coating, alkali metals when molten exhibiting a contact angle with respect to said coating which is less than the contact angle exhibited by the respective molten alkali metals with respect to the material of the particles which underlies their coatings, and the coatings being of a metal oxide selected from the group consisting of the oxides of lead, tin, zinc, copper, iron, manganese and mixtures thereof.
Claim 11
Dependent Claim
155 words
A cell sub-assembly for a high temperature rechargeable electrochemical power storage cell, which sub-assembly comprises a cell housing and a separator which divides the housing into an anode compartment and a cathode compartment, the separator being a conductor of alkali metal ions and having, on its surface exposed to the anode compartment, a layer of particulate material which is electronically conductive and chemically insert at the operating temperatures of such cells to alkali metals and to the separator, and the particles of the layer being coated by a surface coating, alkali metals when molten exhibiting a contact angle with respect to said coating which is less than the contact angle exhibited by the respective molten alkali metals with respect to the material of the particles which underlies their coatings, and the coatings being of a metal oxide selected from the group consisting of the oxides of lead, tin, zinc, copper, iron, manganese and mixtures thereof.
Claim 12
Dependent Claim
134 words
A separator for a high temperature rechargeable electrochemical power storage cell having a molten alkali metal anode, the separator being a conductor of alkali metal ions and having, on a surface thereof, a layer of particulate material which is electronically conductive and chemically inert at the operating temperatures of such cells to alkali metals and to the separator, and the particles of the layer being coated by a surface coating, alkali metals when molten exhibiting a contact angle with respect to said coating which is less than the contact angle exhibited by the respective molten alkali metals with respect to the material of the particles which underlies their coatings,and the coatings being of a metal oxide selected from the group consisting of the oxides of lead, tin, zinc, copper, iron, manganese and mixtures thereof.
Claim 13
Dependent Claim
134 words
A separator for a high temperature rechargeable electrochemical power storage cell having a molten alkali metal anode, the separator being a conductor of alkali metal ions and having, on a surface thereof, a layer of particulate material which is electronically conductive and chemically inert at the operating temperatures of such cells to alkali metals and to the separator, and the particles of the layer being coated by a surface coating, alkali metals when molten exhibiting a contact angle with respect to said coating which is less than the contact angle exhibited by the respective molten alkali metals with respect to the material of the particles which underlies their coatings,and the coatings being of a metal oxide selected from the group consisting of the oxides of lead, tin, zinc, copper, iron, manganese and mixtures thereof.
Claim 14
Dependent Claim
137 words
A cell sub-assembly for a high temperature rechargeable electrochemical power storage cell, which sub-assembly comprises a cell housing and a separator which divides the housing into an anode compartment and a cathode compartment, the separator being a conductor of alkali metal ions and having, on its surface exposed to the anode compartment, a layer of particulate material which is electronically conductive and chemically inert at the operating temperatures of such cells to alkali metals and to the separator, and the particles of the layer being coated by a surface coating, alkali metals when molten exhibiting a contact angle with respect to said coating which is less than the contact angle exhibited by the respective molten alkali metals with respect to the material of the particles which underlies their coatings, and the coatings being reduced metal oxide coatings.
Claim 15
Dependent Claim
137 words
A cell sub-assembly for a high temperature rechargeable electrochemical power storage cell, which sub-assembly comprises a cell housing and a separator which divides the housing into an anode compartment and a cathode compartment, the separator being a conductor of alkali metal ions and having, on its surface exposed to the anode compartment, a layer of particulate material which is electronically conductive and chemically inert at the operating temperatures of such cells to alkali metals and to the separator, and the particles of the layer being coated by a surface coating, alkali metals when molten exhibiting a contact angle with respect to said coating which is less than the contact angle exhibited by the respective molten alkali metals with respect to the material of the particles which underlies their coatings, and the coatings being reduced metal oxide coatings.
Claim 16
Dependent Claim
117 words
A separator for a high temperature rechargeable electrochemical power storage cell having a molten alkali metal anode, the separator being a conductor of alkali metal ions and having, on a surface thereof, a layer of particulate material which is electronically conductive and chemically inert at the operating temperatures of such cells to alkali metals and to the separator, and the particles of the layer being coated by a surface coating, alkali metals when molten exhibiting a contact angle with respect to said coating which is less than the contact angle exhibited by the respective molten alkali metals with respect to the material of the particles which underlies their coatings, and the coatings being reduced metal oxide coatings.
Claim 17
Dependent Claim
117 words
A separator for a high temperature rechargeable electrochemical power storage cell having a molten alkali metal anode, the separator being a conductor of alkali metal ions and having, on a surface thereof, a layer of particulate material which is electronically conductive and chemically inert at the operating temperatures of such cells to alkali metals and to the separator, and the particles of the layer being coated by a surface coating, alkali metals when molten exhibiting a contact angle with respect to said coating which is less than the contact angle exhibited by the respective molten alkali metals with respect to the material of the particles which underlies their coatings, and the coatings being reduced metal oxide coatings.
References Cited (Backward Citations)
GB1461071A
Cited
GB1555133A
Cited
GB1491929A
Cited
GB1569114A
Cited
US4220691A
Cited
US4568620A
Cited
GB2067005A
Cited
US4348467A
Cited
GB2080608A
Cited
GB2089559A
Cited
US4515874A
Cited
US4446213A
Cited
GB2132003A
Cited
GB2140608A
Cited
GB2162680A
Cited
GB2182194A
Cited
GB2195329A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-19 | 1993-09-18 | 1994-03-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-19 | 1997-09-18 | 1998-03-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-19 | 2001-09-18 | 2002-03-20 | $7700.00 | Window Closed / Lapsed |